The open-circuit voltage (Voc) of mixed-phase hydrogenated silicon solar cells has been found to increase after light soaking. In this study, we use micro-Raman to investigate the heterogeneous structure of solar cells in the amorphous-to-nanocrystalline transition region. For a cell with Voc = 0.981 V, Raman spectra show a typical broad Gaussian lineshape around 480 cm-1, a signature of typical amorphous material. A cell with Voc = 0.674 V displays a sharp Lorentzian peak around 516 cm-1, indicative of nanocrystallinity. A cell with Voc = 0.767 V was systematically scanned for 20 different positions in 500 μm increments. Most spectra show a typical Gaussian lineshape around 480 cm-1, several spectra reveal a hint of a nanocrystalline shoulder around 512 cm-1, and one spectrum exhibits a distinct nanocrystalline peak. We conclude that the nanocrystallite distribution in the mixed-phase material is very non-uniform even within a mm dot. This result provides direct evidence supporting a recently proposed two-diode equivalent-circuit model to explain the light-induced effect.
To send this article to your Kindle, first ensure no-reply@cambridge.org is added to your Approved Personal Document E-mail List under your Personal Document Settings on the Manage Your Content and Devices page of your Amazon account. Then enter the ‘name’ part of your Kindle email address below. Find out more about sending to your Kindle. Find out more about saving to your Kindle.
Note you can select to save to either the @free.kindle.com or @kindle.com variations. ‘@free.kindle.com’ emails are free but can only be saved to your device when it is connected to wi-fi. ‘@kindle.com’ emails can be delivered even when you are not connected to wi-fi, but note that service fees apply.
Find out more about the Kindle Personal Document Service.
To save this article to your Dropbox account, please select one or more formats and confirm that you agree to abide by our usage policies. If this is the first time you used this feature, you will be asked to authorise Cambridge Core to connect with your Dropbox account. Find out more about saving content to Dropbox.
To save this article to your Google Drive account, please select one or more formats and confirm that you agree to abide by our usage policies. If this is the first time you used this feature, you will be asked to authorise Cambridge Core to connect with your Google Drive account. Find out more about saving content to Google Drive.