Atmospheric Corrosion of Copper 450 Metres Underground. Results From Three Years Exposure in the Äspö HRL

Published online by Cambridge University Press:  01 February 2011

Claes Taxén
Claes Taxén*
Affiliation:
Swedish Corrosion Institute, Kraeftriket. 23A, SE 105 05 Stockholm, SWEDEN
Get access

Abstract

Results from an atmospheric exposure of copper at the Äspö Hard Rock Laboratory (HRL) are reported. Corrosion test coupons were exposed under sheltered conditions at 450 meters depth. The exposure was performed in order to gain insight into the likely state of a copper canister surface at the time when water begins to fill a repository for nuclear waste. The conditions for the experiment were selected to be relevant for the conditions predicted for a repository during an initial dry phase. Visual observations show that copper exposed at ambient temperature remained bright and shiny whereas coupons exposed at elevated temperature had a dull greenish appearance.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 807: Symposium Scientific Basis for Nuclear Waste Management XXVII , 2003 , 423
Copyright
Copyright © Materials Research Society 2004

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Crumbelin, S. J., Newell, B. and Pascucci, V., “Monitoring environmental tests by coulometric reduction of metallic control samples” J. Testing and Evaluation Vol. 17 pp357–367 (1989)Google Scholar
2. Campbell, W. E and Thomas, U.B. “The electrolytic reduction method for the analysis of films on metal surfaces”, Trans. Amer. Electrochem. Soc. Vol 76, pp 303–328 (1939)Google Scholar
3. “Miljö och korrosionsdata 1998”, Swedish Corrosion Institute.Google Scholar