Melting, solidification and solid-state transformation of the intermetallic Ni3Sn compound were investigated in situ using synchrotron high-energy X-ray diffraction. It was observed that the compound undergoes a hexagonal to cubic transition before melting. In solidification, a disordered cubic phase crystallizes from the liquid at a large undercooling but it is reordered prior to bulk solidification. In melting and solidification, forced or natural flows are active bringing about significant changes of crystal orientations. These in situ observations provided insights into phase transformations of Ni3Sn at elevated temperatures and their roles in formation of metastable microstructure consisting of coarse grains and subgrains.