Formation, corrosion behavior, and mechanical properties of bulk glassy Zr–Al–Co–Nb alloys

Published online by Cambridge University Press:  31 January 2011

Shujie Pang ,
Tao Zhang ,
Katsuhiko Asami  and
Akihisa Inoue
Shujie Pang
Affiliation:
Institute for Materials Research, Tohoku University, Sendai 980-8577, Japan
Tao Zhang
Affiliation:
Institute for Materials Research, Tohoku University, Sendai 980-8577, Japan
Katsuhiko Asami
Affiliation:
Institute for Materials Research, Tohoku University, Sendai 980-8577, Japan
Akihisa Inoue
Affiliation:
Institute for Materials Research, Tohoku University, Sendai 980-8577, Japan
Get access

Abstract

Bulk glassy Zr55Al20–xCo25Nbx (x = 0 to 5 at.%) alloys with critical diameters of 2.5–5 mm and supercooled liquid region of 48–75 K were produced by copper-mold casting. These alloys were spontaneously passivated in 3 mass% NaCl and 1 N H2SO4 solutions. The addition of Nb to the alloy enhanced the pitting corrosion resistance in the NaCl solution and enabled the open-circuit potential in the H2SO4 solution. Zr- and Al-enriched passive films formed on the bulk glassy Zr–Al–Co–Nb alloys exposed to air and on those immersed in the solutions. The increase in Nb content of the alloys resulted in an increase in Zr and Nb concentrations and a decrease in Al concentration of the passive film. The Vickers hardness, Young's modulus, compressive fracture strength, fracture strain, and plastic strain of the bulk glassy Zr–Al–Co–Nb alloys were 550, 98 GPa, 2100 MPa, 2.9%, and 0.9%, respectively.

Type
Articles
Information
Journal of Materials Research , Volume 18 , Issue 7 , July 2003 , pp. 1652 - 1658
Copyright
Copyright © Materials Research Society 2003

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Inoue, A., Zhang, T., and Masumoto, T., Mater. Trans., JIM 30, 965 (1989).Google Scholar
2.Zhang, T., Inoue, A., and Masumoto, T., Mater. Trans., JIM 32, 1005 (1991).Google Scholar
3.Inoue, A., Shibata, T., and Zhang, T., Mater. Trans., JIM 36, 1420 (1995).CrossRefGoogle Scholar
4.Peker, A. and Johnson, W.L., Appl. Phys. Lett. 63, 2342 (1993).Google Scholar
5.Inoue, A., Yokoyama, Y., Shinohara, Y., and Masumoto, T., Mater. Trans., JIM 35, 923 (1994).Google Scholar
6.Inoue, A., Zhang, T., Nishiyama, N., Ohba, K., and Masumoto, T., Mater. Trans., JIM 34, 1234 (1993).Google Scholar
7.Inoue, A., Mater. Trans., JIM 36, 866 (1995).Google Scholar
8.Inoue, A., Acta Mater. 48, 279 (2000).Google Scholar
9.Inoue, A., Mater. Sci. Eng. A304–306, 1 (2001).Google Scholar
10.Inoue, A., Yoshida, S., Mizushima, T., and Makino, A., in Supercooled Liquid Bulk Glassy and Nanocrystalline States of Alloys, edited by Inoue, A., Yavari, A.R., Johnson, W.L., and Dauskardt, R.H. (Mater. Res. Soc. Symp. Proc. 644, Warrendale, PA, 2001) pp. L12.13.1–L12.13.6.Google Scholar
11.Pang, S., Zhang, T., Kimura, H.M., Asami, K., and Inoue, A., Mater. Trans., JIM 41, 1490 (2000).Google Scholar
12.Hiromoto, S., Tsai, A.P., Sumita, M., and Hanawa, T., Corros. Sci. 42, 1651 (2000).Google Scholar
13.Hiromoto, S., Tsai, A.P., Sumita, M., and Hanawa, T., Corros. Sci. 42, 2167 (2000).Google Scholar
14.Hiromoto, S., Tsai, A.P., Sumita, M., and Hanawa, T., Corros. Sci. 42, 2193 (2000).Google Scholar
15.Yamamoto, A., Honma, R., and Sumita, M., J. Biomed. Mater. Res. 39, 331 (1998).Google Scholar
16.Zhang, T. and Inoue, A., Mater. Trans. 43, 267 (2002).Google Scholar
17.Asami, K., Hashimoto, K., and Shimodaira, S., Corros. Sci. 17, 713 (1977).Google Scholar
18.Asami, K. and Hashimoto, K., Corros. Sci. 24, 83 (1984).Google Scholar