Vernadite (MnO2·nH2O) is a mineral with a poorly ordered structure. Its synthetic analogue is designated δ-MnO2. Birnessite and vernadite are independent mineral species and cannot be described further under the same name. They have similar hexagonal unit-cell parameters, a0, but different c0 parameters. Rancieite has a structure similar to that of birnessite. Calcium bearing, 14-Å birnessite occurring in nature was first described by the authors. In addition to the todorokite having the parameters a0 = 9.75 Å, b0 = 2.84 Å, and c0 = 9.59 Å, other species of natural todorokite are known having a0 parameters that are multiples of 4.88 Å equal to 14.6 and 24.40 Å, the b0 and c0 parameters being the same.

The oxidation of As(III) to As(V) by K-birnessite was examined at different temperatures, pHs, and birnessite/As(III) ratios. Experiments ranged in duration from 5 to 64 hr, and solution and solid products were determined at several intervals. All experiments showed that the reaction produced large amounts of K+ to solution and very little Mn2+. As(V) was released to solution and incorporated into the K-birnessite. The oxidation was initially rapid and then slowed. The oxidation of As(III) was probably facilitated initially by autocatalytic Mn-As(V) reactions occurring mostly in the interlayer, in which large amounts of As(V) and K+ could be easily released to solution. The reaction also slowed when interlayer Mn was exhausted by forming Mn-As(V) complexes. Mn(IV) could only be acquired from the octahedral sheets of the birnessite. The two-stage reaction process proposed here depended on the layered structure of birnessite, the specific surface, and presence of exchangeable cations in K-birnessite.

The rate and extent of oxidation of dihydroxybenzenes (DHB) to quinones in acetate-buffered suspensions of synthetic birnessite were studied using Mn dissolution to monitor reaction progress. Concentration of free Mn2+ in the aqueous phase was continuously monitored by electron spin resonance, and ultraviolet-visible (UV-VIS) spectroscopy was utilized to quantify dihydroxybenzene and quinone concentrations. Although dissolution of the oxide and release of Mn2+ to solution generally accompanied phenol oxidation, a threshold oxidation level had to be exceeded before Mn2+ appeared in solution. Once this threshold was surpassed, the mole quantity of Mn2+ dissolved equaled the mole quantity of organic oxidized for 1,4-DHB, but exceeded the quantity of organic oxidized for 1,2-DHB. Thus, the latter phenol was more efficient in dissolving the oxide. Soluble phosphate suppressed Mn2+ release without influencing the degree of organic oxidation, suggesting that phosphate chemically interacted with reduced Mn to hinder its dissolution. UV spectra provided tentative evidence for the transitory existence of Mn3+-1,4-DHB complexes in the solution phase.

Infrared spectra of the birnessite after reaction with 1,4-DHB indicated some new features, which may have been a result of the reduction of surface Mn atoms to the 3+ oxidation state. These features were not present after reaction with 1,2-DHB, confirming that the latter phenol efficiently dissolved the oxide to release Mn2+. Although the initial Mn dissolution was very rapid and was attributed to a surface reaction, further slow Mn release accompanied by more complete oxidation of the phenols suggests a process limited by the rate of dissolution of the solid.

Investigations were conducted to determine the hydrothermal transformations of synthetic birnessite exchanged with different metal ions. Autoclaving in a Teflon-lined stainless steel pressure vessel at 155°C for 24 hr of Mg-, Ca-, La-, and Co-saturated birnessite yielded manganese minerals having 10-Å X-ray powder diffraction (XRD) spacings. The autoclaved Mg-birnessite yielded a mineral identical to natural todorokite in its infrared (IR) spectrum and XRD patterns. High-resolution transmission electron microscopy (HRTEM) provided images having 10-, 12.5-, 15-, and 20-Å wide fringes indicating heterogeneous channel widths in the crystallographic a direction, and IR spectroscopy produced bands at 757, 635, 552, 515, 460, and 435 cm-1, confirming the product obtained by autoclaving Mg-birnessite to be todorokite. Prolonged autoclaving of Mg-birnessite yielded manganite (γ-MnOOH) as a by-product; manganite did not form when the autoclaving time was shortened to 8 hr. Also, when Ca-saturated samples were autoclaved, the product gave d-values of 10 Å, but the XRD lines were broad and heterogeneity of the channel sizes was evident from HRTEM observations. The Ca-derivative had an IR spectrum similar to that of natural todorokite. Images showing 10-Å lattice fringes were observed by HRTEM for the Ni-saturated sample, which also produced an XRD pattern similar to that of the Mg-saturated sample. Co- and Lasaturated samples did not form todorokite, although HRTEM of La-saturated samples indicated some 10-Å lattice fringes that were unstable in the electron beam. Birnessite saturated with Na, K, NH4, Cs, Ba, or Mn(II) gave products having 7-Å spacings upon autoclaving.

