Determination of the Adhesive Strength of Film-Substrate Interfaces Using the Constant Depth Scratch Test

Published online by Cambridge University Press:  21 February 2011

I. Dutta  and
J. C. Campbell
I. Dutta
Affiliation:
Department of Mechanical Engineering, Naval Postgraduate School, Monterey, CA 93943.
J. C. Campbell
Affiliation:
Department of Mechanical Engineering, Naval Postgraduate School, Monterey, CA 93943.
Get access

Abstract

A constant depth scratch test (CDST) has been recently developed to quantify the shear strength of film-substrate interfaces. This test is capable of measuring interfacial adhesion as a function of position on the sample surface during a continuous scratch. Unlike many of the currently available tests which are applicable to a limited array of materials systems, or are experimentally complex, this test is quite versatile, and is relatively straightforward to conduct and interpret because of the constant depth geometry. The theoretical basis and the experimental set-up for the test have been previously presented. In this paper, extensions of the theoretical formulation to account for different debonding behaviors of different film-substrate systems are discussed. Experimental results generated with a number of systems, including chromium on glass, gold on aluminum nitride, gold on aluminum nitride with a chromium inter-layer, and polycrystalline diamond on aluminum nitride are presented.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 390: Symposium S – Electronic Packaging Materials Science VIII , 1995 , 49
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Strong, J., Rev. Sci. Instrum., 6 (1935) 97.Google Scholar
2. Williams, R. C. and Backus, R. C., J. Appl. Phys., 20 (1949) 98.Google Scholar
3. Annual Book of ASTM Standards, Standard Test Methods for Adhesion of Metallic Coatings, v. 2.05 (1991) 327.Google Scholar
4. Heavens, O. S., J. Phys. Radium, 11 (1950) 355.Google Scholar
5. Benjamin, P. and Weaver, C., Proc. Roy. Soc., A254 (1960) 163.Google Scholar
6. Kuwahara, K., Hirota, H. and Umemeto, N. in Adhesion Measurements on Thin Films, Thick Films and Bulk Coatings, Mittal, K. L., ed., ASTM STP 640, ASTM, Philadel. (1978) 198.Google Scholar
7. Kuwahara, K., Nakahara, S. and Nakagawa, T., in Supplement to Transactions, Japan Inst. Metals, 9 (1968) 1034.Google Scholar
8. Krongelb, S. in Adhesion Measurements on Thin Films, Thick Films and Bulk Coatings, Mittal, K. L., ed., ASTM STP 640, ASTM, Philadel. (1978) 107.Google Scholar
9. Vossen, J. L. in Adhesion Measurements on Thin Films, Thick Films and Bulk Coatings, Mittal, K. L., ed., ASTM STP 640, ASTM, Philadel. (1978) 122.Google Scholar
10. Gupta, V., Argon, A. S., Cornie, J. A. and Parks, D. M., Mater. Sci. Eng., A126 (1990) 105.Google Scholar
11. Spies, G. J., J. Aircraft Eng., 25 (1953) 64.Google Scholar
12. Aravas, N., Kim, K. S. and Loukis, M. J., Mater. Sci. Eng., A107 (1989) 159.Google Scholar
13. Marshall, D. B. and Evans, A. G., J. Appl. Phys., 56 (1984) 2632.Google Scholar
14. Rossington, C., Evans, A. G., Marshall, D. B. and Khuri-Yakub, B. T., J. Appl. Phys., 56 (1984) 2639.Google Scholar
15. Engel, P. A., Int. J. Adhesion and Adhesives, 5 (1984) 455.Google Scholar
16. Lin, M.R., Ritter, J. E., Rosenfeld, L. and Lardner, T.J., J. Mater. Research, 5 (1990) 1110.Google Scholar
17. W. Sachsem Kim, K. Y. and Conway, H. D., Proc. MRS Symp., 154 (1989) 293.Google Scholar
18. Valli, J., Makela, U., Matthews, A. and Murama, V., J. Vacuum Sci. Tech., A3 (1985) 2411.Google Scholar
19. Julia-Schmutz, C. and Hintermann, H. E., Surface and Coatings Tech., 48 (1991) 1.Google Scholar
20. Wu, T. W., J. Mater. Res., 6 (1991) 407.Google Scholar
21. Venkataraman, S. K., L.Kohlstedt, D. and Gerberich, W.W., Thin solid Films, 223 (1993) 269.Google Scholar
22. Dutta, I., Lascurain, D.P. and Secor, E.D., Mat. Res. Soc. Symp., 338 (1994) 507.Google Scholar
23. Matthewson, M. J., Appl. Phys. Lett., 49 (1986) 1426.Google Scholar
24. Ritter, J. E., Lardner, T. J., Rosenfeld, L. and Lin, M. R., J. Appl. Phys., 66 (1989) 3626.Google Scholar
25. Hedenqvist, P., Olsson, M. and Jacobson, S., Surface and Coatings Tech., 41 (1990) 31.Google Scholar
26. Bull, S. J., Surface and Coatings Tech., 50 (1991) 25.Google Scholar