Enhanced microstructures and properties of spray-formed M3:2 high-speed steels by niobium addition and thermal-mechanical treatment

Published online by Cambridge University Press:  24 January 2019

Hebin Wang ,
Longgang Hou ,
Ping Ou ,
Xiaofeng Wang Open the ORCID record for Xiaofeng Wang [Opens in a new window] ,
Yabin Li ,
Li Shen ,
Hongjin Zhao ,
Hua Cui  and
Jishan Zhang
Hebin Wang
Affiliation:
School of Materials Science and Engineering, Jiangxi University of Science and Technology, Ganzhou 341000, China
Longgang Hou*
Affiliation:
State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083, China
Ping Ou*
Affiliation:
School of Materials Science and Engineering, Jiangxi University of Science and Technology, Ganzhou 341000, China
Xiaofeng Wang
Affiliation:
The Faculty of Mechanical Engineering and Mechanics, Ningbo University, Ningbo 315211, China
Yabin Li
Affiliation:
School of Materials Science and Engineering, Jiangxi University of Science and Technology, Ganzhou 341000, China
Li Shen
Affiliation:
School of Materials Science and Engineering, Jiangxi University of Science and Technology, Ganzhou 341000, China
Hongjin Zhao*
Affiliation:
School of Materials Science and Engineering, Jiangxi University of Science and Technology, Ganzhou 341000, China
Hua Cui
Affiliation:
State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083, China
Jishan Zhang
Affiliation:
State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083, China
*
a)Address all correspondence to these authors. e-mail: lghou@skl.ustb.edu.cn
b)e-mail: zhj_zyh@163.com
Get access

Abstract

M3:2 high-speed steel (HSS) billets with or without Nb addition were prepared by spray deposition. The effects of Nb and post-thermal-mechanical processing (decomposition treatment and hot forging), as well as heat treatment, on the microstructure and properties of M3:2 HSS were investigated. The microstructure of the as-deposited M3:2 HSS consisted of equiaxed grains with a mean size of approximately 25 μm and discontinuous plate-like M2C and irregular MC carbides distributed along grain boundaries. 0.5% Nb addition can refine the M2C plates and spheroidize MC carbides. With 2% Nb addition, the refined grains with a mean size of approximately 12 μm and continuous net of M6C and a uniform distribution of NbC carbides were obtained. The decomposition of metastable M2C carbides can be accelerated with 0.5% Nb addition due to the refined size and lower thermodynamic stability of M2C plates. With the increased degree of decomposition of M2C carbide, the M6C and MC carbides became refined and more uniformly distributed after optimal thermal-mechanical processing and heat treatment, which leads to a significant increase in bend strength and toughness.