Although numerous, small, manganese oxide deposits associated with dolomite in the Eastern Transvaal escarpment, Republic of South Africa, have been known for many years, their mineralogical make-up is somewhat controversial. Chemical, mineralogical, and morphological properties of the weathering products of dolomite and the coexisting manganese oxide material in the Graskop area were therefore determined. Mn and Fe occur only in minor accessory minerals in the original rock; however, in the weathering residue, these elements are concentrated and occur as separate mineral phases, chiefly birnessite, nsutite, and goethite. Thin veins of pure muscovite and quartz traverse the residua. Rare, pure calcite and maghemite nodules were noted throughout the residual manganese material. The properties of this weathering sequence suggest that the manganese wad deposits were formed in situ as a result of the congruent dissolution of dolomite, leaving a porous, sponge-like structure, highly enriched in Mn and Fe oxides.

The transformation of hausmannite (Mn3O4) into a K-bearing, 7-Å phyllomanganate (K-birnessite) in KOH was followed using X-ray powder diffraction and transmission electron microscopy. The transformation involved dissolution of Mn3O4 followed by reprecipitation of the 7-Å phase. The rate-determining step was the dissolution of Mn3O4. The reaction was accelerated by increasing the pH and/or the temperature of the system.

K-birnessite precipitated initially as thin, irregular plates and films that gradually recrystallized to thicker, more structured plates and laths. A pseudohexagonal unit cell with a0 = 2.87 Å and c0 = 7.09 Å was found for this phase. Synthetic K-birnessite was stable in KOH at 70°C for many months. In neutral to slightly acidic media it converted rapidly to Mn7O13•5H2O, and in more acid media, it dissolved and reprecipitated as γ-MnO2. The replacement of K+ by Na+ was not achieved. Jacobsite and magnetite also underwent a dissolution/reprecipitation transformation in KOH.

The sorption properties of Co, Cu, Ni, and Ca were studied in a mixed mineral suspension of synthetic MnO2 and Wyoming montmorillonite. The distribution of the sorbed cations between the two solid phases was measured by indirect chemical fractionation with acidified NH2OH-HCl and by direct X-ray spectroscopic analysis of mineral particles using electron microscopy. Electron microscope and NH2OH-HCl measurements of the quantity of Co sorbed on MnO2 agreed within 6%. Seventy-seven, 67, and 69% of the total Co, Cu, and Ni sorbed by the mixed mineral suspension was found on the manganese oxide. The opposite distribution was found for sorbed Ca with 28% on the manganese oxide and 72% on the montmorillonite particles. The observed differences in metal sorption by these minerals are related to the cation-sorption mechanisms of manganese oxide and montmorillonite.

The structure of a highly disordered synthetic birnessite was studied by comparing powder X-ray diffraction (XRD) data with calculated patterns generated by BIRNDIF and WILDFIRE© in an attempt to describe the nature of disorder and to estimate the size of the coherent diffracting domains. The material has a turbostratic stacking sequence and coherent diffracting domains that are 25 to 30 Å on a side in the ab plane (N1 = 5 unit cells, N2 = 10 unit cells) and which average 2.5 unit cells thick parallel to c. Turbostratic stacking probably results because there are few constraints on the relationship between adjacent layers.

The amount of Mn2+ adsorbed or removed from solution by birnessite is several times greater than its reported cation exchange capacity. Extractability of the sorbed Mn2+ decreases with aging. It is uncertain whether the sorbed Mn2+ is oxidized on the surface or incorporated into the structure of birnessite. Using X-ray powder diffractometry and transmission electron microscopy, a study was conducted to examine the mineralogical alteration of birnessite after treatment with various concentrations of MnSO4 and solution pH.

