Boiling glauconite from the El-Gideda area of Egypt in different concentrations of HCl and H2SO4 for different periods led to a modified structure. Treatment resulted in progressive destruction of the structure, leaving X-ray amorphous silica and only relics of the original mineral. The glauconitic material was modified structurally in order to increase its adsorption activity. The glauconite was evaluated in terms of mineralogy, chemistry, morphology, structural modification, octahedral cation leaching rate, surface area and cation exchange capacity using X-ray diffraction, infrared spectroscopy, X-ray fluorescence, scanning electron microscopy and surface area analysis. The ratio of extracted octahedral cations to the total octahedral cations in the untreated glauconite was taken as a measure of octahedral sheet decomposition. A progressive decrease in crystallinity and the formation of X-ray amorphous silica Si-O vibration bands at 1100, 800 and 494 cm−1 accompanied octahedral cation depletion. Acid activation using 2 M and 4 M HCl for 6 h destroyed 30% and 61% of the octahedral sheet, respectively. In contrast, similar treatment using 2.9 and 5.5 M H2SO4 destroyed 48% and 93% of the octahedral sheet, respectively. Depending on the extent of cation depletion, the 4 M HCl product surface areas were as high as 259 m2/g, whereas the surface area of the 5.5 M H2SO4 product was only 63 m2/g. The progressive increase in surface area was due to glauconite morphology alteration. Acid-induced dissolution of Al, Fe, Mg cations from octahedral sheet edges led to a wedge-like splitting of the glauconite crystals, mesopore creation, and greater access to interlayer galleries.

This study focused on the structure and physical properties of acid-treated bentonite L45 from the Lieskovec deposit (Slovakia). New applications of near infrared and visible spectroscopies were used to follow Fe-montmorillonite dissolution and layer-charge reduction. Progressive dissolution of L45 results in the formation of a protonated amorphous silica phase. The OH overtone at 7312 cm–1 revealed the creation of Si–OH groups in the mildly treated samples. The area of the Si–O–Moct band, as obtained by a peak-fitting procedure, is a sensitive indicator of the changes in the octahedral sheets. Ultraviolet-visible (UV-VIS) spectroscopy of the smectite dispersions with methylene blue (MB) is an efficient method for controlling the acid activation process of bentonites. The results reveal that acid treatment causes a substantial layer-charge reduction, probably due to prevailing dissolution of MgO4(OH)2 polyhedra in the octahedral sheets. The layer-charge reduction is proportional to the structural changes and to the extent of mineral decomposition upon acid treatment.

Two kaolins containing kaolinites of different crystallinity, as confirmed by the Aparicio-Galán-Ferrell index, were treated in HCl and KOH solutions at 95º and 80ºC, respectively, for periods up to 36 h. Changes resulting from the treatments have been characterized by several methods. Fe occurs in the octahedral sheets of both kaolinites and dissolves similarly to Al. Lower structural ordering, more structural defects and particles of smaller average size and less regular shape are responsible for faster dissolution of KGa-2 in comparison to well ordered Gold Field (Tanzania) kaolinite. More Si than Al is dissolved in KOH from both kaolins after any dissolution time. An aluminosilicate (feldspathoid) phase is thought to occur in the material prepared from KGa-2 in KOH. Near-IR spectra provide very useful information on changes in the mineral structure upon the treatments, on the solid reaction products and on the adsorbed water molecules.

Une méthode proposant d'estimer l'effet de modifications structurales distribuées est exposée ici. Une évolution des formulations classiques permettant de prendre en compte la non-coïncidence des points de mesure et des points de couplage est présentée. La mise en œuvre de la méthodologie à un exemple académique et à un cas d'application industriel permet de mettre en lumière les avantages de la méthodologie exposée.