Synthesis of α–Al2O3 platelets using sodium sulfate flux

Published online by Cambridge University Press:  31 January 2011

Shinobu Hashimoto  and
Akira Yamaguchi
Shinobu Hashimoto*
Affiliation:
Department of Materials Science and Engineering, Nagoya Institute of Technology, Gokiso-cho, Showa-ku, Nagoya 466–8555, Japan
Akira Yamaguchi
Affiliation:
Department of Materials Science and Engineering, Nagoya Institute of Technology, Gokiso-cho, Showa-ku, Nagoya 466–8555, Japan
*
a)Address all correspondence to this author. e-mail: shinobuh@mse.nitech.ac.jp
Get access

Abstract

When powder mixtures of {Al2(SO4)3 + Na2SO4}or {γ–Al2O3 [obtained by heating Al2(SO4)3 at 900 °C for 3 h] + Na2SO4} were heated in an alumina crucible at 1100 °C for 1 h, α–Al2O3 platelets were formed. The powder mixture of {Al2(SO4)3 + 2Na2SO4} yielded aggregations of platelets that were less than 5 μm in size. The size of the aggregations increased in proportion to the amount of Na2SO4, and aggregations of 120 μm were obtained using a mixture of {Al2(SO4)3 + 6Na2SO4}. The powder mixture of {γ–Al2O3 + 2Na2SO4 yielded hexagonal platelets having an average diameter of 3.7 μm and an average thickness of 0.3 μm. In addition to aggregation size, the size of the hexagonal platelets also increased in proportion to the amount of Na2SO4, and platelets having an average diameter of 5 μm were obtained using a mixture of {γ–Al2O3 + 6Na2SO4}.

Type
Articles
Information
Journal of Materials Research , Volume 14 , Issue 12 , December 1999 , pp. 4667 - 4672
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Heussner, K-H. and Claussen, N., J. Eur. Ceram. Soc. 5, 193 (1989).CrossRefGoogle Scholar
2.Form, P.S., Pyrz, R., Clausen, B., and Nielsen, E.Ø., Mater. Sci. Eng. A197, 231 (1995).CrossRefGoogle Scholar
3.Zhou, Y., Vleugels, J., Laoui, T., and Van Der Biest, O., J. Mater. Sci. Lett. 13, 1089 (1994).CrossRefGoogle Scholar
4.Yang, Y., Yang, Z., and Yuan, Q., J. Mater. Sci. Lett. 15, 185 (1996).CrossRefGoogle Scholar
5.Zhou, Y., Vlengels, J., Laoui, T., and Van Der Biest, O., J. Eur. Ceram. Soc. 15, 297 (1995).CrossRefGoogle Scholar
6.Fredel, M.C. and Boccaccini, A.R., J. Mater. Sci. 31, 4375 (1996).CrossRefGoogle Scholar
7.Champion, E., Gautier, S., and Bernache-Assolant, D., J. Mater. Sci. 7, 125 (1996).Google Scholar
8.Boccaccini, A.R. and Trusty, P.A., J. Mater. Sci. 15, 60 (1996).Google Scholar
9.Massardier, V., Maire, E., and Merle, P., Mater. Sci. Eng. A203, 105 (1995).CrossRefGoogle Scholar
10.Daimon, K. and Kato, E., J. Cryst. Growth 75, 348 (1986).CrossRefGoogle Scholar
11.Shaklee, C.A. and Messing, G.L., J. Am. Ceram. Soc. 77, 2977 (1994).CrossRefGoogle Scholar
12.Bell, N.S., Cho, S-B., and Adair, J.H., J. Am. Ceram. Soc. 81, 1411 (1998).CrossRefGoogle Scholar
13.Ono, S., Yamaguchi, G., Yanagida, H., and Shimizu, T., J. Ceram. Soc. Jpn. (Yogyo-Kyokai-shi) 76, 207 (1968).Google Scholar
14.Kato, S., Iga, T., Sano, S., and Ishii, E., J. Ceram. Soc. Jpn. (Yogyo-Kyokai-shi) 77, 60 (1969).Google Scholar
15.Kato, E., Daimon, K., Yamaguchi, A., and Yamada, T., J. Ceram. Soc. Jpn. (Yogyo-Kyokai-shi) 85, 134 (1977).Google Scholar
16.Levin, E.M. and McMurdie, H.F., Phase Diagrams for Ceramists 1975 Supplement (American Ceramic Society, Westerville, OH, 1975), Fig. 4708.Google Scholar
17.Brain, I., Thermochemical Data of Pure Substances, Part II, La-Zr, 2nd ed. (VHC, Weinheim, Germany, 1993), p. 1003.Google Scholar