Electrical Conductivity of Zirconia-Mn Oxide Mixture

Published online by Cambridge University Press:  15 February 2011

J. H. Kim  and
G. M. Choi
J. H. Kim
Affiliation:
Department of Materials Science and Engineering, Pohang University of Science and Technology, Pohang, 790-784, Korea
G. M. Choi
Affiliation:
Department of Materials Science and Engineering, Pohang University of Science and Technology, Pohang, 790-784, Korea
Get access

Abstract

Mn2O3 was added to YSZ (8 mol% yttria- doped zirconia) either to form solid solution or two-phase (Mn2O3 and Mn2O3 doped-YSZ) mixed-conducting oxide. The electrical conductivity was measured between 600 and 1000°C in air using 4-probe d.c. method in a wide composition range to determine composition-dependent conductivity. Up to 12 mol% MnO1.5 addition, the conductivity decreases and the activation energy increases. With further increase of MnO1.5 content, the conductivity of composite begins to increase slowly and then increases rapidly after 30 mol% due to the interconnected, conductive Mn2O3 particles. Above 35 Mol% MnO1.5 content, the activation energy is nearly the same as that of Mn2O3. Hysteresis behavior shown in the conductivity of composite also provides the evidence of percolation by MnO1.5.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 548: Symposia EE – Solid State Ionics V , 1998 , 611
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Minh, N. Q., J. Am. Ceram. Soc., 76, p. 563–88 (1993).Google Scholar
2. Porat, O., Heremans, C. and Tuller, H. L., Solid State Ionics, 94, p. 75–83 (1997).Google Scholar
3. Liou, S. S. and Worrell, W. L., Appl. Phys. A49, p. 25–31 (1989).Google Scholar
4. Colomer, M. T. and Jurado, J. R. in Solid Oxide Fuel Cells, edited by Singhal, S. C. and Iwahara, H. (High Temp. Mater. and Batt. Div. Proc. 93–4, 1993) p. 523.Google Scholar
5. Huang, X. J. and Weppner, W., J. Chem. Soc., Faraday Trans., 92(12), p. 2173–78 (1996).Google Scholar
6. Jayaratna, M., Yoshimura, M. and Somiya, S., J. Mater. Sci., 22, p. 2011–16 (1987).Google Scholar
7. Han, P. and Worrell, W. L., J. Electrochem. Soc., 142, No.12, p. 4235–46 (1995).Google Scholar
8. Kawada, T., Sakai, N., and Yokokawa, H., Solid State Ionics, 53–56, p. 418–25 (1992).Google Scholar
9. Arashi, H. and Naito, H., Solid State Ionics, 53–56, p. 431–35 (1992).Google Scholar
10. Newnham, R.E., Chemtech., 12, p. 732–39 (1989).Google Scholar
11. Gauckler, L.J. and Sasaki, K., Solid State Ionics, 75, p. 203–10 (1995).Google Scholar
12. Tare, V.B., Mehrotra, G.M., and Wagner, J.B., Solid State Ionics, 18–19, p. 747–50 (1986).Google Scholar
13. Ostergard, M.J. L., Clausen, C., Bagger, C., and Mogensen, M., Electrochim. Acta, 40, No.12, p. 1971–81 (1995).Google Scholar
14. Dees, D. W., Claar, T. D., Easier, T. E., Fee, D. C., and Mrazek, F. C., J. Electrochem. Soc., 134, p. 2141–46 (1987).Google Scholar
15. Taimatsu, H., Wada, K., Kaneko, H., and Yamamura, H., J. Am. Ceram. Soc., 75, p. 401–05 (1992).Google Scholar
16. Chen, C. C., Nasrallah, M. M., and Anderson, H. U. in Solid Oxide Fuel Cells, edited by Singhal, S. C. and Iwahara, H. (High Temp. Mater. and Batt. Div. Proc. 93–4, 1993) p. 31.Google Scholar
17. Thampi, K.R., Mcevoy, A. J., and herle, J. Van, J. Electrochem. Soc., 142, No.2, p. 506–13 (1995).Google Scholar
18. Metsellaar, R., Tol, Van, and Piercy, P., J. Solid State Chem., 38, p. 335–41 (1981).Google Scholar
19. Pattanayak, J., Rao, V. Sitakara, and Maiti, H. S., J. Mater. Sci. Lett. 8, p. 1405–07 (1989).Google Scholar