The sorbed Mn2+ was not directly oxidized and remained on the birnessite surface. The sorption of Mn2+ was followed by alteration of birnessite with the formation of new Mn minerals. The specific Mn minerals formed were governed by the pH of the reaction, and the rate of the transformation was determined by Mn2+ concentration and pH. Nsutite and ramsdellite were identified at pH 2.4, crypto-melane at pH 4, groutite at pH 6, and manganite at pH 8. Other Mn minerals formed at these and other pH levels could not be identified. As the concentration of Mn in the solution decreased, the time required to form new minerals from the birnessite increased. The newly formed phases were the result of structural conversion since dissolution of birnessite and reprecipitation of new phases were not observed.

Lithiophorite is a naturally occurring Mn oxide mineral commonly found in soils and sediments. The usual method of synthesizing lithiophorite is via a hydrothermal process in an autoclave at relatively high temperature and pressure. In the present study, an alternative, reflux method, at atmospheric pressure, for synthesis of lithiophorite was developed successfully. The influence of reaction duration, temperature, type of precursor birnessite (H-birnessite, Na-birnessite, aged Na-birnessite), and pH on the formation of lithiophorite were investigated by reflux treatment of lithium-aluminum hydroxide complex ion ()-exchanged birnessite. The results show that the degree of conversion of lithiophorite decreases with decreasing reaction temperature. Lithiophorite can be obtained at pH values from 5.0 to 9.0, but a circumneutral pH is more favorable for formation at atmospheric pressure. Conversion of Na-birnessite (Bir-OH) to lithiophorite is more favored than aged Na-birnessite (Bir-OH-A). Lithiophorite was not obtained by refluxing the ion-exchanged H-birnessite (Bir-H) sample. The rate of conversion of lithiophorite increases with increasing reflux time. Lithiophorite synthesized by a reflux process has pseudo-hexagonal crystals of 0.1–0.5 µm with a chemical composition of Li0.24Al0.46MnO2.67(H2O)1.25. The results have important implications for the origin and underlying mechanism of lithiophorite formation in the environment.

An O2 oxidation and freeze-dry procedure has been used to synthesize birnessite through the oxidation of Mn2+ in alkali media. The effects of O2 flow rate, the fluxion velocity of reaction suspension, the reaction temperature, pretreatment the reaction solutions with N2, and the hydration conditions on the purity of birnessite, the crystallinity, the ion-exchange properties, and the phase transformation of intermediate phases were examined. Buserite with a 1 nm basal spacing, produced after the oxidation, is transformed to 0.7 nm Na birnessite by complete freeze drying. Increasing the fluxion velocity of the reaction suspension and the O2 flow rate facilitated oxidation of Mn(OH)2. Prephase I (a phase related to hausmannite, γ-Mn3O4 (Luo and Suib, 1997; Luo et al., 1998), and feitknechtite (β-MnOOH) were formed as intermediates during the synthesis. Mechanical stirring was used to change the fluxion velocity of the reactive suspension. When the speed of stirring and the O2 flow rate were raised to 250 rpm and 3.0 L/min, respectively, or 450 rpm and 2.0 L/min, respectively, birnessite was the only phase in the final product. Irrespective of temperature in other reactions, pure birnessite was synthesized as long as the temperature during the initial mixing of the reaction solutions was maintained below 10°C. Increasing the reaction temperature led to a larger crystal size, better crystallinity and lower surface area. The pretreatment of solutions with N2 or O2 had little effect on the synthesis; synthesized birnessites had the same purity (100%) as, and similar crystallinity to, that of the no-pretreatment control. Dehydration of the buserite by freeze drying and heating at 60°C did not affect the production of birnessite; however, the latter caused partial loss of ion-exchange capacity with Mg2+. The pathways of the birnessite formation in this study might be:

1. (1) Mn(OH)2 (amorphous) → feitknechtite → buserite → birnessite, and

2. (2) Mn(OH)2 (amorphous) → prephase I → feitknechtite → buserite → birnessite

Mn(OH)2 existed in an X-ray amorphous state, not in the form of ‘pyrochroite’, during the synthesis.

The adopted conditions for synthesis of pure birnessite were NaOH to Mn molar ratio of 13.7, O2 flow rate of 2 L/min and oxidation for 5 h during vigorous stirring at 450 rpm at room temperature. The birnessite synthesized had a hexagonal platy morphology with good crystallinity, an average composition of Na0.25MnO2.07.0.66H2O, and a surface area of 38 m2/g.

