Effect of Processing on the High Temperature Mechanical Properties of Mosi2

Published online by Cambridge University Press:  01 January 1992

S.N. Patankar  and
J.J. Lewandowski
S.N. Patankar
Affiliation:
Dept. of Materials Science and Engineering, Case Western Reserve University, Cleveland OH 44106
J.J. Lewandowski
Affiliation:
Dept. of Materials Science and Engineering, Case Western Reserve University, Cleveland OH 44106
Get access

Abstract

Polycrystalline MoSi2 has been processed via spex milling and the notched fracture behavior has been determined at 800 -1400°C. Elemental Mo and Si powders were mechanically alloyed to produce MoSi2 and were subsequently vacuum hot pressed to fully dense MoSi2 compacts. Microstructures were analyzed and both hardness and notched fracture tests were conducted at high temperatures. The material toughness was constant at 4.5 MPa m½between 800 and 1000 °C, with significant plasticity exhibited at 1200°C. The results will be compared to recent work on the effects of C on high temperature properties of MoSi2.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 288: Symposium L – High-Temperature Ordered Intermetallic Alloys V , 1992 , 829
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1) Meschter, P.J. and Schwartz, D.S., JOM, 41(1989), 52.Google Scholar
2) Calka, A.,Radlinski, A.P., Shanks, R.A. and Pogany, A.P., J. Mater. Sc. Letters, 10 (1991),734–737.Google Scholar
3) Munir, Z.A., High Temp. Sc., 27(1990), 279–293.Google Scholar
4) Atzmon, M., Phy. Rev. Letters, 64(1990), 487–490.Google Scholar
5) Kumar, K.S. and Mannan, S.K., Mater. Res. Soc. Symp. Proc, 133(1989), 415–421.Google Scholar
6) Atzmon, M., Mater. Sci. and Eng., A134(1991), 1326–1329.Google Scholar
7) Deevi, S.C., J. Mater. Sci., 26(1991), 3343–3353.Google Scholar
8) Vasudevan, A.K. and Petrovic, J.J., Mater. Sc. and Eng., A155(1992), 1–17.Google Scholar
9) Aikin, R.M., Scripta Metall. et Mater., 26(1992), 1025–1030.Google Scholar
10) Patankar, S.N.,Xiao, S.Q.,Lewandowski, J.J., and Heuer, A.H., J. of Materials Research, (1992),Submitted.Google Scholar
11) Maloy, S., Heuer, A.H.,Lewandowski, J.J. and Petrovic, J., J. Am. Ceram. Soc, 74(1991), 2704–2706.Google Scholar
12) Evans, A.G. and Charles, E.A., J. Am. Ceram. Soc, 59(1976), 371.Google Scholar