Interior crack initiation and growth behaviors and life prediction of a carburized gear steel under high cycle fatigue and very high cycle fatigue

Published online by Cambridge University Press:  27 July 2015

Wei Li ,
Zhenduo Sun ,
Hailong Deng ,
Zhenyu Zhang  and
Tatsuo Sakai
Wei Li*
Affiliation:
School of Mechanical Engineering, Beijing Institute of Technology, Beijing 100081, China
Zhenduo Sun
Affiliation:
School of Mechanical Engineering, Beijing Institute of Technology, Beijing 100081, China
Hailong Deng
Affiliation:
School of Mechanical Engineering, Beijing Institute of Technology, Beijing 100081, China
Zhenyu Zhang
Affiliation:
School of Mechanical Engineering, Beijing Institute of Technology, Beijing 100081, China
Tatsuo Sakai
Affiliation:
College of Mechanical Engineering, Ritsumeikan University, Kusatsu 5258577, Japan
*
a)Address all correspondence to this author. e-mail: lliw@bit.edu.cn
Get access

Abstract

The axial loading test was performed to investigate the effect of carburizing on crack initiation and growth behaviors of a gear steel under high cycle fatigue (HCF) and very high cycle fatigue (VHCF). As a result, the carburized gear steel exhibits the duplex S–N characteristics associated with different interior failure mechanisms. The failure process in the HCF regime can be described as inclusion → fisheye → final crack growth zone (FCGZ) → momentary fracture zone (MFZ), whereas that in the VHCF regime is described as inclusion → fine granular area (FGA) → fisheye → FCGZ → MFZ. Based on the definition of crack sizes at different transition stages and the evaluation of stress intensity factor, the models for predicting crack initiation and growth lives in the HCF regime and in the VHCF regime were established. The predicted crack initiation life tends to increase with the decrease of stress amplitude. In the VHCF regime, the crack initiation life associated with the FGA size is almost equivalent to the total fatigue life, whereas the crack growth life only occupies a tiny fraction. In view of the good agreement between the predicted and experimental results, the theoretical modeling method based on crack initiation and growth can be well used to predict the fatigue life of carburized steel with the interior inclusion-induced failure in the HCF regime and in the VHCF regime.

