Hardening and Microstructure of Model Reactor Pressure Vessel Steel Alloys Using Proton Irradiation

Published online by Cambridge University Press:  21 March 2011

Q. Yu ,
G. S. Was ,
L. M. Wang ,
R. Odette  and
D. E. Alexander
Q. Yu
Affiliation:
Department of Nuclear Engineering and Radiological Sciences, University of Michigan
G. S. Was
Affiliation:
Department of Nuclear Engineering and Radiological Sciences, University of Michigan
L. M. Wang
Affiliation:
Department of Nuclear Engineering and Radiological Sciences, University of Michigan
R. Odette
Affiliation:
Department of Mechanical and Environmental Engineering, University of California at Santa Barbara
D. E. Alexander
Affiliation:
Materail Science Division, Argonne National Laboratory
Get access

Abstract

As part of a broad effort to understand the mechanisms of irradiation embrittlement in reactor pressure vessels steels, irradiation hardening and microstructural evolution in simple model Fe-0.9Cu-1.0Mn, Fe-0.9Cu and Fe alloys irradiated with 3.2 MeV protons at 300°C are compared to the corresponding changes in hardening produced by neutron irradiation over a similar dose range of 0.0004 to 0.015 dpa. In the case of the proton irradiated samples, Vickers hardness was measured at a 25 g load and the microstructures were characterized using small angle x-ray scattering (SAXS). In spite of the much higher dpa rate for protons (3 × 10−7 dpa/s compared to neutron rates of about 10−9 to 10−10 dpa/s) as well as very different primary recoil spectra, the observed hardening-dose response is very similar in both cases. The large increase in hardness in the alloys with 0.9% copper, and the SAXS data are consistent with precipitation of coherent copper-rich features accelerated by irradiation enhanced diffusion, as well as a much smaller contribution presumably from defect clusters that do not require the presence of copper.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 650: Symposium R – Microstructural Processes in Irradiated Materials-2000 , 2000 , R6.2
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Alekseenko, N. N., Amaev, A., Gorynin, I., Nikolaev, V. A., Radiation damage of nuclear power plant pressure vessel steels, ANS, 1997, p. 20.Google Scholar
2. Was, G. S., Allen, T. R., Busby, J. T., Gan, J., Damcott, D., Carter, D., Atzmon, M. and Kenik, E., J. Nucl. Mater, 270 (1999) 96.Google Scholar
3. Damcott, D., Cookson, J., Rotberg, V. and Was, G. S., Nucl. Instr. Meth. B 99, (1995) 780.Google Scholar
4. Ziegler, J. F., Biersack, J. P. and Littmark, U., The Stopping and Range of Ions in Solids, Pergamon Press, New York, 1996.Google Scholar
5. Cookson, J. and Was, G. S., Corrosion, 54 (4) (1998) 299.Google Scholar
6. Alexander, D. E. and Rehn, L. E., Odette, G. R., Lucas, G. E., Klingensmith, D. and Gragg, D., 9th International Conference on Environmental Degradation of Materials in Nuclear Power Systems Water Reactors, Bruemmer, S. M., Ford, F. P. and Was, G. S., eds., TMS, Pittsburgh, PA, 1999, 827.Google Scholar
7. Mancuso, J. F., Spritznagel, J. A., Shogan, R. P., and Holland, J. R., Effects of Radiation on Materials: 10th Conference, ASTM STP 725, 1981, 38.Google Scholar
8. Lucas, G. E., Odette, G. R., Maiti, R., Sheckherd, J. W., ASTM-STP-956, 379. Google Scholar
9. Odette, G. R., Lucas, G. E., and Klingensmith, D., On the Effect of Neutron Flux and Composition on Hardening of Reactor Pressure Vessel Steels and Model Alloys (this proceedings).Google Scholar
10. Odette, G. R., Mader, E., Lucas, G. E., Phythian, W. J., English, C. A., ASTM-STP-1175, American Society for Testing and Materials, 373 (1993).Google Scholar
11. Odette, G. R., Lucas, G. E., Klingensmith, D., ASTM-STP-1325, 1999, 1089.Google Scholar
12. Eason, E. D., Wright, J. E. and Odette, G. R., NUREG/CR-6551, U. S. Nuclear Regulatory Commission, Washington D.C., 1998.Google Scholar
13. Williams, T., Ellis, D., ASTM STP 1405, in press.Google Scholar
14. Buswell, J., Little, E. and Sinclair, R., Nuclear Energy, 37, (1998) 387.Google Scholar
15. Wirth, B. D., On the Character of Nano-scale Features in Reactor Pressure Vessel Steels Under Neutron Irradiation, PhD Dissertation, University of California, Santa Barbara (1998).Google Scholar
16. Taylor, G. I., J. Inst. Met. 62, (1938) 307.Google Scholar