Keywords

high-speed steelspray formingniobiumproperties
Type
Article
Information
Journal of Materials Research , Volume 34 , Issue 6 , 28 March 2019 , pp. 1043 - 1053
Copyright
Copyright © Materials Research Society 2019 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Pirtovšek, T.V., Kugler, G., Godec, M., and Terčelj, M.: Three important points that relate to improving the hot workability of ledeburitic tool steels. Metall. Mater. Trans. A 43, 3797 (2012).CrossRefGoogle Scholar
Guo, J., Ai, L.Q., Wang, T.T., Feng, Y.L., Wan, D.C., and Yang, Q.X.: Microstructure evolution and micro-mechanical behavior of secondary carbides at grain boundary in a Fe–Cr–W–Mo–V–C alloy. Mater. Sci. Eng., A 715, 359 (2018).CrossRefGoogle Scholar
Vitry, V., Nardone, S., Breyer, J.P., Sinnaeve, M., and Delaunois, F.: Microstructure of two centrifugal cast high speed steels for hot strip mills applications. Mater. Des. 34, 372 (2012).CrossRefGoogle Scholar
Deng, G.Y., Zhu, Q., Tieu, K., Zhu, H.T., Reid, M., Saleh, A.A., Su, L.H., Ta, T.D., Zhang, J., Lu, C., Wu, Q., and Sun, D.L.: Evolution of microstructure, temperature and stress in a high speed steel work roll during hot rolling: Experiment and modeling. J. Mater. Process. Technol. 240, 200 (2017).CrossRefGoogle Scholar
Serna, M.M. and Rossi, J.L.: MC complex carbide in AISI M2 high-speed steel. Mater. Lett. 63, 691 (2009).CrossRefGoogle Scholar
Zhou, X.F., Fang, F., Li, F., and Jiang, J.Q.: Morphology and microstructure of M2C carbide formed at different cooling rates in AISI M2 high speed steel. J. Mater. Sci. 46, 1196 (2011).CrossRefGoogle Scholar
Bombač, D., Terčelj, M., Fazarinc, M., and Kugler, G.: On the increase of intrinsic workability and hot working temperature range of M42 ledeburitic super high steel in as-cast and wrought states. Mater. Sci. Eng., A 703, 438 (2017).CrossRefGoogle Scholar
Mesquita, R.A. and Barbosa, C.A.: High-speed steels produced by conventional casting, spray forming and powder metallurgy. Mater. Sci. Forum 498, 244 (2005).CrossRefGoogle Scholar
Shen, W.J., Yu, L.P., Li, Z., He, Y.H., Zhang, Q.K., Zhang, H.B., Jiang, Y., and Lin, N.: In situ synthesis and strengthening of powder metallurgy high speed steel in addition of LaB6. Met. Mater. Int. 23, 1150 (2017).CrossRefGoogle Scholar
Garcia, C., Romero, A., Herranz, G., Blanco, Y., and Martin, F.: Effect of vanadium carbide on dry sliding wear behavior of powder metallurgy AISI M2 high speed steel processed by concentrated solar energy. Mater. Char. 121, 175 (2016).CrossRefGoogle Scholar
Zhang, D., Li, Z., Xie, L., Xiao, Y.F., and Yin, F.C.: Powder metallurgy of high speed steel produced by solid state sintering and heat treatment. Int. J. Mater. Res. 106, 870 (2015).CrossRefGoogle Scholar
Trabadelo, V., Giménez, S., and Iturriza, I.: Microstructural characterization of vacuum sintered T42 powder metallurgy high-speed steel after heat treatments. Mater. Sci. Eng., A 499, 360 (2009).CrossRefGoogle Scholar
Lavernia, E.J. and Srivatsan, T.S.: The rapid solidification processing of materials: Science, principles, technology, advances, and applications. J. Mater. Sci. 45, 287 (2010).CrossRefGoogle Scholar
Zhang, G.Q., Yuan, H., Jiao, D.L., Li, Z., Zhang, Y., and Liu, Z.W.: Microstructure evolution and mechanical properties of T15 high speed steel prepared by twin-atomiser spray forming and thermo-mechanical processing. Mater. Sci. Eng., A 558, 566 (2012).CrossRefGoogle Scholar
Jesus, E.R., Jesus, E.S., and Rossi, J.L.: Performance assessment of spray formed AISI M2 high-speed steel tools. Mater. Sci. Forum 530, 315 (2006).CrossRefGoogle Scholar
Grant, P.S.: Solidification in spray forming. Metall. Mater. Trans. A 38, 1520 (2007).CrossRefGoogle Scholar
Lu, L., Hou, L.G., Zhang, J.X., Wang, H.B., Cui, H., Huang, J.F., Zhang, Y.A., and Zhang, J.S.: Improved the microstructures and properties of M3:2 high-speed steel by spray forming and niobium alloying. Mater. Charact. 117, 1 (2016).CrossRefGoogle Scholar
Mesquita, R.A. and Barbosa, C.A.: Spray forming high speed steel-properties and processing. Mater. Sci. Eng., A 383, 87 (2004).CrossRefGoogle Scholar
Kim, C.K., Park, J.I., Lee, S., Kim, Y.C., Kim, N.J., and Yang, J.S.: Effects of alloying elements on microstructure, hardness, and fracture toughness of centrifugally cast high-speed steel rolls. Metall. Mater. Trans. A 36, 87 (2005).CrossRefGoogle Scholar
