Inverse gas chromatography (IGC) at zero surface coverage was used for determining the surface characteristics of a slate sample. Previously this sample had been characterized by means of X-ray diffraction (XRD), chemical analysis, infrared (IR) spectroscopy and nitrogen adsorption. Quartz, muscovite and chlorite were the minerals foming the slate. A well-defined mesoporous structure with pores of 15 Å of interlayer distance was observed. Chemical analysis and IR spectroscopy corroborated the X-ray results. The surface characteristics of the slate were defined in relation to nonspecific and specific interactions with organic molecules. In accordance with the nonspecific interactions, the London component (γSD) of the surface free energy gave an estimation of the surface energy of the slate sample. The obtained values for γSD were 140.0, 124.8, 108.2 and 96.8 mN m-1 at 100, 110, 120 and 130 °C, respectively. These values were characteristic of an inorganic sample of high surface energy. The values of the thermodynamic variables—differential heat of adsorption, free energy and entropy of adsorption—were in accordance with these results. At the same time, specific interactions were characterized by the ηπ parameter and the acid-base (KA, KB) indices. The positive value of ηπ (0.09 kJ mol-1) indicated the presence of Lewis acidic sites on the slate surface. The value of KA (acid index) of 1.17 was higher than the value of KB (base index) of 0.37; this result confirmed the acidic nature of the studied slate's surface.

Oil recovery is strongly related to the wettability of reservoir rocks that are formed of quartz grains attached by mineral hydroxides and clay minerals. Illites and kaolinites are the most active due to their high specific surface areas and electrical charge densities. Therefore, these minerals’ relative affinities for oil or water when in contact with a water-oil mix are of great importance. In order to model such a complex system, we used a mix of organic model molecules of the oil constituents and water vapor. Their interactions were estimated by inverse gas chromatography (IGC). IGC experiments were performed using a carrier gas with controlled humidity. By means of IGC at infinite dilution conditions, the dispersive component of the surface energy, γsd, was determined. A strong decrease of γsd, due to water molecules shielding the highest-energy sites, was observed. The energetic surface heterogeneity of the clays was examined using IGC at finite concentration conditions, allowing the determination of organic probe adsorption isotherms in the presence of water. From these isotherms, adsorption energy distribution functions were computed for propanol-2 and pyridine probes. Water mainly modifies the illite distribution functions, whereas practically no change was observed in the case of kaolinite. This observation is related to the higher hydrophilicity of illite as compared with kaolinite, and explains the different behaviors of the 2 clay families in oil reservoirs.

Inverse gas chromatography at infinite dilution, employing alkanes and alkenes as probes, has been used to characterize the surface properties of a series of smectites of varying chemical composition. The results of this study show that the acidic centers and the interlayer distances have a great influence on the specific interaction of the smectite surface with π-bonds of alkenes. High values of the specific interaction parameter, ɛπ, are caused by the existence of strong acidic centers that are connected with interlayer cations as well as with the chemical structure of the mineral sheets. On the other hand, alkanes, whose interaction with the smectites is predominantly dispersive, are unaffected by changes in the clays’ composition and/or structure.

The sorption properties of carbon-composite materials based on montmorillonite and hydrotalcite matrices have been studied using nitrogen adsorption isotherms and inverse gas chromatography. Carbon composite materials derived from both types of inorganic precursors contain pore structure accessible for adsorbate molecules. Adsorption capacity per unit mass of these composite adsorbents is larger in the case of hydrotalcite than in montmorillonite-based materials. Exposing these materials to ambient conditions results in their hydration. Subsequent water removal by heating under vacuum increases nitrogen adsorption capacity, which is explained by the opening of the adsorption space. The water content of hydrated samples and its effect on adsorption capacity is greater for the case of hydrotalcite-based materials. No direct relationship between carbon content and adsorption properties of the materials studied is observed.

The most common means of reducing the particle size of solids is by grinding, a process which can affect the surface properties and the behavior of the solid in later stages (granulation, compaction, etc.), and which can influence the end-use properties of the final product. Inverse gas chromatography (IGC) measurements were used here to evaluate the influence of grinding, in a ball mill, on attapulgite. The milling experiments were performed in dry media for various periods. After 30 min of grinding, significant decreases in the particle size and specific surface areas were observed when calculated using different probes. No noticeable variation in the surface properties was observed by IGC either at infinite dilution or at finite concentration, however. In particular, the distribution functions of the adsorption energies (DFAE), giving information about the surface heterogeneity for both an apolar probe (octane) and a polar probe (isopropanol), remained unchanged, regardless of the grinding time. The stability of the surface energy with respect to the grinding process was seen to be related to the particular fibrous structure of the attapulgite clay.

The present paper shows the importance of Inverse Gas Chromatography (IGC) for the determination of the surface properties of bentonites. These properties are dispersive surface energy, acid-base properties, surface heterogeneity, sorption isotherms, BET surface areas and heat of sorption, using different probe molecules. IGC can contribute to the interpretation, prediction and optimization of the studied materials' properties. The paper focuses on two distinctive bentonite samples from Porto Santo Island, Madeira archipelago. In view of their potential value, achieved through their incorporation in products for dermopharmacy and dermocosmetics, particle size and particle surface properties are of fundamental importance.