Published online by Cambridge University Press: 01 February 2011
Half-Heusler phases have gained recently much interest as thermoelectric materials. Screening of possible systems was performed by drawing their stability region in a three-dimensional Pettifor map. The fabrication of Half-Heusler phases requires three steps, surface activation of the raw material by ball milling, arc-melting of pressed pellets and finally long-term annealing treatment in a vacuum furnace. On doped TiCoSb specimens, Seebeck coefficients of 0.1 mV/K, on NiNbSn 0.16 mV/K were measured, although the microstructure was not yet optimized.