Published online by Cambridge University Press: 15 February 2011
Iridium silicides formation by rapid thermal annealing (RTA) under vacuum at several temperatures in the range of 350 to 650°C has been investigated. The substrates and the silicide films were analyzed by Rutherford backscattering spectrometry (RBS) and Auger electron spectroscopy (AES). At 350°C, no distinguishable phase was detected for 240 seconds of annealing time. At 400°C, for processing time up to 45 seconds only Ir1Si1 was formed, for longer processing time Ir1Si1.75 was formed too. At higher temperatures even for very short processing time, Ir1Si1.75 was formed. Ir, Ir1Si1 and Ir1Si1.75 were present simultaneously if the iridium film was thick enough and the processing time was long enough too. For thin iridium layers, the Ir1Si1 formed was totally converted to Ir1Si1.75, if the annealing time was long enough. Formation rates were observed to be three to five orders of magnitude faster than the reported for furnace annealing.
To send this article to your Kindle, first ensure no-reply@cambridge.org is added to your Approved Personal Document E-mail List under your Personal Document Settings on the Manage Your Content and Devices page of your Amazon account. Then enter the ‘name’ part of your Kindle email address below. Find out more about sending to your Kindle. Find out more about saving to your Kindle.
Note you can select to save to either the @free.kindle.com or @kindle.com variations. ‘@free.kindle.com’ emails are free but can only be saved to your device when it is connected to wi-fi. ‘@kindle.com’ emails can be delivered even when you are not connected to wi-fi, but note that service fees apply.
Find out more about the Kindle Personal Document Service.
To save this article to your Dropbox account, please select one or more formats and confirm that you agree to abide by our usage policies. If this is the first time you used this feature, you will be asked to authorise Cambridge Core to connect with your Dropbox account. Find out more about saving content to Dropbox.
To save this article to your Google Drive account, please select one or more formats and confirm that you agree to abide by our usage policies. If this is the first time you used this feature, you will be asked to authorise Cambridge Core to connect with your Google Drive account. Find out more about saving content to Google Drive.