High Temperature Strength of Co-based γ/γ' Superalloys

Published online by Cambridge University Press:  26 February 2011

Akane Suzuki ,
Garret C DeNolf  and
Tresa M Pollock
Akane Suzuki
Affiliation:
akanes@umich.edu, University of Michigan, Materials Science and Engineering, 3062 H.H.Dow, 2300 Hayward St., Ann Arbor, MI, 48109, United States, 734-763-1406, 734-615-5168
Garret C DeNolf
Affiliation:
denolfgc@umich.edu, University of Michigan, Materials Science and Engineering, 2300 Hayward St., Ann Arbor, MI, 48109, United States
Tresa M Pollock
Affiliation:
tresap@umich.edu, University of Michigan, Materials Science and Engineering, 2300 Hayward St., Ann Arbor, MI, 48109, United States
Get access

Abstract

The high temperature strength of new Co-Al-W based alloys consisting of a ?-Co (fcc) matrix phase and a high volume fraction of ?'-Co3(Al, W) ternary L12 intermetallic compound has been examined in order to understand the strengthening mechanisms and to explore the possibility for high temperature applications. The flow stress exhibits a strong, positive dependence on temperature above 873 K. Additions of Ta improve the high temperature strength, and the strength of a Ta containing alloy is comparable to Ni-base superalloys at 1173 K. Transmission microscopy on the deformed Ta containing alloy revealed that the active slip modes within the ?' precipitates are <110>{111} and <112>{111} below and above the peak temperature, respectively. At the peak flow temperature, multiple slip modes including <110>{111}, <110>{001} and <112>{111} were observed.

Keywords

Costrengthdislocations
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 980: Symposium II – Advanced Intermetallic-Based Alloys , 2006 , 0980-II08-09
Copyright
Copyright © Materials Research Society 2007

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Beltran, A.M., in Superalloys II, edited by C.T., Sims, N.S., Stoloff and W.C., Hagel (Wiley,New York, 1987), pp. 135–163.Google Scholar
2. Sato, J., Omori, T., Oikawa, K., Ohnuma, I., Kainuma, R. and Ishida, K., Science 312, 90 (2006).10.1126/science.1121738Google Scholar
3. Feng, Q., Nandy, T.K., Tin, S. and Pollock, T.M., Acta Mater. 51, 269 (2003).10.1016/S1359-6454(02)00397-XGoogle Scholar
4. Gabb, T.P. and Dreshfield, R.L., in Superalloys II, edited by C.T., Sims, N.S., Stoloff and W.C., Hagel (Wiley, New York, 1987), pp. 575–597.Google Scholar
5. Pope, D.P. and Ezz, S.S., Intl. Metals Rev. 29, 136 (1984).Google Scholar
6. Nabarro, F.R.N. and Duesbery, M.S. (Eds.), Dislocations in Solids, vol.10, (Elsevier, Amsterdam, 1997).Google Scholar
7. Pollock, T.M. and Field, R.D., in Dislocations in Solids, vol.11, edited by F.R.N., Nabarro and M.S., Duesbery (Elsevier, Amsterdam, 2002), pp. 546–618.Google Scholar
8. Milligan, W.W. and Antolovich, S.D., Metall. Trans. 18A, 85 (1987).10.1007/BF02646225Google Scholar
9. Haasen, P., Physical Metallurgy, 2nd ed. (Cambridge University Press, Cambridge, 1986) p. 120.Google Scholar