Fabrication and mechanical properties of Al/Al2O3 composite bodies by reactive infiltration of molten Al into SiO2 preform

Published online by Cambridge University Press:  31 January 2011

Noboru Yoshikawa ,
Singo Funahashi ,
Shoji Taniguchi  and
Atsushi Kikuchi
Noboru Yoshikawa*
Affiliation:
School of Metallurgy, Division of Engineering, Graduate Schools of Tohoku University, 02 Aza-Aoba, Aramaki, Aoba-ku, Sendai, Miyagi, Japan 980–8579
Singo Funahashi
Affiliation:
School of Metallurgy, Division of Engineering, Graduate Schools of Tohoku University, 02 Aza-Aoba, Aramaki, Aoba-ku, Sendai, Miyagi, Japan 980–8579
Shoji Taniguchi
Affiliation:
School of Metallurgy, Division of Engineering, Graduate Schools of Tohoku University, 02 Aza-Aoba, Aramaki, Aoba-ku, Sendai, Miyagi, Japan 980–8579
Atsushi Kikuchi
Affiliation:
School of Metallurgy, Division of Engineering, Graduate Schools of Tohoku University, 02 Aza-Aoba, Aramaki, Aoba-ku, Sendai, Miyagi, Japan 980–8579
*
a)Address all correspondence to this author.
Get access

Abstract

Al/Al2O3 composites were fabricated by a displacement reaction between SiO2 and molten Al. In this study, fabrication of Al/Al2O3 composites was attempted by means of reactive infiltration to provide variation of their mechanical properties. SiO2 preforms having various porosities and pore size distributions were prepared by sintering the powder at different temperatures between 1273 and 1723 K. Molten Al was infiltrated at 1373 K without application of pressure. Infiltration kinetics were studied and the microstructures of the composite bodies were observed by means of scanning electron microscopy (with energy dispersive x-ray microanalysis), wave dispersive x-ray microanalysis, and x-ray diffractions. The infiltrated specimens were mainly composed of Al and α–Al2O3 phases, and the Si content was less than 5 at.%. Volume fraction of Al phase in the composite bodies was not altered very much with the porosities of the SiO2 preforms because of the difficulty in filling out the entire pore space. Properties and microstructures of Al/Al2O3 composites, however, were dependent on the sintering temperature of the SiO2 preforms. In the case of low sintering temperature, a thick Al channel existed, which deformed upon compression. In the case of high sintering temperature, the microstructure became homogeneous and had thinner Al channels. The composite bodies became brittle. The deformation behavior was shown to be changed from ductile to brittle as an increase of the sintering temperature of the preforms.

Type
Articles
Information
Journal of Materials Research , Volume 15 , Issue 11 , November 2000 , pp. 2314 - 2321
Copyright
Copyright © Materials Research Society 2000

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Matsuo, S. and Inaba, T., Ceramics, 26, 222 (1991).Google Scholar
2.Breslin, M.C., Ringnalda, J., Xu, L., Fuller, M., Seeger, J., Daehn, G.S., Otani, T., and Fraser, H.L., Mater. Sci. Eng. A 195, 113 (1995).CrossRefGoogle Scholar
3.Fishman, S.G., In-Situ Composite Science and Technology, edited by Singh, M. and Lewis, D. (TMS, Pittsburgh, PA, 1994), pp. 1–19.Google Scholar
4.Newkirk, M.S., Urquhart, A.W., Zwicker, H.R., and Breval, E., J. Mater. Res. 1, 81 (1986).CrossRefGoogle Scholar
5.Antolin, S., Nagelberg, A.S., and Creber, D.K., J. Am. Ceram. Soc. 75, 447 (1992).CrossRefGoogle Scholar
6.Xiao, P. and Derby, B., J. Am. Ceram. Soc. 77, 1771 (1994).CrossRefGoogle Scholar
7.Gao, Y., Jia, J., Loehman, R.E., and Ewsuk, K.G., J. Mater. Res. 10, 1216 (1995).CrossRefGoogle Scholar
8.Ewsuk, K.G., Glass, S.J., Loehman, R.E., Tomsia, A.P., and Fahrenhortz, W.G., Met. Trans. 27A, 2122 (1996).CrossRefGoogle Scholar
9.Saiz, E. and Tomsia, A.P., J. Am. Ceram. Soc. 81, 2381 (1998).CrossRefGoogle Scholar
10.Loehman, R.E., Ewsuk, K., and Tomsia, A.P.J. Am. Ceram. Soc. 79, 27 (1996).CrossRefGoogle Scholar
11.Daehn, G.S., Starck, B., Xu, L., Elfishawy, K.F., Ringnalda, J., and Fraser, H.L., Acta Mater. 44, 249 (1996).CrossRefGoogle Scholar
12.Yoshikawa, N., Watanabe, Y., Veloza, Z.M., Kikuchi, A., and Taniguchi, S., J. Jpn. Inst. Metals 63, 312 (1999).CrossRefGoogle Scholar
13.Fahrenholtz, W.G., Ewsuk, K.G., Loehman, R.E., and Lu, P., J. Am. Ceram. Soc. 81, 2533 (1998).CrossRefGoogle Scholar
14.Saiz, E., Foppiano, S., MoberlyChan, W. and Tomsia, A.P., Composites, Part A 30, 399 (1999).CrossRefGoogle Scholar
15.Matsuo, S., Ito, K., Inaba, T., and Sakai, Y., Kinzoku 61 (1989).Google Scholar
16.Standage, A.E. and Gani, M.S., J. Am. Ceram. Soc. 50, 101 (1967).CrossRefGoogle Scholar
17.Hanabe, M. and Aswath, P.B., J. Mater. Res. 11, 1562 (1996).CrossRefGoogle Scholar
18.Hanabe, M. and Aswath, P.B., Acta Mater. 45, 4067 (1997).CrossRefGoogle Scholar
19.Zhou, X.Y., Deng, Z.D., Ying, T.Z., and Shen, H., Key Engineering Mateirals, (Trans. Tech. Publication, Switzerland, 1999), Vol. 161–163, pp. 99–106.Google Scholar
20.Tomsia, A.P., Saiz, E., and Loehman, E., Proc. of 6th Inter. Conf. on Ceramic Materials and Components for Engines (1997), pp. 62–66.Google Scholar
21.Kingery, W.D., Bowen, H.K., and Uhlmann, D.R., Introduction to Ceramics, 2nd ed. (John Wiley and Sons, New York, 1975), pp. 728–755.Google Scholar
22.Davidge, R.W., Mechanical Behavior of Ceramics (Cambridge University Press, Cambridge, United Kingdom, 1977), p. 82.Google Scholar