Hybrid Organic/Inorganic Coatings for Abrasion Resistance on Plastic and Metal Substrates

Published online by Cambridge University Press:  10 February 2011

J. Wen ,
K. Jordens  and
G. L. Wilkes
J. Wen
Affiliation:
Department of Chemical Engineering and Polymer Materials and Interfaces Laboratory, Virginia Polytechnic Institute and State University, Blacksburg, VA 24061
K. Jordens
Affiliation:
Department of Chemical Engineering and Polymer Materials and Interfaces Laboratory, Virginia Polytechnic Institute and State University, Blacksburg, VA 24061
G. L. Wilkes
Affiliation:
Department of Chemical Engineering and Polymer Materials and Interfaces Laboratory, Virginia Polytechnic Institute and State University, Blacksburg, VA 24061
Get access

Abstract

Novel abrasion resistant coatings have been successfully prepared by the sol-gel method. These materials are spin coated onto bisphenol-A polycarbonate, diallyl diglycol carbonate resin (CR-39) sheet, aluminum, and steel substrates and are thermally cured to obtain a transparent coating of a few microns in thickness. Following the curing, the abrasion resistance is measured and compared with an uncoated control. It was found that these hybrid organic/inorganic networks partially afford excellent abrasion resistance to the polycarbonate substrates investigated. In addition to having excellent abrasion resistance comparable to current commercial coatings, some newly developed systems are also UV resistant. Similar coating formulations applied to metals can greatly improve the abrasion resistance despite the fact that the coatings are lower in density than their substrates.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 435: Symposium V – Better Ceramics Through Chemistry VII , 1996 , 207
Copyright
Copyright © Materials Research Society 1996

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Kasi, J., JPn. Kokai Tokkyo Koho, JP 6335, 633 (88,35,633).Google Scholar
2. Schmidt, H., Walter, H., J. Non-Cryst. Solids 121, 428, (1990).Google Scholar
3. Wilkes, G. L., Orler, B., Huang, H. H., Polymer Preprints 26(2), 300, (1985).Google Scholar
4. Huang, H., Glaser, R. H., Wilkes, G. L., ACS Symp. Ser. 360, 354, (1988).Google Scholar
5. Huang, H., Wilkes, G. L., Polymer 30, 2001, (1989).Google Scholar
6. Betrabet, C., Wilkes, G. L., Polymer Preprints 32(2), 286, (1992).Google Scholar
7. Tamami, B., Betrabet, C., Wilkes, G. L., Polymer Bulletin 30, 39, (1993).Google Scholar
8. Tamami, B., Betrabet, C., Wilkes, G. L., Polymer Bulletin 30, 393, (1993).Google Scholar
9. Wang, B. and Wilkes, G.L., J. Macromol. Sci.-Pure Appl. Chem. A31, 249, (1994).Google Scholar
10. Wang, B., Wilkes, G. L., Smith, C. D., McGrath, J. E., Polymer Commu. 32, 400, (1991).Google Scholar
11. Betrabet, C. and Wilkes, G. L., J. Inorganic & Organometallic Polymers 4, 343, (1994)Google Scholar
12. Wang, B; Wilkes, G. L. US patent 5,316,855.Google Scholar
13. Betrabet, C. S.; Wilkes, G. L. J. Inorganic & Organometallic Polym. 4, 343, (1994).Google Scholar
14. Wen, J. and Wilkes, G. L., Journal of Inorganic & Organometallic Polymers 5, 343, (1995).Google Scholar
15. Wen, J., Vasudevan, V. J., and Wilkes, G. L., J. Sol-Gel Science & Technology 5, 115, (1995).Google Scholar
16. Wen, J. and Wilkes, G. L., PMSE Preprints 73, 429, (1995).Google Scholar
17. Jordens, K. and Wilkes, G. L., PMSE Preprints 73, 290, (1995).Google Scholar