High Dielectric Constant Hf-Ti-Sn-O Off-Axis Cosputtered Films

Published online by Cambridge University Press:  10 February 2011

L. F. Schneemeyer
Affiliation:
Bell Laboratories, Lucent Technologies, Murray Hill, NJ 07974
R. B. van Dover
Affiliation:
Bell Laboratories, Lucent Technologies, Murray Hill, NJ 07974
R. M. Fleming
Affiliation:
Bell Laboratories, Lucent Technologies, Murray Hill, NJ 07974
Get access

Abstract

New Hf-Sn-Ti-O thin-film dielectric materials were explored using a compositional-spread approach. Thin films of composition Hf0.2Sn0.05Ti0.75O2 prepared at 250°C have excellent dielectric properties: 40-50 nm thick films with a dielectric constant of 40-60 were obtained, depending on the processing conditions, yielding a specific capacitance of 9-17 fF/µm2. Breakdown fields were measured to be about 4 MV/cm, yielding a Figure of Merit εε0Ebr=19 µC/cm2. Leakage currents, measured at 1 MV/cm, were in the range 10−7- 10−6 A/cm2. Film properties are strongly dependent on substrate temperature during deposition. Like their recently reported zirconium analogs, these materials are of interest for use in Si-IC device technology, for example as storage capacitors in DRAM.

Type
Research Article
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Shinriki, H. and Nakata, M., IEEE Trans. Electron Dev. ED–38, 455 (1991); K. W. Kwon, et al., IEDM Technical Digest 1994, pp.835-838. M.-B. Lee, et al., IEDM Tech. Dig. 1996, pp. 683-686.Google Scholar
2. Sun, S. C. and Chen, T. F., IEEE Electron Device Letters 17, 355 (1996).Google Scholar
3. Fujikawa, H. and Taga, Y., J. Appl. Phys. 75, 2538 (1994).Google Scholar
4. Dover, R. B. van, Schneemeyer, L. F. and Fleming, R. M., Nature 392, 162 (1998).Google Scholar
5. Sawatzky, E. and Kay, E., IBM J. Res. Develop. 13, 696 (1969)Google Scholar
6. Hanak, J. J., J. Mater. Sci. 5, 964 (1970).Google Scholar
7. Shannon, R. D., J. Appl. Phys. 73, 348 (1993).Google Scholar
8. Dover, R. B. van and Schneemeyer, L. F., IEEE Electron Device Letters 19, 329 (1998).Google Scholar
9. Wakino, K., Minai, K. and Tamura, H., J. Am. Ceram. Soc. 67, 278 (1984).Google Scholar
10. Sreemoolanadhan, H., Ratheesh, R., Sebastian, M. T. et al. , J. Phys. D 30, 1809 (1997).Google Scholar
11. Mackay, R., Sleight, A. W., and Subramanian, M. A., J. Solid State Chem. 121,437 (1996).Google Scholar