High temperature mechanical properties of Cr2Nb-based intermetallics

Published online by Cambridge University Press:  03 March 2011

T. Takasugi
Affiliation:
Institute for Materials Research, Tohoku University, Katahira 2-1-1, Aoba-ku, Sendai, 980 Japan
S. Hanada
Affiliation:
Institute for Materials Research, Tohoku University, Katahira 2-1-1, Aoba-ku, Sendai, 980 Japan
K. Miyamoto
Affiliation:
Institute for Materials Research, Tohoku University, Katahira 2-1-1, Aoba-ku, Sendai, 980 Japan
Get access

Abstract

The results of high-temperature compressive deformation tests on a two-phase alloy consisting of Cr2Nb, a C15 Laves phase, and a soft Nb-based solid solution, are presented along with measurements of oxidation kinetics at 1273 K in air. These alloys are deformable only at temperatures above 1273 K. The measured 0.2% yield stress decreases steadily with increasing temperature and is only slightly sensitive to alloy composition. The steady state flow stress decreases steadily with increasing temperature and depends on alloy composition. A constitutive equation was fitted to the experimental data with a composition-independent stress exponent of about 2.7 and an apparent activation energy which ranges between 477 and 391 kJ/mol, also depending on alloy composition. Microstructural examination shows that cracking (cavitation) and interfacial sliding between the two constituent phases, in addition to bulk deformation of the constituent phases, are responsible for the deformation. The oxidation resistance of these alloys is very good.

Type
Articles
Copyright
Copyright © Materials Research Society 1993

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Thomas, D. J. and Perepezko, J. H., in Intermetallic Matrix Composites, edited by Anton, D. L., Martin, P. L., Miracle, D. B., and McMeeking, R. (Mater. Res. Soc. Symp. Proc. 194, Pittsburgh, PA, 1990), p. 105.Google Scholar
2Morris, M. A., J. Mater. Sci. 26, 1157 (1991).CrossRefGoogle Scholar
3Morris, M. A. and Morris, D. J., J. Mater. Sci. 26, 4687 (1991).CrossRefGoogle Scholar
4Thomas, D. J. and Perepezko, J. H., Mater. Sci. Eng. A 156, 97 (1992).CrossRefGoogle Scholar
5Anton, D. L. and Shah, D. M., in Intermetallic Matrix Composites, edited by Anton, D. L., Martin, P. L., Miracle, D. B., and McMeeking, R. (Mater. Res. Soc. Symp. Proc. 194, Pittsburgh, PA, 1990), p. 45.Google Scholar
6Vignoul, G. E., Sanchez, J. M., and Tien, J. K., in High Temperature Ordered Intermetallic Alloys IV, edited by Johnson, L. A., Pope, D. P., and Stiegler, J. O. (Mater. Res. Soc. Symp. Proc. 213, Pittsburgh, PA, 1991), p. 739.Google Scholar
7Takeyama, M. and Liu, C. T., Mater. Sci. Eng. A 132, 61 (1991).CrossRefGoogle Scholar
8Anton, D. L. and Shah, D. M., Mater. Sci. Eng. A 153, 410 (1992).CrossRefGoogle Scholar
9Einziger, R. E., Mundy, J. N., and Hoff, H. A., Phys. Rev. B 17, 440 (1978).CrossRefGoogle Scholar
10Perkins, R. A., Chiang, K. T., Meier, G. H., and Miller, R., Oxidation of High-Temperature Intermetaliics, edited by Grobstein, T. and Doychak, J. (The Minerals, Metals and Materials Society, Warrendale, PA, 1989), p. 157Google Scholar