The composition of carbides in steel, measured by atom probe tomography, can be influenced by limitations in the ion detector system. When carbides are analyzed, many ions tend to field evaporate from the same region of the specimen during the same laser or voltage pulse. This results in a so-called multiple event, meaning that several ions impact the detector in close proximity both in time and space. Due to a finite detector dead-time not all ions can be detected, a phenomenon known as detector pile-up. The evaporation behavior of carbon is often different than the evaporation behavior of metals when analyzing alloy carbides, leading to preferential loss of carbon ions, and a measured carbon concentration below the expected value. This effect becomes stronger as the overall detection efficiency gets higher. Here, the detection efficiency was deliberately reduced by inserting a grid into the flight-path, which resulted in a higher and more correct carbon concentration, accompanied by an increase in the statistical uncertainty.

Small additions of boron can remarkably improve the long-term creep resistance of 9–12% Cr steels. The improvement has been attributed to boron segregation to grain boundaries during quenching, and subsequent boron incorporation into certain families of precipitates during tempering. However, the detailed mechanisms are not yet fully understood. Atom probe tomography (APT) is an excellent technique for gaining insights into boron distribution, however, in order to acquire accurate analysis of boron in 9–12% Cr steels using APT, there are several key challenges. In order to better understand and address these challenges, we developed a novel method for site-specific APT specimen preparation, which enables convenient preparation of specimens containing specifically selected grain boundaries positioned approximately perpendicular to the axis of the APT tip. Additionally, when analyzing boron at boundaries and in carbides (as diluted solute) and borides, a widening of the profile of boron distribution compared to other elements was repeatedly observed. This phenomenon is particularly analyzed and discussed in light of the evaporation field of different elements. Finally, the possible effects of detector dead-time on quantitative analysis of boron in metal borides are discussed. A simple method using 10B correction was used to obtain good quantification.

In this research, the effect of austenitizing at 900–1100 °C and tempering at 250–650 °C on the microstructure and mechanical properties of 410 and 410 Ni martensitic stainless steels was investigated. The transformation of austenite to ferrite surrounded the austenitizing within the temperature range of 900–1050 °C. The grain size and hardness measurements proved that austenitizing at 1050 °C leads to the partial dissolution of carbides without a considerable growth of austenite grains. The mechanical tests showed two peaks in strength and troughs in ductility by tempering at 450 and 650 °C due to the formation of primary and secondary carbides. The better ductility and fracture toughness in 410 Ni, comparing to 410, were attributed to the effect of Ni on stacking fault energy. Fractured surfaces revealed ductile fracture of the samples tempered at low temperatures, e.g., 250 °C. However, after tempering at 450 and 650 °C, 410 showed a brittle fracture and 410 Ni exhibited a dual intergranular-brittle fracture mechanism.

The microstructural evolution of spray-formed high speed steel during hot deformation was investigated as well as the effects of spray forming parameters on the porosity formation. Four distinct zones are identified in the as-deposited material, and interstitial porosity is present in the bottom and peripheral zones, while gas-related porosity is mainly found in the central zone. It can keep the porosity at a minimum value by using the optimum parameters, e.g., the average porosity of central zone is 3.7% for a superheat of 170 °C and a gas-to-metal flow rate of 0.7. During hot deformation at 1150 °C, the amount of porosity can be obviously decreased by increasing the height reduction which also plays a key role in breaking up eutectic carbides. The critical height reduction for the breakdown of the eutectic carbides is 50%, the dominant mechanism being mechanical fragmentation.

Carbide precipitation within low carbon AISI H13 hot work tool steel that had either been quenched at 80 °C or cryogenically treated at −196 °C prior to tempering has been examined using micrometer-scale synchrotron diffraction mapping. Vanadium-rich cubic M8C7 carbide, lattice parameter of approximately 0.8610 nm, not identifiable using laboratory powder x-ray diffraction (PXRD), was found to be present in all samples. The concentration of this phase was greatest in the rapidly cooled cryogenically treated sample. However, all cryogenic treatments resulted in greater carbide concentrations than in the quenched sample. In addition rapid cryogenic cooling by immersion in liquid nitrogen (N2), as compared with slow cooling to −196 °C over a 3 h duration, results in greater order within the carbide phase subsequent to tempering, as interpreted by analysis of unit cell size variation, and the smallest stress, as interpreted by diffraction peak full width half maximum height distributions.

Producing high purity aluminum nitride crystals by the sublimation-recondensation technique is difficult due to the inherently reactive crystal growth environment, normally at temperature in excess of 2100 °C. The durability of the furnace fixture materials (crucibles, retorts, etc.) at such a high temperature remains a critical problem. In the present study, the suitability of several refractory materials for AlN crystal growth is investigated, including tantalum carbide, niobium carbide, tungsten, graphite, and hot-pressed boron nitride. The thermal and chemical properties and performance of these materials in inert gas, as well as under AlN crystal growth conditions are discussed. TaC and NbC are the most stable crucible materials with very low elemental vapor pressures in the crystal growth system. Compared with refractory material coated graphite crucibles, HPBN crucible is better for AlN self-seeded growth, as crystals tend to nucleate in thin colorless platelets with low dislocation density.