Todorokite is a common Mn oxide (with a tunnel structure) in the Earth surface environment, and can be obtained by hydrothermal treatment or refluxing process from precursor buserite with a layered structure. Several chemical reaction conditions for the phase transformation from Na-buserite to todorokite at atmospheric pressure were investigated, including temperature, pH, crystallinity of precursor Na-buserite, the amount of the interlayer Mg2+ of the Mg-buserite and clay minerals. The results showed that the conversion rate and crystallinity of todorokite decreased with falling temperature, and Mg-buserite could not be completely transformed to todorokite at lower temperatures (40°C). The poorly crystalline Na-buserite could be converted into todorokite more easily than highly crystalline Na-buserite. Todorokite can be prepared at pH 5–9, but the rate of conversion and crystallinity of todorokite did vary with pH in the order: neutral ≈ alkali > acidic. The conversion rate of todorokite decreased with decreasing interlayer Mg2+ content of the Mg-buserite. The presence of montmorillonite or goethite slowed the formation reaction of todorokite in the refluxing process, and the reaction time was prolonged when the amounts of those minerals were increased.

Birnessite can be used as a precursor in the preparation of manganese oxides. Synthesis of pure birnessite is difficult because of a side reaction, which yields hausmannite. This study aimed to develop a modified oxidation-deprotonation reaction (ODPR) method to eliminate the formation of hausmannite, and to investigate the influence of alkalinity on the synthetic products. In contrast to the conventional synthesis of birnessite through oxygen or permanganate oxidation, the ODPR method can produce birnessite without any impurities, within 5 h, and in a reproducible fashion. The distinctive feature of the ODPR method is the bubbling of N2 gas into NaOH and Mn2+ solutions before mixing the NaOH with Mn2+, in order to keep oxygen away from each solution. As soon as white pyrochroite was formed, oxygen gas was forced in as an oxidant to initiate the oxidation reaction. A black suspension with a blue tint appeared after 5 h of reaction. These precipitates were collected and examined by X-ray diffraction (XRD), scanning electron microscopy (SEM), infrared (IR) and Raman spectroscopy. The average oxidation state of the Mn oxides was also determined. The results showed that pure birnessite with good crystallinity was formed. Oxidation of 1 M NaOH mixed with Mn2+ solution formed random-stacked birnessite. However, the oxidation of 4 M NaOH mixed with Mn2+ formed birnessite. Random-stacked birnessite can be transformed into birnessite by ageing suspensions at 313 to 373 K.

Freshwater ferromanganese nodules (FFN) from Green Bay, Lake Michigan have been investigated by X-ray powder diffraction (XRD), micro X-ray fluorescence (XRF), scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), and scanning transmission electron microscopy (STEM). The samples can be divided into three types: Mn-rich nodules, Fe-Mn nodules, and Fe-rich nodules. The manganese-bearing phases are todorokite, birnessite, and buserite. The iron-bearing phases are feroxyhyte, goethite, 2-line ferrihydrite, and proto-goethite (intermediate phase between feroxyhyte and goethite). The XRD patterns from nodule cross sections suggest the transformation of birnessite to todorokite. The TEM-EDS spectra show that todorokite is associated with Ba, Co, Ni, and Zn; birnessite is associated with Ca and Na; and buserite is associated with Ca. The todorokite has an average chemical formula of Ba0.28p2+(Zn0.14p+2Co0.05p3+Ni0.02p2+) (Mn4.99p4+Mn0.82p3+Fe0.12p3+Co0.05p3+Ni0.02p2+) O12·nH2O. Barium is the main cation in the structural tunnels of the todorokite. The average chemical formula of birnessite and Ca-buserite are: Na0.14p+Ca0.19p2+(Mn1.48p4+Mn0.52p3+0.52) O4·nH2O and Ca0.27p2+(Mn1.46p4+Mn0.54p3+)O4·nH2O, respectively. Most nodules have a concretionary structure of alternating Fe/Mn layers, commonly with a core of reddish feldspar containing phyllosilicates and hematite micro-crystals. Other cores consist of goethite, cristobalite, tridymite, hercynite, hematite-bearing quartz, coal, and chlorite-bearing rock fragments. The hexagonal or hexagonal-like structures of hematite micro-crystals and clay minerals in the cores may serve as heterogeneous nucleation sites for the Mn-oxides and Fe-(oxyhydr)oxides. The alternating Fe/Mn layers in FFNs might be caused by oscillatory redox condition fluctuations at the sediment-water interface due to changes in water level.

