The ballistic failure mechanisms and sequence in semi-infinite. supported alumina tiles

Published online by Cambridge University Press:  31 January 2011

Dov Sherman  and
D. G. Brandon
Dov Sherman
Affiliation:
Department of Materials Engineering, Technion-Israel Institute of Technology, Haifa 32000, Israel
D. G. Brandon
Affiliation:
Department of Materials Engineering, Technion-Israel Institute of Technology, Haifa 32000, Israel
Get access

Abstract

The basic ballistic failure mechanisms and their sequence occurring in dense alumina tiles during projectile penetration were investigated. The alumina tiles were supported by semi-infinite support blocks made of three different materials. Initially, a drop-weight test (DWT) was used to gain an insight into the damage mechanisms and sequence during quasi-static impact conditions. The quasi-static damage mechanisms were compared with the damage obtained in 0.3 cal. armor-piercing tests (APT). The DWT's results suggested the following sequence of quasi-static failure mechanisms: Radial tensile cracks, associated with the low tensile strength of the ceramic formed initially, as a result of the bending induced by local deformation at the opposing surface. Subsequently, a shear-dominated cone crack propagated from the edge of the contact zone. If sufficient energy was available, crushing of the material beneath the contact zone developed during the final stages of failure. It is shown that these so-called “quasi-static” damage mechanisms, identified from the DWT's, also corresponded to the damage mechanisms and sequence during APT's.

Type
Articles
Information
Journal of Materials Research , Volume 12 , Issue 5 , May 1997 , pp. 1335 - 1343
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1.Ceramic Armor–Encyclopedia of Adv. Cer. Mat. (Pergamon Press, New York, 1991), pp. 22–24.Google Scholar
2.Laible, R. C., in Ballistic Materials and Penetration Mechanics, edited by Laible, R. C. (Elsevier Scientific Publishing, New York, 1980), pp. 133–143.Google Scholar
3.Wilkins, M. L., Cline, C. F., and Hondol, C. A., Tech. Rept. UCRL-50694, Lawrence Radiation Laboratory (1969).Google Scholar
4.Wilkins, M. L., in Ballistic Materials and Penetration Mechanics, edited by Laible, R. C. (Elsevier Scientific Publishing, New York, 1980), pp. 225–252.CrossRefGoogle Scholar
5.Ravid, M., Bodner, S. R., and Holcman, I., 10th International Symposium on Ballistics, California, 1987.Google Scholar
6.Ravid, M. and Bodner, S. R., Int. J. Eng. Eci. 21, 577–591 (1983).Google Scholar
7.Kolsky, H., Ballistic Materials and Penetration Mechanics, edited by Laible, R. C. (Elsevier Scientific Publishing, New York, 1980), pp. 185–222.CrossRefGoogle Scholar
8.Lee, Y. J., Int. J. Frac. 57, 25–46 (1992).Google Scholar
9.Ma, C. C. and Chen, S. K., Int. J. Frac. 58, 345–359 (1992).Google Scholar
10.Kobayashi, A. S., Mater. Sci. Eng. A143, 111–117 (1991).Google Scholar
11.Rosenberg, Z., Yeshurun, Y., and Brandon, D. G., J. de Phys. C5 (8), 331–341 (1985).Google Scholar
12.Shockey, D. A., Marchand, A. H., Skaggs, S. R., Cort, G. E., Burkett, M. W., and Parker, R., Int. J. Impact. Eng. 9, 263–275 (1990).CrossRefGoogle Scholar
13.Shockey, D. A., Rowcliffe, D. J., Dao, K. C., and Seaman, L., J. Am. Ceram. Soc. 73 (6), 1613–1619 (1990).Google Scholar
14.Field, J. E.et al., in Dynamic Behavior of Materials, edited by Meyers, M. A. (1994).Google Scholar
15.Follansbee, P. S., in Metals Handbook (1985), Vol. 8, pp. 198–203.Google Scholar
16.Viecknicky, D. J., Slavin, M. J., and Kliman, M. I., Ceram. Bull. 70 (6), 1035 (1991).Google Scholar
17.Ashby, M. F. and Hallam, S. D., Acta Metall. 34 (3), 497 (1986).Google Scholar
18.Lawn, B. R., Wilshaw, T. R., and Hartley, N. E. W., Int. J. Fracture 10, 1 (1974).Google Scholar
19.Mouginot, R. and Maugis, D., J. Mater. Sci. 20, 4354 (1985).Google Scholar