Epitaxial Growth of (111) TbFe2 by Sputter Deposition

Published online by Cambridge University Press:  15 February 2011

C.T. Wang ,
R.M. Osgood ,
R.L. White  and
B.M. Clemens
C.T. Wang
Affiliation:
Department of Materials Science and Engineering, Stanford University, Stanford, CA 94305- 2205
R.M. Osgood
Affiliation:
Department of Materials Science and Engineering, Stanford University, Stanford, CA 94305- 2205
R.L. White
Affiliation:
Department of Materials Science and Engineering, Stanford University, Stanford, CA 94305- 2205
B.M. Clemens
Affiliation:
Department of Materials Science and Engineering, Stanford University, Stanford, CA 94305- 2205
Get access

Abstract

The effect of in-plane strain in (111)-oriented epitaxial TbFe2 films on the magnetization orientations was studied. Magnetocrystalline anisotropy, shape anisotropy, and magnetoelastic energy were calculated to determine the magnetization orientation in the presence of various in-plane strains. Theoretical considerations indicate that a compressive strain smaller than -0.065% can induce an out-of-plane magnetization. DC magnetron sputtering from Tb and Fe elemental targets was used to grow 50, 100, 200, and 400 Å thick epitaxial TbFe2(111) films at 600°C on (110)-oriented sapphire substrates with 1000 Å thick epitaxial Mo(110) buffer layers. The growth rate of the TbFe2(111) films was 1.44 Å/sec. X-ray diffractometry, Rutherford backscattering spectrometry, and vibrating sample magnetometry were used to characterize the crystal structure, epitaxial orientation, composition, stress and strain state, and magnetic properties of the TbFe2 films. The TbFe2(111) films were epitaxial with twins rotated by 60° and were in tensile strain states with the resulting in-plane magnetization.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 384: Symposium L – Magnetic Ultrathin films, Multilayers and Surfaces , 1995 , 79
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Clark, A.E., in Ferromagnetic Materials, edited by Wohlfahrt, E. P. (North-Holland, Amesterdam, 1908), p. 531.Google Scholar
2. Schatz, F., Hirscher, M., Schnell, M., Filk, G., and Kronmiiller, H., J. Appl. Phys. 76, 5380 (1994).Google Scholar
3. Chikazumi, S. and Charap, S.H., Physics of Magnetism (Kreiger, Malabar, Florida, 1986).Google Scholar
4. Bain, J.A., Ph.D. Dissertation, Stanford University, 1993.Google Scholar
5. Kwo, J., Hong, M., and Nakahara, S., Appl. Phys. Lett. 49, 319 (1986).Google Scholar
6. Siirgers, C. and Lbhneysen, H.V., Thin Solid Films 219, 69 (1992).Google Scholar