Lithiophorite is a naturally occurring phyllomanganate which has been identified in soils and ores. Studies on a synthetic version have shed light on the conditions required for the formation of lithiophorite. In this study, we successfully prepared lithiophorite under highly alkaline conditions. In addition, we found that Li+, Al3+ and hydrothermal treatment are all necessary for the formation of lithiophorite. Lithiophorite, birnessite and Li-intercalated gibbsite were examined by infrared (IR) spectroscopy. The Mn oxide sheets of lithiophorite and birnessite were found to have quite similar structural environments. On the other hand, the LiAl2(OH)6 sheets are affected more markedly by the Mn oxide sheets. After intercalation, the symmetry of the six interlayer OH groups of LiAl2(OH)6 is reduced and they are divided into two groups occupying different sites, corresponding to the IR absorption bands at 3480 and 3312 cm−1, respectively.

The relationship between vacant Mn structural sites in birnessites and heavy-metal adsorption is a current and important research topic. In this study, two series of birnessites with different average oxidation states (AOS) of Mn were synthesized. One birnessite series was prepared in acidic media (49.6–53.6 wt.% Mn) and the other in alkaline media (50.0–56.2 wt.% Mn). Correlations between the Pb2+ adsorption capacity and the d110 interlayer spacing, the AOS by titration, and the release of Mn2+, H+, and K+ during adsorption of Pb2+ were investigated. The maximum Pb2+ adsorption by the birnessites synthesized in acidic media ranged from 1320 to 2457 mmol/kg with AOS values that ranged from 3.67 to 3.92. For birnessites synthesized in alkaline media, the maximum Pb2+ adsorption ranged from 524 to 1814 mmol/kg, with AOS values between 3.49 and 3.89. Birnessite AOS values and Pb2+ adsorption increased as the Mn content decreased. The maximum Pb2+ adsorption to the synthetic birnessites calculated from a Langmuir fit of the Pb adsorption data was linearly related to AOS. Birnessite AOS was positively correlated to Pb2+ adsorption, but negatively correlated to the d110 spacing. Vacant Mn structural sites in birnessite increased with AOS and resulted in greater Pb2+ adsorption. Birnessite AOS values apparently reflect the quantity of vacant sites which largely account for Pb2+ adsorption. Therefore, the Pb2+ adsorption capacity of birnessite is mostly determined by the Mn site vacancies, from which Mn2+, H+, and K+ released during adsorption were derived.

Crystal truncation rod (CTR) X-ray diffraction is an invaluable tool for measuring mineral surface and adsorbate structures, and has been applied to several environmentally and geochemically important systems. Traditionally, the method has been restricted to single crystals with lateral dimensions >3 mm. Minerals that meet this size criterion represent a minute fraction of those that are relevant to interfacial geochemistry questions, however. Crystal screening, data collection, and CTR measurement methods have been developed for crystals of <0.3 mm in lateral size using the manganese oxide mineral chalcophanite (ZnMn3O7·3H2O) as a case study. This work demonstrates the feasibility of applying the CTR technique to previously inaccessible surfaces, opening up a large suite of candidate substrates for future study.

