Heating Rate Effects in Rapid Thermal Annealing of Arsenic Implanted Silicon

Published online by Cambridge University Press:  22 February 2011

J.P. de Souza ,
P.F.P. Fichtner  and
D.K. Sadana
J.P. de Souza
Affiliation:
Instituto de Fisica, UFRGS, 91501-970 Porto Alegre, R.S., Brazil
P.F.P. Fichtner
Affiliation:
Escola de Engenharia, UFRGS, 90025-190 Porto Alegre, R.S., Brazil
D.K. Sadana
Affiliation:
Thomas J. Watson Research Center, IBM, Yorktown Heights, N.Y., 10598, USA
Get access

Abstract

Cross section TEM and channeling analysis show that the heating rate (HR) of a rapid thermal annealing (RTA) cycle affects the residual defect distribution in Si implanted with As+ to a heavy dose (≈ 1016 cm−2). Two defect bands are observed after solid phase epitaxial growth (SPEG): the first one centered at a depth corresponding to the projected range of the As (band I), and the second one located at depth corresponding to the original amorphous crystalline (a-c) interface (band II). The density of defects in band I is found to increase with the As dose, and with the annealing temperature (550 - 650°C, furnace annealing). However, for RTA (800 - 1000°C) both the density and depth distribution of these defects are dependent on HR. We propose that Si self-interstitials (SiI) are created at the a-c interface when As becomes substitutional during SPEG. The SPEG velocity determines whether the SiI are accommodated in the amorphous Si layer (low velocities) or are captured by the regrowing c-Si (high velocities)

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 342: Symposium G – Rapid Thermal and Integrated Processing III , 1994 , 351
Copyright
Copyright © Materials Research Society 1994

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Sands, T., Washburn, J., Myers, E. and Sadana, D.K., Nucl. Instr. Meth. B7/8, 337 (1985).Google Scholar
2. Wu, N.R., Sadana, D.K. and Washburn, J., Appl. Phys. Lett. 44, 782 (1984).Google Scholar
3. Pennycook, S.J., Narayan, J. and Culbertson, R.J., in Impurity Diffusion and Gettering in Silicon, edited by Fair, R.B., Pearce, C.W. and Washburn, J. (Mater. Res. Soc. 36, Pittsburg, PA, 1985) p. 151.Google Scholar
4. Olson, G.L., Roth, J.A., Hess, L.D. and Narayan, J., in Layered Structures and Interface Kinetics, edited by Furukawa, S. (KTK Scientific Publishers, Tokyo, 1985) p. 73.Google Scholar
5. Culbertson, R.J. and Pennycook, S.J., in Beam-Solid Interactions and Phase Transformations, ed. by Kurz, H., Olson, G.L. and Poate, J.M. (Mater. Res. Soc. 51, Pittsburg, 1986) p. 357.Google Scholar
6. Pennycook, S.J. and Culbertson, R.J., in Rapid Thermal Processing, edited by Sedgwick, T.O, Seidel, T.E. and Tsaur, B-Y (Mat. Res. Soc. vol. 52, Pittsburg, 1986) p. 37.Google Scholar
7. Hasenack, C.M., Souza, J.P. de and Erichsen, R. Jr, Semic. Sci. and Techn. 3, 979 (1988).Google Scholar