Shape Memory Effect through L10-fcc Order-Disorder Transition

Published online by Cambridge University Press:  26 February 2011

K. Tanaka
K. Tanaka*
Affiliation:
Department of Advanced Materials Science, Kagawa University, Takamatsu 761–0396, Japan
Get access

Abstract

Shape memory effect not associated with martensitic transformation but with order-disorder phase transformation is examined in the compounds of AuCu, CoPt and FePd. These exhibit the L10-fcc transition at 680K, 1060K and 950K, respectively, which is relatively high temperature. Under a uniaxial compressive stress, a reversible shape change (reduction and elongation in edge length) is observed by cooling and heating the specimen temperature. The elongation of the specimen associated with the disordering occurs at their equilibrium transition temperatures, and the reduction along the direction of a compressive stress associated with the ordering occurs at a certain supercooled temperature. A trial actuator constructed with FePd polycrystalline wire and a conventional inconel wire properly works by heating up and cooling down the temperature.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 842: Symposium S – Integrative and Interdisciplinary Aspects of Intermetallics , 2004 , S3.8
Copyright
Copyright © Materials Research Society 2005

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Otsuka, K., Oda, K., Ueno, Y., Piao, M., Ueki, T., and Horikawa, H., Scripta Met. Mater., 29, 1355 (1993).Google Scholar
2. Otsuka, K. and Ren, X., Intermetallics, 7, 511 (1999).Google Scholar
3. Fonda, R. W., Jones, H. N. and Vandermeer, R. A., Scripta Mater., 39, 1031 (1998).Google Scholar
4. Hirabayashi, M., J. Phys. Soc. Jpn., 14, 149 (1959).Google Scholar
5. Ohta, M., Shiraishi, T., Ouchida, R., Nakagawa, M. and Matsuya, S., J. Alloys and Comp., 265, 240 (1998).Google Scholar
6. Tanaka, K., Ichitsubo, T. and Koiwa, M., Mater. Sci. Eng., A312, 118 (2001).Google Scholar
7. Tanaka, K. and Morioka, K., Phil. Mag., 83, 1797 (2003).Google Scholar
8. Roberts, B. W., Acta Met., 2, 597 (1954).Google Scholar
9. Leroux, C., Cadeville, M. C., Pierron-Bohnes, V., Inden, G. and Hinz, F., J. Phys. F, 18, 2033 (1988).Google Scholar