The role of Mn oxide in the abiotic formation of humic substances has been well demonstrated. However, information on the effect of crystal structure and surface-chemical characteristics of Mn oxide on this process is limited. In the present study, hexagonal and triclinic birnessites, synthesized in acidic and alkali media, were used to study the influence of the crystal-structure properties of birnessites on the oxidative polymerization of hydroquinone and to elucidate the catalytic mechanism of birnessites in the abiotic formation of humic-like polymers in hydroquinone-birnessite systems. The intermediate and final products formed in solution and solid-residue phases were identified by UV/Visible spectroscopy, atomic absorption spectrometry, Fourier-transform infrared spectroscopy, X-ray diffraction, solid-phase microextraction-gaschromatography-mas ss pectrometry, ion chromatography, and ultrafiltration. The degree of oxidative polymerization of hydroquinone wasenhanced with increase in the interlayer hydrated H+, the average oxidation state (AOS), and the specific surface area of birnessites. The nature of the functional groups of the humic-like polymers formed was, however, almost identical when hydroquinone was catalyzed by hexagonal and triclinic birnessites with similar AOS of Mn. The results indicated that crystal structure and surface-chemistry characteristics have significant influence on the oxidative activity of birnessites and the degree of polymerization of hydroquinone, but have little effect on the abiotic formation mechanism of humic-like polymers. The proposed oxidative polymerization pathway for hydroquinone isthat, asit approachesthe birnessite, it formsp recursor surface complexes. Asa strong oxidant, birnessite accepts an electron from hydroquinone, which is oxidized to 1,4-benzoquinone. The coupling, cleavage, polymerization, and decarboxylation reactionsaccompany the generation of 1,4-benzoquinone, lead to the release of CO2 and carboxylic acid fragments, the generation of rhodochrosite, and the ultimate formation of humic-like polymers. These findings are of fundamental significance in understanding the catalytic role of birnessite and the mechanism for the abiotic formation of humic substances in nature.

The formation of manganese (Mn) oxides is influenced by environmental conditions and, in some red soils, Mn oxides occur as coatings on the surface of kaolinite particles in the form of colloidal films or fine particles. The present study aimed to explore the types of formation mechanisms of Mn oxide minerals on the surface of kaolinite. Mn oxide minerals synthesized by reducing the Mn in KMnO4 with a divalent Mn salt (MnSO4) were examined using X-ray diffraction (XRD) and scanning electron microscopy (SEM). The effects of various initial molar ratios of Mn2+/Mn7+ (R = 1:0.67, 1:1, 1:2, and 1:4), cationic species (Na+ or Mg2+), synthesis temperatures (30, 60, and 110°C), and amount of added kaolinite (0.25, 0.5, 1.0, 2.0, and 5.0 g) on the formation of Mn oxides were studied. The results showed that Mn oxide mineral types were affected by the initial R value and the background cation. With decreases in the initial R value, the synthesized minerals transformed from cryptomelane to birnessite. The relative mass ratios of kaolinite to Mn oxide were calculated as 1:0.92, 1:0.63, 1:1.15, and 1:1.63. The sodium cation (Na+) had a greater role than Mg2+ in promoting the dissolution–recrystallization of birnessite to cryptomelane. The synthesis temperature had no effect on mineral types, but Mn content increased as temperature increased. When the amount of added kaolinite was increased from 0.25 to 5.0 g, Mn oxide minerals formed gradually and transformed from birnessite to cryptomelane. This work revealed a possible formation process and reaction mechanism on the surface of kaolinite particles in some red soils.

Todorokite is a common manganese oxide mineral, with a tunnel structure, found in Earth surface environments, and is easily synthesized from layered birnessite. The aim of the current study was to prepare birnessites with different average manganese oxidation states (AOS) by controlling the ${\text{MnO}}_4^{-}{\text{/Mn}}^{2+}$\$\end{document} ratio in concentrated NaOH or KOH. A series of (Na,K)-birnessites, Na-birnessites, and K-birnessites with different AOS was synthesized successfully in strongly alkaline media. The (Na,K)-birnessites and Na-birnessites prepared in NaOH clearly contained both large (500–1000 nm) and small (40–400 nm), plate-shaped crystallites. The K-birnessites prepared in KOH media consisted mostly of irregular (100–200 nm), plate-shaped crystallites. The degree of transformation of birnessite to todorokite at atmospheric pressure decreased as the AOS values of (Na,K)-birnessites and Na-birnessites increased from 3.51 to 3.80. No todorokite was present when a Na-birnessite with an AOS value of 3.87 was used as the precursor. Pyrophosphate, which is known to form strong complexes with Mn3+ at a pH range of 1–8, was added to a suspension of (Na,K)-birnessites in order to sequester the available Mn3+ in (Na,K)-birnessites. Removal of Mn3+ from birnessite MnO6 layers by pyrophosphate restricted transformation to todorokite — no (Na,K)-birnessite transformed to todorokite after pyrophosphate treatment. The interlayer K+ initially within (Na,K)-birnessites could not be completely ion-exchanged with Mg2+ to form todorokite at atmospheric pressure. No todorokite was forthcoming from K-birnessites even from those with small AOS values (3.50).