Pan, F.S., Ding, P.D., Zhou, S.Z., Kang, M., and Edmonds, D.V.: Effects of silicon additions on the mechanical properties and microstructure of high speed steels. Acta Mater. 45, 4703 (1997).CrossRefGoogle Scholar
Chaus, A.S.: Modifying cast tungsten-molybdenum high-speed steels with niobium, zirconium, and titanium. Met. Sci. Heat Treat. 47, 53 (2005).CrossRefGoogle Scholar
Park, J.W., Lee, H.C., and Lee, S.: Composition, microstructure, hardness, and wear properties of high-speed steel rolls. Metall. Mater. Trans. A 30, 399 (1999).CrossRefGoogle Scholar
Dobrzański, L.A. and Zarychta, A.: The structure and properties of W–Mo–V high-speed steels with increased contents of Si and Nb after heat treatment. J. Mater. Process. Technol. 77, 180 (1998).CrossRefGoogle Scholar
Mesquita, R.A. and Kestenbach, H.J.: Influence of silicon on secondary hardening of 5 wt% Cr steels. Mater. Sci. Eng., A 556, 970 (2012).CrossRefGoogle Scholar
Filipovic, M., Kamberovic, Z., Korac, M., and Gavrilovski, M.: Microstructure and mechanical properties of Fe–Cr–C–Nb white cast irons. Mater. Des. 47, 41 (2013).CrossRefGoogle Scholar
Hamidzadeh, M.A., Meratian, M., and Zahrani, M.M.: A study on the microstructure and mechanical properties of AISI D2 tool steel modified by niobium. Mater. Sci. Eng., A 556, 758 (2012).CrossRefGoogle Scholar
Zhi, X.H., Xing, J.D., Fu, H.G., and Xiao, B.: Effect of niobium on the as-cast microstructure of hypereutectic high chromium cast iron. Mater. Lett. 62, 857 (2008).CrossRefGoogle Scholar
Coelho, G.C., Golczewski, J.A., and Fischmeister, H.F.: Thermodynamic calculations for Nb-containing high-speed steels and white-cast-iron alloys. Metall. Mater. Trans. A 34, 1749 (2003).CrossRefGoogle Scholar
Pan, F.S., Wang, W.Q., Tang, A.T., Wu, L.Z., Liu, T.T., and Cheng, R.J.: Phase transformation refinement of coarse primary carbides in M2 high speed steel. Prog. Nat. Sci.: Mater. 21, 180 (2011).CrossRefGoogle Scholar
Fredriksson, H., Hillert, M., and Nica, M.: The decomposition of the M2C carbide in high speed steel. Scand. J. Metall. 8, 116 (1970).Google Scholar
Lee, E.S., Park, W.J., Baik, K.H., and Ahn, S.: Different carbide types and their effect on bend properties of a spray-formed high speed steel. Scr. Mater. 39, 1133 (1998).CrossRefGoogle Scholar
Lee, E.S., Park, W.J., Jung, J.Y., and Ahn, S.: Solidification microstructure and M2C carbide decomposition in a spray-formed high-speed steel. Metall. Mater. Trans. A 29, 1395 (1998).CrossRefGoogle Scholar
Luan, Y.K., Song, N.N., Bai, Y.L., Kang, X.H., and Li, D.Z.: Effect of solidification rate on the morphology and distribution of eutectic carbides in centrifugal casting high-speed steel rolls. J. Mater. Process. Technol. 210, 536 (2010).CrossRefGoogle Scholar
Mclaughlin, J., Kraft, R.W., and Goldstein, J.I.: Characterization of the solidification structures within the dendritic core of M2 high speed steel. Metall. Trans. A 8, 1787 (1977).CrossRefGoogle Scholar
Barkalow, R.H., Kraft, R.W., and Goldstein, J.I.: Solidification of M2 high speed steel. Metall. Trans. 3, 919 (1972).CrossRefGoogle Scholar
Fischmeister, H.F., Riedl, R., and Karagöz, S.: Solidification of high-speed tool steels. Metall. Trans. A 20, 2133 (1989).CrossRefGoogle Scholar
Zepon, G., Ellendt, N., Uhlenwinkel, V., and Bolfarini, C.: Solidification sequence of spray-formed steels. Metall. Mater. Trans. A 47, 842 (2016).CrossRefGoogle Scholar
Karagöz, S. and Fischmeister, H.F.: Niobium-alloyed high speed steel by powder metallurgy. Metall. Trans. A 19, 1395 (1988).CrossRefGoogle Scholar
Wang, H.B., Hou, L.G., Zhang, J.X., Lu, L., Cui, H., Huang, J.F., and Zhang, J.S.: Microstructures and high temperature properties of spray formed Nb-containing M3 high speed steel. Mater. Werkst. 45, 689 (2014).CrossRefGoogle Scholar
Wang, H.B., Hou, L.G., Zhang, J.X., Lu, L., Yu, Y.P., Cui, H., and Zhang, J.S.: Microstructures and properties of spray formed Nb-containing M3 high speed steel. Acta Metall. Sin. 50, 1421 (2014).Google Scholar
Henein, H., Uhlenwinkel, V., Fritsching, U.: Metal Spray and Spray Deposition, 1st ed. (Springer International Publishing, Cham, Switzerland, 2017); p. 320.CrossRefGoogle Scholar