Microstructures of thermomechanically treated eutectoid Zn–Al alloy (II)

Published online by Cambridge University Press:  03 March 2011

Yao Hua Zhu
Affiliation:
Instituto de Investigaciones en Materiales, Universidad Nacional Autonoma de Mexico, Apdo. Postal 70-360, 04510 Coyoacan, D. F. Mexico
Frank E. Goodwin
Affiliation:
International Lead and Zinc Research Organization, Inc., P.O. Box 12036, Research Triangle Park, North Carolina 27709
Get access

Abstract

The evolution of microstructure in a cast, extruded, and aged eutectoid Zn-Al-Cu alloy is described based on x-ray diffraction an micrographic observations. Whereas the three phases α′, β′, and η′ were found in the as-cast state, the three phases α, T′, and η′E were observed in this alloy after extrusion at 250 °C. The Al-rich fcc α phase appeared as isolated particles with clear boundaries. The Zn-rich η′E phase decomposed upon aging into α, T′, and η phases. It was found possible to control the phase makeup of the alloy by controlling extrusion temperature. At extrusion temperatures greater than 268 °C, α, E, and η′E were detected, whereas temperatures below this, the phases α, T′, and η′E were found. After prolonged aging, the phase makeup of the alloy was found to be the same regardless of prior treatment routes. Early shrinkage of the extruded alloy occurred after aging at 91 and 150 °C and was related to precipitation of aluminum from the η′E phase during its decomposition to α, T′, and η products.

Type
Articles
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Anderson, E. A. and Werley, G. L., Zamak Alloys for Zinc Alloy Die Casting (The New Jersey Zinc Company, New York, 1946).Google Scholar
2Gervais, E., Levert, H., and Bess, M., “Development of a Family of Zinc-Based Foundry Alloys,” American Foundrymen's Society, 84th Casting Congress & Exhibition, St. Louis, MO, April 21–25, 1980.Google Scholar
3Pelzel, E., Metallwirtschaft 17(8), 788 (1963).Google Scholar
4Landgon, T. G., in Proc. Third Int. Conf. on Zn–AI Alloys, Mexico City, March 29–30, 1994 (International Lead Zinc Research Organization, Inc., Research Triangle Park, NC, 1994), pp. 177182.Google Scholar
5Zhu, Y. H. and Goodwin, F. E., J. Mater. Sci. Technol. 10, 121126 (1994).Google Scholar
6Zhu, Y. H., Ph.D. Thesis, University of Aston, Birmingham, U.K. (1983).Google Scholar
7Zhu, Y. H. and Murphy, S., J. Mater. Sci. Technol. 3, 261 (1987).Google Scholar
8Zhu, Y. H., J. Mater. Sci. Technol. 6, 125 (1990).Google Scholar
9Zhu, Y. H. and Murphy, S., J. Mater. Sci. Technol. 2, 105 (1986).Google Scholar
10Zhu, Y. H., Torres Vallasefior, G., and Pifia, C., J. Mater. Sci. 29, 1549 (1994).Google Scholar
11Murphy, S., Metal Sci. 9, 163 (1975).Google Scholar
12Murphy, S., Z. Metallk. 71, 96 (1980).Google Scholar
13Zhu, Y. H., J. Mater. Sci. Technol. 5, 113 (1989).Google Scholar
14Lohberg, K., Z. Metallk. 32, 86 (1941).Google Scholar