This issue of MRS Bulletin provides an overview of the current status of research and development in the area of high-temperature superconductor (HTS) wires. High-temperature oxide superconductors, discovered in the late 1980s, are moving into the second generation of their development.The first generation relied on bismuth strontium calcium copper oxide, and the second generation is based on yttrium barium copper oxide, which has the potential to be less expensive and to perform better.The potential uses of HTS wires for electric power applications include underground transmission cables, oil-free transformers, superconducting magnetic-energy storage units, fault-current limiters, high-efficiency motors, and compact generators.Wires of 10–100 m in length can now be made, but material and processing issues must be solved before an optimized production scheme can be achieved.This issue covers a range of processing techniques using energetic beams, rolling, and laser and chemical methods to form wires with good superconducting properties.

This article provides an overview of the fabrication of epitaxial, biaxially aligned buffer layers on rolling-assisted biaxially textured substrates (RABiTS) as templates for YBCO films carrying high critical current densities.The RABiTS technique uses standard thermomechanical processing to obtain long lengths of flexible, biaxially oriented substrates with smooth surfaces.The strong biaxial texture of the metal is conferred to the superconductor by the deposition of intermediate metal and/or oxide layers that serve both as a chemical and a structural buffer.Epitaxial YBCO films with critical current densities exceeding 3 106A/cm2at 77K in self-field have been grown on RABiTS using a variety of techniques and demonstrate magnetic-field-dependent critical current values that are similar to those of epitaxial films on single-crystal ceramic substrates.The RABiTS architecture most commonly used consists of a CeO2 (sputtered)/YSZ (sputtered)/Y203 (e-beam)/Ni-W alloy.

The desired texture of the base metal has been achieved in 100 m lengths and 10cm widths.Scaleable and cost-effective techniques are also being pursued to deposit the epitaxial multilayers.The results discussed here demonstrate that this technique is a viable route for the fabrication of long lengths of high-critical-current-density wire capable of carrying high currents in magnetic fields and at temperatures accessible by cooling with relatively inexpensive liquid nitrogen (up through the 77K range).