Hydrogen storage properties of mechanically alloyedMg–8 mol% LaNi0.5 composite

Published online by Cambridge University Press:  01 October 2004

Qian Li ,
Qin Lin ,
Kuo-Chih Chou ,
Li-Jun Jiang  and
Feng Zhan
Qian Li*
Affiliation:
Department of Physical Chemistry, University of Science and Technology Beijing, Beijing 100088, People’s Republic of China; and Research Center of Energy Materials and Technology, General Research Institute for Nonferrous Metals, Beijing 100083, People’s Republic of China
Qin Lin
Affiliation:
Department of Physical Chemistry, University of Science and Technology Beijing, Beijing 100088, People’s Republic of China
Kuo-Chih Chou
Affiliation:
Department of Physical Chemistry, University of Science and Technology Beijing, Beijing 100088, People’s Republic of China
Li-Jun Jiang
Affiliation:
Research Center of Energy Materials and Technology, General Research Institute for Nonferrous Metals, Beijing 100083, People’s Republic of China
Feng Zhan
Affiliation:
Research Center of Energy Materials and Technology, General Research Institute for Nonferrous Metals, Beijing 100083, People’s Republic of China
*
a)Address all correspondence to this author.e-mail: lq75@263.net
Get access

Abstract

A new nano-ternary Mg–8 mol% LaNi0.5 was prepared by melted and subsequent mechanical alloying technique for hydrogen storage. It was found from our experiments that, this kind of alloy had superior hydriding/dehydriding characteristics in comparison with conventional materials for hydrogen storage. It possessed large hydrogen capacity at a lower temperature, which could absorb 4.55–7.01 mass% H under 3 MPa hydrogen pressure and desorb 4.40–6.90 mass% H under 0.0133 MPa in 600 s above 423 K without any activation requirement drawn from our pressure-composition isotherm and kinetic experiments. Through the x-ray diffraction and transmission electron microscopy experiments, we further found that these superior characteristics could be attributed to the multiphase structure and a catalytic effect of LaH3 and Mg2Ni that were formed in the material preparation of mechanical alloying process. Finally, based on these data the relationships between equilibrium pressure of hydrogen and temperature were obtained, they were lgp(0.1 MPa) = −3985/T + 7.188(553 K ⩽ T ⩽ 573K) for hydriding and lgp(0.1 MPa) = −3804/T + 6.770 (553 K ⩽ T ⩽ 573 K) for dehydriding.

Keywords

Intermetallic alloysAbsorptionMechanical alloying
Type
Articles
Information
Journal of Materials Research , Volume 19 , Issue 10 , October 2004 , pp. 2871 - 2876
Copyright
Copyright © Materials Research Society 2004

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Stioui, M., Ggayevsky, A., Resnik, A., Shaltiel, D. and Kaplan, N.: Macroscopic and microscopic kinetics of hydrogen in magnesium-rich compounds. J. Less-Common Met. 123, 9 (1986).CrossRefGoogle Scholar
2Liang, G., Huot, J., Boily, S., Van Neste, A. and Schulz, R.: Hydrogen storage properties of nanocrystalline Mg1.9Ti0.1Ni made by mechanical alloying. J. Alloys Compd. 282, 286 (1999).CrossRefGoogle Scholar
3Tsushi, Y., Enoki, H. and Akiba, E.: Energy distribution of hydrogen sites for MgNi0.86Ml (Ml = Cr, Fe, Co, Mn) alloys desorbing hydrogen at low temperature. J. Alloys Compd. 285, 298 (1999).CrossRefGoogle Scholar
4Qian, Li, Qin, Lin, Lijun, Jiang, Kuo-chih, Chou, Feng, ZhanZhengQiang, and Xiuying, Wei: Properties of hydrogen storage alloy Mg2-xAgx Ni (x = 0.05, 0.1, 0.5) by hydriding combustion synthesis. J. Alloys Compd. 359, 128 (2003).CrossRefGoogle Scholar
5Liu, F.J. and Suda, S.: Hydriding behavior of F-treated Mg2Ni at moderate conditions. J. Alloys Compd. 232, 212 (1996).CrossRefGoogle Scholar
6Hampton, M.D., Lomness, J.K. and Giannuzzi, L.A.: Surface study of liquid water treated and water and water vapor treated Mg2.35Ni alloys. Int. J. Hydrogen Energy 27, 79 (2002).CrossRefGoogle Scholar
7Ji, S.J., Sun, J.C., Yu, Z.W., Hei, Z.K. and Yan, L.: On the preparation of amorphous Mg-Ni alloys by mechanical alloying. Int. J. Hydrogen Energy 24, 59 (1999).CrossRefGoogle Scholar
8Cennari, F.C., Castro, F.J. and Urretavizcaya, G.: Hydrogen desorption behavior from magnesium hydrides synthesized by reactive mechanical alloying. J. Alloys Compd. 321, 46 (2001).Google Scholar
9Yamaura, S.I., Isogai, K., Kimura, H. and Inoue, A.: Electrochemical and thermal properties of hydrogen-absorbed Mg67Ni28Pd5 amorphous alloy. J. Mater. Res. 17, 60 (2002).CrossRefGoogle Scholar
10Zaluska, A., Zaluski, L. and Ström-Olsen, J.O.: Nanocrystalline magnesium for hydrogen storage. J. Alloys Compd. 288, 217 (1999).CrossRefGoogle Scholar
11Zaluski, L., Zaluska, A. and Ström-Olsen, J.O.: Nanocrystalline metal hydrides. J. Alloys Compd. 253–254, 70 (1997).CrossRefGoogle Scholar
12Terzieva, M., Khrussanova, M. and Peshev, P.: Hydriding and dehydriding characteristics of Mg-LaNi5 composite materials prepared by mechanical alloying. J. Alloys Compd. 267, 235 (1998).CrossRefGoogle Scholar
13Liang, G., Huot, J., Boily, S., Van Neste, A. and Schulz, R.: Hydrogen storage in mechanically milled Mg-LaNi5 and MgH2-LaNi5 composites. J. Alloys Compd. 297, 261 (2000).CrossRefGoogle Scholar
14Barkhordarian, G., Klassen, T. and Bormann, R.: Effect of Nb2O5 content on hydrogen reaction kinetics of Mg. J. Alloys Compd. 364, 242 (2004).CrossRefGoogle Scholar
15Bouaricha, S., Dodelet, J-P., Guay, D., Huot, J. and Schulz, R.: Study of the activation process of Mg-based hydrogen-storage materials modified by graphite and other carbonaceous compounds. J. Mater. Res. 16, 2893 (2001).CrossRefGoogle Scholar
16Semboshi, S. and Masahashi, N.Degrdation of hydrogen absorbing capacity cyclically hydrogenation TiMn2. Acta Mater. 49, 927 (2001)Google Scholar
17Slattery, D.K.: The hydriding-dehydriding characteristics of La2Mg17. Int. J. Hydrogen Energy 20, 971 (1995).CrossRefGoogle Scholar
18Yin, J. and Tanaka, K.Hydriding-dehydriding properties of Mg-rich Mg-Ni-Nd alloys with refined microstructures. Mater. Trans. 43, 1732 (2002).CrossRefGoogle Scholar