Type
Articles
Information
Journal of Materials Research , Volume 30 , Issue 14 , 28 July 2015 , pp. 2247 - 2257
Copyright
Copyright © Materials Research Society 2015 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Chen, B., Huang, B.X., Liu, H., Li, X.L., Ni, M.T., and Lu, C.: Surface nanocrystallization induced by shot peening and its effect on corrosion resistance of 6061 aluminum alloy. J. Mater. Res. 29, 3002–3010 (2014).Google Scholar
Peng, Y.C., Zhang, M.C., Dong, J.X., and Du, C.Y.: Investigations on carburizing mechanisms of Cr35Ni45Nb subjected to different service conditions in a high-temperature vacuum environment. J. Mater. Res. 30(6), 841–851 (2015). doi: 10.1557/jmr.2015.46.Google Scholar
Bathias, C.: There is no infinite fatigue life in metallic materials. Fatigue Fract. Eng. Mater. Struct. 22, 559–565 (1999).CrossRefGoogle Scholar
Shiozawa, K., Murai, M., Shimatani, Y., and Yoshimoto, T.: Transition of fatigue failure mode of Ni-Cr-Mo low-alloy steel in very high cycle regime. Int. J. Fatigue 32, 541–550 (2010).Google Scholar
Li, W., Sun, Z.D., Zhang, Z.Y., Deng, H.L., and Sakai, T.: Influence of case-carburizing and micro-defect on competing failure behaviors of Ni-Cr-W steel under gigacycle fatigue. Int. J. Fatigue 72, 66–74 (2015).Google Scholar
Nishijima, S. and Kanazawa, K.: Step S-N curve and fisheye failure in gigacycle fatigue. Fatigue Fract. Eng. Mater. Struct. 22, 601–607 (1999).Google Scholar
Sakai, T., Sato, Y., and Oguma, N.: Characteristic S-N properties of high-carbon-chromium-bearing steel under axial loading in long-life fatigue. Fatigue Fract. Eng. Mater. Struct. 25, 765–732 (2002).Google Scholar
Murakami, Y., Yokoyama, N., and Nagata, J.: Mechanism of fatigue failure in ultralong life regime. Fatigue Fract. Eng. Mater. Struct. 25, 735–746 (2002).Google Scholar
Shiozawa, K., Morii, Y., Nishino, S., and Lu, L.: Subsurface crack initiation and propagation mechanism in high strength steel in a very high cycle fatigue regime. Int. J. Fatigue 28, 1521–1532 (2006).Google Scholar
Sakai, T., Takeda, M., Shiozawa, K., Ochi, Y., Nakajima, M., and Nakamura, T.: Experimental reconfirmation of characteristic S-N property for high carbon chromium bearing steel in wide life region in rotating bending. J. Soc. Mater. Sci., Jpn. 49, 779–785 (2000).Google Scholar
Shiozawa, K., Lu, L., and Ishihara, S.: S-N curve characteristics and subsurface crack initiation behavior in ultra-long life fatigue of a high carbon-chromium bearing steel. Fatigue Fract. Eng. Mater. Struct. 24, 781–790 (2001).Google Scholar
Murakami, Y., Nomoto, T., and Ueda, T.: Factors influencing the mechanism of surperlong fatigue failure in steels. Fatigue Fract. Eng. Mater. Struct. 22, 581–590 (1999).Google Scholar
Sohar, C.R., Betzwar-Kotas, A., Gierl, C., Weiss, B., and Danninger, H.: Fractographic evaluation of gigacycle fatigue crack nucleation and propagation of a high Cr alloyed cold work tool steel. Int. J. Fatigue 30, 2192–2199 (2008).Google Scholar
Yu, Y., Gu, J.L., Bai, B.Z., Liu, Y.B., and Li, S.X.: Very high cycle fatigue mechanism of carbide-free bainite/martensite steel micro-alloyed with Nb. Mater. Sci. Eng., A 527, 212–217 (2009).Google Scholar
Nie, Y.H., Fu, W.T., Hui, W.J., Dong, H., and Weng, Y.Q.: Very high cycle fatigue behavior of 2000MPa ultra-high-strength spring steel with bainite-martensite duplex microstructure. Fatigue Fract. Eng. Mater. Struct. 32, 189–196 (2009).Google Scholar
Nakamura, T., Oguma, H., and Shinohara, Y.: The effect of vacuum-like environment inside sub-surface fatigue crack on the formation of ODA fracture surface in high strength steel. Procedia Eng. 2, 2121–2129 (2010).Google Scholar
Grad, P., Reuscher, B., and Brodvanski, A.: Mechanism of fatigue crack initiation and propagation in the very high cycle fatigue regime of high-strength steels. Scr. Mater. 67, 838–841 (2012).Google Scholar
Murakami, Y. and Endo, M.: Effects of defects, inclusions and inhomogeneities on fatigue strength. Int. J. Fatigue 16, 163–182 (1994).Google Scholar
Tanaka, K. and Akiniwa, Y.: Fatigue crack propagation behavior derived from S-N data in very high cycle regime. Fatigue Fract. Eng. Mater. Struct. 25, 775–784 (2002).Google Scholar
Liu, Y.B., Li, Y.D., Li, S.X., and Yang, Z.G.: Prediction of the S-N curves of high-strength steels in the very high cycle fatigue regime. Int. J. Fatigue 32, 1351–1357 (2010).Google Scholar
Mayer, H., Haydn, W., Schuller, R., Issler, S., Furtner, B., and Bacher-Hochst, B.: Very high cycle fatigue properties of bainitic high carbon-chromium steel. Int. J. Fatigue 31, 242–249 (2009).Google Scholar
Sun, C., Xie, J., Zhao, A., Lei, Z., and Hong, Y.: A cumulative damage model for fatigue life estimation of high-strength steels in high-cycle and very-high-cycle fatigue regimes. Fatigue Fract. Eng. Mater. Struct. 35, 638–647 (2012).Google Scholar
Chapetti, M.D.: Prediction of threshold for very high cycle fatigue (N>107 cycles). Procedia Eng. 2, 257–264 (2010).Google Scholar
Zhao, A., Xie, J., Sun, C., Lei, Z., and Hong, Y.: Prediction of threshold value for FGA formation. Mater. Sci. Eng., A 528, 6872–6877 (2011).Google Scholar
Pilkey, W.D. and Pilkey, D.F.: Peterson’s Stress Concentration Factors, 3rd ed. (John Wiley and Sons Inc., Hoboken, New Jersey, 2008).Google Scholar
Marines-Garcia, I., Paris, P.C., Tada, H., Bathias, C., and Lados, D.: Fatigue assessment using an integrated threshold curve method—Applications. Eng. Fract. Mech. 75, 1657–1665 (2008).Google Scholar
Tanaka, K. and Mura, T.: A theory of fatigue crack initiation at inclusions. Metal. Trans. A 13A, 117–123 (1982).Google Scholar
Venkataraman, G., Chung, Y.W., and Mura, T.: Application of minimum energy formalism in a multiple slip band model for fatigue—I. Calculation of slip band spacings. Acta Metall. Mater. 39, 2621–2629 (1991).Google Scholar
Chan, K.S.: A microstructure-based fatigue-crack initiation model. Metall. Mater. Trans. A 34A, 43–57 (2003).Google Scholar
Cheng, A.S. and Laird, C.: Fatigue life behavior of copper single crystals. Part II: Model for crack nucleation in persistent slip bands. Fatigue Fract. Eng. Mater. Struct. 4, 343–353 (1981).Google Scholar
García, I.G., Mantič, V., and Graciani, E.: Crack onset at the spherical-inclusion matrix interface. Application of a coupled stress and energy criterion. Procedia Mater. Sci. 3, 1336–1341 (2014).Google Scholar
Paris, P.C., Marines-Garcia, I., Hertzberg, R.W., and Donald, J.D.: The relationship of effective stress intensity, elastic modulus and Burgers-vector on fatigue crack growth as associated with “fisheye” gigacycle fatigue phenomena. In Proc.VHCF-3, Kyoto, Japan. (Society of Materials Science, Japan (JSMS), Kyoto, Japan, 2004).Google Scholar