Evaluation of Corrosion of Refractory Materials Using Electron Microscopy

Published online by Cambridge University Press:  23 July 2021

Pavol Vadász ,
Dávid Medveď ,
Beatrice Plešingerová  and
Jerzy Labaj
Pavol Vadász*
Affiliation:
Faculty of Materials, Metallurgy and Recycling, Technical University of Košice, Letná 1/9, Košice 040 02, Slovakia
Dávid Medveď
Affiliation:
Faculty of Materials, Metallurgy and Recycling, Technical University of Košice, Letná 1/9, Košice 040 02, Slovakia
Beatrice Plešingerová
Affiliation:
Faculty of Materials, Metallurgy and Recycling, Technical University of Košice, Letná 1/9, Košice 040 02, Slovakia
Jerzy Labaj
Affiliation:
Department of Metallurgy and Recycling, Faculty of Materials Engineering, Silesian University of Technology, Krasinskiego 8, Katowice 40 019, Poland
*
*Corresponding author: Pavol Vadász, E-mail: pavol.vadasz@tuke.sk
Get access

Abstract

The interaction of NCC-A (no cement content, with tabular corundum) refractory castable with corrosive refining steel slag CaO–Al2O3–SiO2–MgO–(FeO, MnO) was studied with static crucible corrosion tests. The corrosion process was evaluated using chemical and phase analyses, and the macro- and microstructures on the corrosion boundary of slag–refractory materials were investigated. We describe the corrosion progress and explain the NCC-A corrosion mechanism by oxide metallurgical slags. The alumina refractory material surface was wetted with molten oxide slag (contact angle θ1390°C from 10° to 20°). The slag penetrated through dissolution of the matrix (fine alumina cement), and the Ca–Si–Al slag, enriched with alumina, attacked the corundum grog. Marked changes in the chemical composition of the slag had an impact on the primary crystallization temperature. As the concentration of Al–O complexes increased in the slag, the binding parameters in Si–O complexes changed and complex tetrahedral units (Al–O–Si) and (Al–O–Mg) were created. Analyses of the corrosion interface grog show that calcium ions diffuse through structural defects in the corundum but Mg2+ diffusion was not observed. A sharp interface is observed between the slag and the corroded corundum layer. Differences in the chemical composition of the slag in the corrosion zone affected the convention stream, and formed the concave corrosion profile of the crucible.

Keywords

corrosioncorundumrefractory concreteSEM-EDSslag
Type
The XVIIth International Conference on Electron Microscopy (EM2020)
Information
Microscopy and Microanalysis , Volume 28 , Issue 3 , June 2022 , pp. 983 - 992
Copyright
Copyright © The Author(s), 2021. Published by Cambridge University Press on behalf of the Microscopy Society of America

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Cavalier, G & Sandreo-Dendon, M (1960). Rev Métallurg 57, 1143–1157. In Schlackenatlas, 1981. Düsseldorf, Germany: Verlag Stahleisen M.B.H., p. 57. ISBN 3-514-00228-2.Google Scholar
Jeon, J, Kang, Y, Hyun Park, J & Chung, Y (2017). Corrosion-erosion behavior of MgAl2O4 spinel refractory in contact with high MnO slag. Ceram Int 43, 15074–15079.CrossRefGoogle Scholar
Kim, H, Matsuura, H, Tsukihashi, F, Wang, W, Min, DJ & Sohn, I (2013). Effect of Al2O3 and CaO/SiO2 on the viscosity of calcium-silicate–based slags containing 10 mass Pct MgO. Metall Mater Trans B 44B, 5–12.CrossRefGoogle Scholar
Levin, EM & McMurdie, HF (1957). Phase diagrams for ceramists, supplement. USA. p. 100. In Steel Institute VDEh, Schlackenatlas, 1. Auflage, Publisher Stahleisen, Düsseldorf, Germany, 1981. p. 28. ISBN 3-514-00228-2.Google Scholar
Malfliet, A, Lotfian, S, Scheunis, L, Petkov, V, Pandelaers, L, Jones, PT & Blanpain, B (2014). Degradation mechanisms and use of refractory linings in copper production processes: a critical review. J Eur Ceram Soc 34, 849–876.CrossRefGoogle Scholar
Mao, H, Fabrichnaya, O, Selleby, M & Sundman, B (2005). Thermodynamic assessment of the MgO-Al2O3-SiO2 system. J Mater Res 20/4, 975–986.CrossRefGoogle Scholar
Mosttaghel, S, Matsushita, T, Samuelson, C, Björkman, B & Seetharaman, S (2013). Influence of alumina on physical properties of an industrial zinc–copper smelting slag. Part 2 – Apparent density, surface tension and effective thermal diffusivity. Miner Process Extr Metall, Trans Inst Min Metall C 122, 1.Google Scholar
Nakamoto, M, Kiose, A, Tanaka, T, Holappa, L & Hämäläinen, M (2007). Evaluation of the surface tension of ternary silicate melts containing Al2O3, CaO, FeO, MgO or MnO. ISIJ Int 47/1, 38–43.CrossRefGoogle Scholar
Roine, A, Lamberg, P, Mansikka-Aho, J, Bjőrklund, P, Kentala, JP, Talonen, T, Kotiranta, T, Ahlberg, R, Grőhn, A, Saarinen, O, Myyri, J, Sipilä, J, Vartiainen, A, et al. (2012). Software: Outotec, Research Center, 1974–2012, HSC Chemistry 7.193, Finland.Google Scholar
STN ISO 540 (44 1363) (2010). Hard Coal and Coke. Determination of Ash Fusibility.Google Scholar
Trömel, G, Obst, K-H, Konopnicky, K, Bauer, H & Patzak, I (1957). Ber Dtsch Keram Ges 34, 397–402. In Steel Institute VDEh, Schlackenatlas, 1. Auflage, Publisher Stahleisen, Düsseldorf, Germany, 1981. p. 31. ISBN 3-514-00228-2.Google Scholar
Veit, U & Rüssel, C (2016). Density and Young's modulus of ternary glasses close to the eutectic composition in the CaO-Al2O3-SiO2–system. Ceram Int 42, 5810–5822.CrossRefGoogle Scholar
Volf, MB (1978). Chemie skla/Chemistry of Glass, 1st ed. SNTL Praha, p. 472 (in Czech).Google Scholar
Xin, J, Wang, N, Chen, M & Gan, L (2019). Accurate density calculation for molten slags in SiO2-Al2O3-CaO-MgO-‘FeO’-‘Fe2O3’ systems. ISIJ Int 59/5, 759–767.CrossRefGoogle Scholar
Zhang, R, Min, Y, Wang, Y, Zhao, X & Liu, C (2020). Structural evolution of molten slag during the early stage of basic oxygen steelmaking. ISIJ Int 60, 212–219.CrossRefGoogle Scholar