Chemical Routes to Improved Mechanical Properties of PECVD Low K Thin Films
Published online by Cambridge University Press: 17 March 2011
Abstract
Increasing the elastic modulus and hardness of low K films is one of the key challenges towards integration of these materials into future integrated circuits. Several approaches are explored for increasing the hardness of carbon doped oxide (CDO) dielectrics. Several low K precursors and their mixtures specifically chosen to enhance the hardness (H) and modulus (E) of CDO films through chemically induced cross-linking. Composition and FTIR measurements suggest the presence of C-C and C-Si cross-linking with concurrent observation of improved film hardness and modulus at relatively low deposition temperatures. Films deposited at 373°C using diethoxy-methyl-oxiranyl have a hardness and modulus of 2.5 GPa and 18.1 GPa respectively. Films deposited at 180°C using tetramethylcyclotetrasiloxane (TMCTS) and 25% hardener have hardness and modulus of 1.5 GPa and 9.4 GPa, respectively. These film properties are significantly higher than those observed for TMCTS alone under similar deposition conditions. Based on these results a low temperature process with 25% hardener and 75% TMCTS combined with a porogen was used to produce a porous film with a k<2.5 and a hardness of 0.72GPa.
- Type
- Research Article
- Information
- Copyright
- Copyright © Materials Research Society 2004
References
- 4
- Cited by