Crystallization of ion beam deposited calcium phosphate coatings

Published online by Cambridge University Press:  03 March 2011

Tse S. Chen  and
William R. Lacefield
Tse S. Chen
Affiliation:
Department of Biomaterials, University of Alabama at Birmingham, Birmingham, Alabama 35294
William R. Lacefield
Affiliation:
Department of Biomaterials, University of Alabama at Birmingham, Birmingham, Alabama 35294
Get access

Abstract

Amorphous calcium phosphate coatings on the order of 1 μm thick were deposited onto titanium and silicon substrates using an ion-beam sputtering technique. The target material utilized for sputter deposition was plasma-sprayed fluorapatite [Ca10(PO4)6F2; FA]. X-ray diffraction (XRD) and transmission electron microscopy (TEM) were employed to analyze the coatings. The amorphous as-deposited coatings were annealed in air (at 500 °C or 600 °C) to a crystalline state consisting of a polycrystalline FA matrix with a small amount of microcrystallites of a different composition. The higher annealing temperature (600 °C) tended to produce coarser FA and microcrystallite grains; however, the coatings buckled on the titanium substrates as a result of the heat treatment. Attempts to form the FA phase by in situ annealing in the vacuum chamber at a substrate temperature of 500 °C were not successful. The average bond strength for the as-deposited and 500 °C post-annealed coatings was comparable, while the lowest bond strength was observed in the 600 °C post-annealed coatings. The results suggest that the 500 °C post-annealed coatings have a suitable structure and possess sufficient adherence to be acceptable for use in certain medical and dental implant applications, and further tests under physiologic conditions will be conducted.

Type
Articles
Information
Journal of Materials Research , Volume 9 , Issue 5 , May 1994 , pp. 1284 - 1290
Copyright
Copyright © Materials Research Society 1994

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Damien, C. J. and Parsons, J. R., J. Appl. Biomat. 2, 187–208 (1991).Google Scholar
2de Groot, K., Geesink, R. G. T., Klein, C. P. A. T., and Serekian, P., J. Biomed. Mater. Res. 21, 1375–1387 (1987).Google Scholar
3Thomas, K. A., Kay, J. F., Cook, S. D., and Jarcho, M., J. Biomed.Mater. Res. 21, 1395–1406 (1987).Google Scholar
4Hench, L. L. and Wilson, J., Mater. Res. Bull. XVI (9), 62–74 4 (1991).CrossRefGoogle Scholar
5Hagen, A. R., Calc. Tiss. Res. 13, 259–270 (1973).CrossRefGoogle Scholar
6Kay, M. I., Young, R. A., and Posner, A. S., Nature 204, 1050–1052 (1964).CrossRefGoogle Scholar
7Jenkins, G. N., J. Dent. Res. (Supplement to No. 1) 42, 444–452 (1963).Google Scholar
8Newesely, H., Archs. Oral Biol. 6, 174–180 (1961).Google Scholar
9Moreno, E. C., Kresak, M., and Zahradnik, R. T., Caries Res. 11 (Suppl. 1), 142–171 (1977).CrossRefGoogle Scholar
10Dhert, W. J. A., Klein, C. P. A. T., Wolke, J. G. C., van der Lubbe, H. B. M., de Groot, K., and Rozing, P. M., Trans. Soc. Biomat. 14, 168 (1991).Google Scholar
11Rigney, E. D., Ph.D. Dissertation, University of Alabama at Birmingham (1989).Google Scholar
12Ong, J. L., M. S. Thesis, University of Alabama at Birmingham (1991).Google Scholar
13Whitehead, R. Y., M. S. Thesis, University of Alabama at Birmingham (1991).Google Scholar
14Lacefield, W. R., Rigney, E. D., Lucas, L. C., Ong, J. L., and Gantenberg, J. B., in Ceramics in Substitutive and Reconstructive Surgery (Elsevier Press, New York, 1991), pp. 167–176.Google Scholar
15Yamauchi, H., White, R. J., Ayukawa, M., Murray, T. C., and Robinson, J. W., J. Mater. Res. 3, 105–111 (1988).Google Scholar
16Mattox, D. M., in Deposition Technologies for Films and Coatings, edited by Bunshah, R. F. (Noyes Publications, Park Ridge, NJ, 1982), pp. 63–82.Google Scholar