Three different bioactive materials suitable as dentine substitutes in tooth repair have been studied: glass-ionomer cement, particulate bioglass, and calcium-silicate cement. On 15 permanent human molars, Class V cavities were prepared and the bottom of each cavity was de-mineralized by an artificial caries gel. After the de-mineralization, the teeth were restored with: (1) Bioglass®45S5 and ChemFil® Superior; (2) Biodentine™ and ChemFil® Superior; and (3) ChemFil® Superior for a complete repair. The teeth were stored for 6 weeks in artificial saliva, then cut in half along the longitudinal axis: the first half was imaged in a scanning electron microscope (SEM) and the other half was embedded in resin and analyzed by SEM using energy-dispersive X-ray analysis. The glass-ionomer and the bioglass underwent ion exchange with the surrounding tooth tissue, confirming their bioactivity. However, the particle size of the bioglass meant that cavity adaptation was poor. It is concluded that smaller particle size bioglasses may give more acceptable results. In contrast, both the glass-ionomer and the calcium-silicate cements performed well as dentine substitutes. The glass-ionomer showed ion exchange properties, whereas the calcium silicate gave an excellent seal resulting from its micromechanical attachment.

A series of synthetic calcium silicates has been produced comprising nano-sized plates. The starting calcium silicate referred to as nano-structured calcium silicate, NCS, appears itself X-ray amorphous but contains impurities of calcite. These impurities decompose during the dry thermal conversion of the material into wollastonite. NCS can be enriched with calcium or silicon, respectively. The silicon enriched NCS can be hydrothermally transformed into a sheet material related to Ca7Si16O38(OH)2. The X-ray pattern of this material was sufficient to allow the calculation of its unit cell with a comparatively high figure of merit. The calcium enriched NCS can form two very distinctly different ceramic materials upon hydrothermal treatment, one a band material (formed below 200 °C) and the other a rose petal shaped material (formed above 210 °C). The X-ray diffraction patterns could not be resolved. The fit between the observed and calculated patterns was less than 50% as expressed in comparatively low figures of merit (unusually <20), which is attributed to calcium carbonate impurities in the samples disrupting the long range order. The patterns of these calcium enriched samples could be best compared to those of tobermorite or truscotite.

Silicon (Si) can improve resistance of plants to insect attack and may also enhance tolerance of water stress. This study tested if Si-mediated host plant resistance to insect attack was augmented by water stress. Four sugarcane cultivars, two resistant (N21, N33) and two susceptible (N26, N11) to Eldana saccharina Walker were grown in a pot trial in Si-deficient river sand, with (Si+) and without (Si−) calcium silicate. To induce water stress, irrigation to half the trial was reduced after 8.5 months. The trial was artificially infested with E. saccharina eggs after water reduction and harvested 66 days later. Silicon treated, stressed and non-stressed plants of the same cultivar did not differ appreciably in Si content. Decreases in numbers of borers recovered and stalk damage were not associated with comparable increases in rind hardness in Si+ cane, particularly in water-stressed susceptible cultivars. Overall, Si+ plants displayed increased resistance to E. saccharina attack compared with Si− plants. Borer recoveries were significantly lower in stressed Si+ cane compared with either stressed Si− or non-stressed Si− and Si+ cane. Generally, fewer borers were recovered from resistant cultivars than susceptible cultivars. Stalk damage was significantly lower in Si+ cane than in Si− cane, for N21, N11 and N26. Stalk damage was significantly less in Si+ combined susceptible cultivars than in Si− combined susceptible cultivars under non-stressed and especially stressed conditions. In general, the reduction in borer numbers and stalk damage in Si+ plants was greater for water-stressed cane than non-stressed cane, particularly for susceptible sugarcane cultivars. The hypothesis that Si affords greater protection against E. saccharina borer attack in water-stressed sugarcane than in non-stressed cane and that this benefit is greatly enhanced in susceptible cultivars is supported. A possible active role for soluble Si in defence against E. saccharina is proposed.