Lattice Site Location of Group VII Impurities in Silicon

Published online by Cambridge University Press:  25 February 2011

D.O. Boerma ,
P.J.M. Smulders  and
T.S. Wierenga
D.O. Boerma
Affiliation:
L.A.N. and Materials Science Centre, University of Groningen, Westersingel 34, 9718 CM Groningen, The Netherlands
P.J.M. Smulders
Affiliation:
L.A.N. and Materials Science Centre, University of Groningen, Westersingel 34, 9718 CM Groningen, The Netherlands
T.S. Wierenga
Affiliation:
L.A.N. and Materials Science Centre, University of Groningen, Westersingel 34, 9718 CM Groningen, The Netherlands
Get access

Abstract

Chlorine- and iodine-implanted silicon have been investigated using the channeling/RBS technique after laser and oven annealing. Both annealing methods result in good epitaxial recrystallization of the implanted layer. A large near-substitutional I fraction exceeding 90% was found after oven annealing at 875°C. The near-substitutional fractions found after laser annealing for Cl and I, and after thermal annealing at 900°C for Cl are in the order of 50% only. The precise lattice site for these Cl and I fractions are determined by fitting the angular scans with simulated results. The results are interpreted in terms of vacancy association.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 27: Symposium E – Ion Implantation and Ion Beam Processing of Materials , 1983 , 259
Copyright
Copyright © Materials Research Society 1984

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Dean, P.J., Cullis, A.G. and White, A.M., Handbook on Semiconductors, ed. Keller, S.P., Vol. 3 (North Holland Publ. Co., Amsterdam, 1980) p. 113.Google Scholar
2. Kemerink, G.J., de Wit, J.C., de Waard, H., Boerma, D.O. and Niesen, L., Phys. Lett. 82A, 255 (1981).Google Scholar
3. Kemerink, G.J., de Waard, H., Niesen, L. and Boerma, D.O., Hyperfine Interactions 14, 53 (1983).Google Scholar
4. Kemerink, G.J., Boerma, D.O., de Waard, H. and Niesen, L., Rad. Eff. 70, 183 (1983)Google Scholar
4a. and Rad. Eff. 69, 83 (1983).Google Scholar
5. Boerma, D.O., Niesen, L., Smulders, P.J.M. and du Marchie van Voorthuysen, E.H., Nucl. Instr. Meth. 209/210, 375 (1983).Google Scholar
6. Greeuw, G. and Verwey, J.F., Solid State Electronics 26, 241 (1983).Google Scholar
7. Biersack, J.P. and Ziegler, J.F., Nucl. Instr. Meth. 194, 93 (1982).Google Scholar