Annealing Temperature and Substrate Effects on the Raman Spectra of Transferred CVD Graphene

Published online by Cambridge University Press:  29 February 2012

Barbara M. Nichols
Affiliation:
U.S. Army Research Laboratory, 2800 Powder Mill Road, Adelphi, MD 20783, U.S.A.
Yasmine R. Doleyres
Affiliation:
U.S. Army Research Laboratory, 2800 Powder Mill Road, Adelphi, MD 20783, U.S.A.
Gregory P. Meissner
Affiliation:
U.S. Army Research Laboratory, 2800 Powder Mill Road, Adelphi, MD 20783, U.S.A.
Get access

Abstract

This work explores the influence of the post-transfer anneal temperature and the substrate on transferred graphene and its Raman properties. Graphene grown by low pressure chemical vapor deposition on copper foils was transferred to SiO2/Si, fused silica, and silicon substrates via a process that involves coating the graphene with PMMA as a protective handling layer during the wet chemical etching of the copper and then placing the PMMA/graphene onto the substrate. The PMMA layer was then removed by heating in a hydrogen/argon atmosphere at temperatures ranging from 350 to 550 °C or by exposing the PMMA to heated acetone vapor/liquid. Raman spectroscopy measurements, taken before and after PMMA removal, reveal differences in the prominent Raman features, the G and G’ peaks, upon annealing. These changes include (1) a shift in the average G and G’ peak positions when comparing Raman spectra before and after PMMA removal and (2) a decrease in the G’:G peak intensity ratio (IG’/IG), which is typically used as a measure of the number of graphene layers. For both the as-transferred graphene and graphene removed by the heated acetone, the IG’/IG peak ratio was approximately 2, indicating single layer graphene. However, when the graphene was annealed at temperatures above 350 °C, the IG’/IG intensity ratio varied from 0.5 to 1.5. These changes in the Raman spectra are similar to those observed in exfoliated single layer graphene supported on SiO2/Si substrates and are indicative of graphene-substrate interaction effects that lead to hole doping of the graphene [1,2]. These trends were observed for graphene transferred to all three substrates, regardless of the substrate surface roughness and/or composition.

Type
Research Article
Copyright
Copyright © Materials Research Society 2012

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Cheng, Z., Zhou, Q., Wang, C., Li, Q., Wang, C., and Fang, Y., Nano Letters 11, 767 (2011).Google Scholar
2. Nourbakhsh, A., Cantoro, M., Klekachev, A., Clemente, F., Soree, B., van der Veen, M. H., Vosch, T., Stesmans, A., Sels, B., and De Gendt, S., J. Physical Chemistry C 114, 6894 (2010).Google Scholar
3. Bolotina, K.I., Sikesb, K.J., Jianga, Z., Klimac, M., Fudenberga, G., Honec, J., Kima, P., and Stormera, H.L., Solid State Communications 146, 351 (2008).Google Scholar
4. Murali, R., Yang, Y., Brenner, K., Beck, T., and Meindl, J. D., Applied Physics Letters 94, 243114 (2009).Google Scholar
5. Nair, R. R., Blake, P., Grigorenko, A. N., Novoselov, K. S., Booth, T. J., Stauber, T., Peres, N. M. R., and Geim, A. K., Science 320, 1308 (2008).Google Scholar
6. Ni, Z. H., Wang, H. M., Luo, Z. Q., Wang, Y. Y., Yu, T., Wu, Y. H., and Shen, Z. X., Journal of Raman Spectroscopy 41, 479 (2010).Google Scholar
7. Kashiwagi, T., Inaba, A., Brown, J. E., Hatada, K., Kitayama, T., and Masuda, E., Macromolecules 19, 2160 (1986).Google Scholar
8. Lee, S., Lee, K., and Zhong, Z., Nano Letters 10, 4702 (2010).Google Scholar
9. Cao, H., Yu, Q., Jauregui, L. A., Tian, J., Wu, W., Liu, Z., Jalilian, R., Benjamin, D. K., Jiang, Z., Bao, J., Pei, S. S., and Chen, Y. P., arXiv:0910.4329v1, (2009).Google Scholar
10. Gupta, A., Chen, G., Joshi, P., Tadigadapa, S., and Eklund, P.C., Nano Letters 6, 2667 (2006).Google Scholar
11. Dean, C. R., Young, A. F., Meric, I., Lee, C., Wang, L., Sorgenfrei, S., Watanabe, K., Taniguchi, T., Kim, P., Shepard, K. L., and Hone, J., Nature Nanotechnology 5, 722 (2010).Google Scholar