The formation of hydroxy-Al-interlayered montmorillonite was affected by complexing organic acids. Montmorillonite (<2.0 μm) was aged for three months at an initial pH of 5.0 or 6.0 in AlCl3 solutions containing citric or tannic acid at organic acid/Al molar ratios from 0 to 1.0. The Al/clay ratio in the system was 900 meq Al3+/100 g of montmorillonite. Ion-exchange experiments revealed that organically complexed Al ions have both positive and negative charges. Evidence from X-ray powder diffraction, electron microscopic examination, measurements of specific surface, cation-exchange capacity, organic carbon, and the nature of sorbed Al indicates that citric and tannic acids influence differently the hydroxy-Al interlayer formation in montmorillonite. Hydroxy-Al-citrate can be adsorbed as interlayers in montmorillonite, but hydroxy-Al-tannate exists principally as a separate phase binding the clay particles. The differences observed between the influence of citric and tannic acids on Al interlayering are probably due to their differences in molecular weight (size) and structure.

The purpose of this study was to investigate the clay mineral phases in a Rhodic Acrisol soil and to discuss their evolution in subtropical conditions. Prairie and forest soil profiles were sampled and clay fractions of the parent material and soil horizons analysed by X-ray diffraction (XRD) at the Federal University of Santa Maria, Rio Grande do Sul-Brazil. The XRD results show the presence of interstratified kaolinite-smectite and illite-smectite as well as illite in the parent material. These minerals were also found in the soil samples but with two new phases: hydroxy-aluminium interlayered vermiculite (HIV), which showed incomplete collapse with treatment at 550ºC, and a newly formed kaolinite (d = 7.17 Å). Under a subtropical climate and a sandy lithology, HIV and kaolinite appear to be a result of a specific pedogenic clay formation, related to the natural vegetation. Originally, under the prairie area, the intensity of the weathering processes was weak (within 2:1 clay minerals), as only small quantities of kaolinite and Fe oxides, and no evidence of gibbsite, were found.