The Effect of Ge and Ti Additions on the Microstructures and Properties of Nb-18Si Based Alloys

Published online by Cambridge University Press:  19 January 2011

Zifu Li  and
Panos Tsakiropoulos
Zifu Li
Affiliation:
IMMPETUS, Department of Materials Science and Engineering, The University of Sheffield, Sir Robert Hadfield Building, Mappin Street, Sheffield S1 3JD, England, UK
Panos Tsakiropoulos
Affiliation:
IMMPETUS, Department of Materials Science and Engineering, The University of Sheffield, Sir Robert Hadfield Building, Mappin Street, Sheffield S1 3JD, England, UK
Get access

Abstract

The effects of Ge and Ti additions on the microstructure, hardness and oxidation behaviour of the alloys Nb–18Si–5Ge (ZF1) and Nb–24Ti–18Si–5Ge (ZF3) were studied. The as cast microstructure of the alloy ZF1 consisted of Nbss (cI2), and βNb5Si3 (tI32) with the latter being the primary phase and the two phases forming high volume fractions of Nbss + βNb5Si3 eutectic. The Ge addition stabilised the βNb5Si3 (tI32), and destabilised the Nb3Si (tP32) and the Nbss + Nb3Si eutectic. After heat treatment at 1200 °C for 100 h the βNb5Si3 (tI32) was partially transformed to the αNb5Si3 (tI32), and equilibrium was reached after heat treatment at 1500 °C for 100 h. The phases present in the as cast alloy ZF3 were the Nbss (cI2), and the Nb3Si (tP32), βNb5Si3 (tI32) and Ti5Si3 (hP16) silicides, with the latter forming a eutectic with the solid solution. The same phases were present after heat treatment at 1200 °C for 100 h but only the Nbss, and the Nb3Si and Nb5Si3 silicides were present after 100 h at 1500 °C where TiO2 was also formed. The Ge addition increased the microhardness of the Nb5Si3. The synergy of Ti with Ge resulted in a strong hardening effect and a remarkable retention of the hardness of the alloy ZF3. The additions of Ge and Ti to the Nb-18Si alloy improved the oxidation resistance at 800 °C, but pest oxidation behaviour was not eliminated.

Keywords

microstructurecastingphase transformation
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1295: Symposium N – Intermetallic-Based Alloys for Structural and Functional Applications , 2011 , mrsf10-1295-n07-07
Copyright
Copyright © Materials Research Society 2011

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Bewlay, B. P., Jackson, M. R. and Lipsitt, H. A., Metall. Mater. Trans. A 27, 3801 (1996).Google Scholar
2. Geng, J., Tsakiropoulos, P. and Shao, G., Mater. Sci. Eng. A 441, 26 (2006):.Google Scholar
3. Davidson, D. L. and Metall, K. S.. Mater. Trans. A 30, 2007 (1999).Google Scholar
4. Cockeram, B.V. and Rapp, R.A., Surf. Coat. Technol. 76–77, 20 (1995).Google Scholar
5. Bewlay, B. P., Briant, C. L., Davis, A. W. and Jackson, M. R., Mater Res Soc Symp Proc 2001;646:N 2.7.1–N 2.7.6.Google Scholar
6. Zelenitsas, K. and Tsakiropoulos, P., Intermetallics 14, 639 (2006).Google Scholar
7. Vellios, N. and Tsakiropoulos, P., Intermetallics 15, 1518 (2007).Google Scholar
8. Jackson, M. R., Bewlay, B. P. and Zhao, J. C, patent US 6,913,655 B2, July 5 (2005)Google Scholar
9. Schlesinger, M. E., Gokhale, A. B. and Abbaschian, R., J. Phase Equilib. 14, 502 (1993).Google Scholar
10. Pan, V. M., Latysheva, V. I., Kulik, O. G. and Popov, A. G., Russian Metallurgy, Translated from Izvestiya Akademii Nauk SSSR, Metally, 167 (1982).Google Scholar
11. Nowotny, H., Benesovsky, H. F., Rudy, E. and Wittman, A., Mh Chem Bd. 91, 975 (1960).Google Scholar
12. Zhao, J. C., Jackson, M. R. and Peluso, L. A., Mater. Sci. Eng. A 372, 21 (2004).Google Scholar
13. Bewlay, B. P., Jackson, M. R. and Bishop, R.R., J. Phase Equilib. 19, 577 (1998).Google Scholar
14. Thandorn, T. and Tsakiropoulos, P., unpublished research, The University of Sheffield, 2008.Google Scholar
15. Thandom, T.. and Tsakiropoulos, P., Intermetallics 18, 1033 (2010).Google Scholar
16. Zelenitsas, K. and Tsakiropoulos, P., Mater. Sci. Eng. A 416, 269 (2006).Google Scholar