Activation energies for the intermixing reaction of textured metal-metal multilayer thin films have been determined using X-ray diffraction analysis. Kinetic data were collected utilizing an area detector so as to reduce intensity bias from changes in out-of-plane texture during the intermixing reaction. Activation energies for Al/Pt, Ni/Ti, and Co/Al metal-metal multilayer thin films have been determined as 95.4(2) kJ/mol, 201(13) kJ/mol, and 247(19) kJ/mol, respectively.

In situ laboratory-based and in situ synchrotron X-ray diffraction techniques were employed to study quantitatively the strain-induced austenite-to-martensite (A–M) transformation in thermally cycled (TC) superelastic NiTi alloys. The propagation of the A–M interfaces and the evolution of the microstructure were traced during uniaxial tensile loading. It was shown that the TC material exhibits localized transformation via the propagation of transformation bands. The amount of the martensite phase depends approximately linearly on the applied strain. Analysis of the broadening of the austenite diffraction lines indicates the presence of highly deformed austenite grains within the transformation bands. Analysis of the austenite diffraction-line shifts indicates that the overall lattice strain in the (retained) austenite in the transformation bands differs from that of the austenite in the adjacent untransformed regions.

Focused ion beam specimen preparation has been used for NiTi samples and SrTiO3/SrRuO3 multilayers with prevention of surface amorphization and Ga implantation by a 2-kV cleaning procedure. Transmission electron microscopy techniques show that the samples are of high quality with a controlled thickness over large scales. Furthermore, preferential thinning effects in multicompounds are avoided, which is important when analytical transmission electron microscopy measurements need to be interpreted in a quantitative manner. The results are compared to similar measurements acquired for samples obtained using conventional preparation techniques such as electropolishing for alloys and ion milling for oxides.