Tuning the Tunability in Epitaxial Barium Strontium Titanate Film via Internal Stresses

Published online by Cambridge University Press:  11 February 2011

Z.-G. Ban
Affiliation:
Department of Metallurgy and Materials Engineering and Institute of Materials Science, University of Connecticut, Storrs, CT 06269
S. P. Alpay
Affiliation:
Department of Metallurgy and Materials Engineering and Institute of Materials Science, University of Connecticut, Storrs, CT 06269
Get access

Abstract

The tunability of epitaxial barium strontium titanate films is analyzed theoretically for the first time using a modified phenomenological Landau-Devonshire approach taking into account the formation of unusual ferroelectric phases that cannot form in bulk and single-crystal ceramics. It is shown that enhanced tunability can be achieved by adjusting the misfit strain especially in the vicinity of a structural phase transformation. The internal stresses in epitaxial films as characterized by the misfit strain can be controlled by changing the substrate material and/or varying the film thickness. The latter is due to the possibility of stress relaxation by formation of misfit dislocations that relieve epitaxial stresses at film growth temperature. Based on the thermodynamic model, we provide quantitative estimations of tunability of (001) Ba0.5Sr0.5TiO3 films on (001) LaAlO3 (LAO) and SrTiO3 (STO) as a function of film thickness. The analysis indicates that films on STO substrates should be as thick as possible in order to achieve optimum tunability. To obtain maximum tunability on LAO substrates, the thickness of films should be as close as possible to a critical film thickness (∼120 nm).

Type
Research Article
Copyright
Copyright © Materials Research Society 2003

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Summerfelt, S., (Ba,Sr)TiO3 Thin Films for DRAM's, in Thin Film Ferroelectric Materials and Devices, edited by Ramesh, R. (Kluwer Academic Publisher, Boston, 1997), p. 1.Google Scholar
2. Chang, W., Gilmore, C.M., Kim, W.-J., Pond, J.M., Kirchoefer, S.W., Qadri, S.B., Chrisey, D.B. and Horwitz, J.S., J. Appl. Phys. 87, 3044 (2000).Google Scholar
3. Shaw, T.M., Trolier-McKinstry, S. and McIntyre, P.C., Annu. Rev. Mater. Sci. 30, 263 (2000).Google Scholar
4. Knauss, L.A., Pond, J.M., Horwitz, J.S., Chrisey, D.B., Mueller, C.H. and Treece, R., Appl. Phys. Lett. 69, 25 (1996).Google Scholar
5. Carlson, C.M., Rivikin, T.V., Parilla, P.A., Perkins, J.D., Ginley, D.S., Kozyrev, A.B., Oshadchy, V.N. and Pavlov, A.S., Appl. Phys. Lett. 76, 1920 (2000).Google Scholar
6. Ban, Z.-G. and Alpay, S.P., J. Appl. Phys. 91, 9288 (2002).Google Scholar
7. Pertsev, N.A., Zembilgotov, A.G. and Tagantsev, A.K., Phys. Rev. Lett. 80, 1988 (1998).Google Scholar
8. Landolt-Börnstein, , Numerical Data and Functional Relationships in Science and Technology, Vol. 16, edited by Hellwege, K.-H. and Hellwege, A.M. (Springler-Verlag, Berlin, 1981).Google Scholar
9. Pertsev, N.A., Tagantsev, A.K. and Setter, N., Phys. Rev. B 61, R825 (2000).Google Scholar
10. Yamada, T., J. Appl. Phys. 43, 328 (1972).Google Scholar
11. Hilton, A.D. and Ricketts, B.W., J. Phys. D: Appl. Phys. 29, 1321 (1996).Google Scholar
12. Matthews, J.W. and Blakeslee, A.E., J. Crystal Growth 27, 118 (1974).Google Scholar
13. Alpay, S.P. and Roytburd, A.L., J. Appl. Phys. 83, 4714 (1998).Google Scholar
14. van der Merve, J.H., J. Appl. Phys. 34, 123 (1963).Google Scholar
15. Alpay, S.P., Nagarajan, V., Bendersky, A., Vaudin, M.D., Aggarwal, S., Ramesh, R. and Roytburd, A.L., J. Appl. Phys. 85, 3271 (1999).Google Scholar