Multi Scale Characterization of Stress Corrosion Cracking of Alloy X750

Published online by Cambridge University Press:  15 January 2013

Kevin Fisher ,
Sébastien Teysseyre  and
Emmanuelle A Marquis
Kevin Fisher
Affiliation:
Department of Materials Science and Engineering, University of Michigan, Ann Arbor MI
Sébastien Teysseyre
Affiliation:
ATR National Scientific User Facility, Idaho National Laboratory, Idaho Falls, ID
Emmanuelle A Marquis
Affiliation:
Department of Materials Science and Engineering, University of Michigan, Ann Arbor MI
Get access

Abstract

Grain boundary chemistry in an X750 Ni alloy was analyzed by atom probe tomography in an effort to clarify the possible roles of elemental segregation and carbide presence on the stress corrosion cracking behavior of Ni alloys. Two types of cracks are observed: straight cracks along twin boundaries and wavy cracks at general boundaries. It was found that carbides (M23C6 and TiC) are present at both twin and general boundaries, with comparable B and P segregation for all types of grain boundaries. Twin boundaries intercept γ’ precipitates while the general boundaries wave around the γ’ and carbide precipitates. Near a crack tip, oxidation takes place on the periphery of carbide precipitate.

Keywords

corrosiongrain boundariesnanoscale
Type
Articles
Information
MRS Online Proceedings Library (OPL) , Volume 1519: Symposium MM – Materials under Extreme Environments , 2013 , mrsf12-1519-mm10-02
Copyright
Copyright © Materials Research Society 2013

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Garner, G.L. and Smith, J.L. Identification and characterization of commercial nuclear power plant components fabricated from age-hardenable alloys X-750, A-286, and 718, EPRI Report RP-2058-4, 1984.Google Scholar
Jenssen, A., Efsing, P., Sandberg, J. Influence of heat treatment, aging, and neutron irradiation on the fracture toughness and crack growth rate in BWR environments of alloy X-750, Proceedings of the 12th International Conference on Environmental Degradation of Materials in Nuclear Power Systems – Water Reactors, pp. 73–85, 2005.Google Scholar
James, L.A. Effect of fast neutron irradiation on fatigue crack growth behavior of three nickel-base alloys, Nuclear Technology, Vol. 53, pp. 64–68, 1981.10.13182/NT81-A17057CrossRefGoogle Scholar
Was, G.S. and Liang, K. Role of Carbides in Stress Corrosion Cracking Resistance of Alloy 600 and Controlled-Purity Ni-16% Cr-9% Fe in Primary Water at 360°C, Corrosion Vol54, 09, (1988)Google Scholar
Kozaczek, K.J. et al. . Micromechanical modelling of microstress fields around carbide precipitates in alloy 600, 1995 Modelling Simul. Mater. Sci. Eng. 3 829 10.1088/0965-0393/3/6/006CrossRefGoogle Scholar
Grove, C.A. and Petzold, L.D. Mechanisms of Stress-corrosion cracking of alloy X-750 in high-purity water. Journal of Materials for Energy Systems, 1985. 7(2): p. 147–162.10.1007/BF02833560CrossRefGoogle Scholar
Sinha, A.K. and Moore, J.J. Precipitation of M23C6 carbides in an aged Inconel X-750. Metallography, 1986. 19(1): p. 87–98.10.1016/0026-0800(86)90009-1CrossRefGoogle Scholar
Sennour, M., et al. ., Advanced TEM characterization of stress corrosion cracking of Alloy 600 in pressurized water reactor primary water environment. Journal of Nuclear Materials, 2009. 393(2): p. 254–266.10.1016/j.jnucmat.2009.06.014CrossRefGoogle Scholar