Understanding subcritical fracture of low-k dielectric materials and barrier thin films in buffered solutions of different pH value is of both technical and scientific importance. Subcritical delamination of dielectric and metal barrier films from low-k organosilicate glass (OSG) films in pH buffer solutions was studied in this work. Crack path and subcritical fracture behavior of OSG depends on the choice of barrier layers. For the OSG/TaN system, fracture takes place in the OSG layer near the interface, while in OSG/SiNx system, delamination occurs at the interface. Delamination behavior of both systems is well described by a hyperbolic sine model that had been developed previously based on a chemical reaction controlled fracture process at the crack tip. The threshold toughness of both systems decreases linearly with increasing pH value. The slopes of the reaction-controlled regime of the crack velocity curves for both systems are independent of pH as predicted by the model. Near transport-controlled regime behavior was observed in OSG/TaN system.
To send this article to your Kindle, first ensure no-reply@cambridge.org is added to your Approved Personal Document E-mail List under your Personal Document Settings on the Manage Your Content and Devices page of your Amazon account. Then enter the ‘name’ part of your Kindle email address below. Find out more about sending to your Kindle. Find out more about saving to your Kindle.
Note you can select to save to either the @free.kindle.com or @kindle.com variations. ‘@free.kindle.com’ emails are free but can only be saved to your device when it is connected to wi-fi. ‘@kindle.com’ emails can be delivered even when you are not connected to wi-fi, but note that service fees apply.
Find out more about the Kindle Personal Document Service.
To save this article to your Dropbox account, please select one or more formats and confirm that you agree to abide by our usage policies. If this is the first time you used this feature, you will be asked to authorise Cambridge Core to connect with your Dropbox account. Find out more about saving content to Dropbox.
To save this article to your Google Drive account, please select one or more formats and confirm that you agree to abide by our usage policies. If this is the first time you used this feature, you will be asked to authorise Cambridge Core to connect with your Google Drive account. Find out more about saving content to Google Drive.