Measurement of the Critical Level of Moisture for Initiation of Water-Vapor-Induced Environmental Embrittlement in an Fe3Al-Based Alloy

Published online by Cambridge University Press:  01 January 1992

C. G. McKamey  and
E. H. Lee
C. G. McKamey
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831-6114
E. H. Lee
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831-6114
Get access

Abstract

Iron aluminides based on Fe3Al are of interest as structural materials because of their excellent corrosion resistance in many environments. However, studies have shown that one of the major causes of low room temperature tensile ductility, which so far has limited the use of these alloys, is an environmental reaction involving aluminum in the presence of water vapor. During this reaction, atomic hydrogen is released, moves into the sample ahead of the crack tip during stressing, and causes failure before the true ultimate tensile strength of the material is reached. This reaction is reduced significantly by testing in oxygen or vacuum. In the present study, an Fe3Al-based alloy was tensile tested as a function of the level of water vapor in the test environment, from a vacuum of 10−4 Pa to a water vapor partial pressure of 1330 Pa. The results show that a water vapor level of as low as 133 Pa (1 torr) can result in significant embrittlement. The fracture mode remains transgranular cleavage, but the scale of the cleavage facets changes with the water vapor level.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 288: Symposium L – High-Temperature Ordered Intermetallic Alloys V , 1992 , 983
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. DeVan, J. H., in Oxidation of High-Temperature Intermetallics. ed. by Grobstein, T. and Doychak, J. (TMS, Warrendale, PA, 1989), pp. 107–15.Google Scholar
2. Smialek, J. L., Doychak, J., and Gaydosh, D. J., in Oxidation of High-Temperature Intermetallics, ed. by Grobstein, T. and Doychak, J., (TMS, Warrendale, PA, 1989), pp. 83–95.Google Scholar
3. McKamey, C. G., DeVan, J. H., Tortorelli, P. F., and Sikka, V. K., J. Mater. Res. 6, 1779 (1991).Google Scholar
4. Sikka, V. K., McKamey, C. G., Howell, C. R., and Baldwin, R. H., Fabrication and Mechanical Properties of Fe3 Fabrication and Mechanical Properties of Fe3Al-Based Aluminides Al-Based Aluminides. ORNL/TM-11465 (Oak Ridge National Laboratory, Oak Ridge, TN, March 1990).Google Scholar
5. Sikka, V. K., McKamey, C. G., Howell, C. R., and Baldwin, R. H., Properties of Large Heats of Fe3 Al-Based Alloys. ORNL/TM-11796 (Oak Ridge National Laboratory, Oak Ridge, TN, March 1991).Google Scholar
6. Liu, C. T., Lee, E. H., and McKamey, C. G., Scr. Metall. 23, 875 (1989).Google Scholar
7. Liu, C. T., McKamey, C. G., and Lee, E. H., Scr. Metall. 24, 385 (1990).Google Scholar
8. Castagna, A. and Stoloff, N. S., Scripta Metall. 26, 273 (1992).Google Scholar
9. McKamey, C. G. and Liu, C. T., to be published in Environmental Effects on Advanced Materials, proceedings of ADVMAT/91 (NACE, 1992).Google Scholar
10. Liu, C. T. and George, E. P., Scr. Metall. 24, 1285 (1990).Google Scholar
11. Nishimura, C. and Liu, C. T., Scr. Metall. 25, 791 (1991).Google Scholar
12. Takasugi, T., Suenaga, H., and Izumi, O., J. Mater. Sci. 26, 1179 (1991).Google Scholar
13. Nishimura, C. and Liu, C. T., Acta Metall. 40, 723 (1992).Google Scholar
14. Kuruvilla, A.K. and Stoloff, N. S., Scr. Metall. 19, 83 (1985).Google Scholar
15. Stoloff, N. S., J. Metals, 40, 23 (1988).Google Scholar
16. Takasugi, T. and Izumi, O., Acta Metall. 34, 607 (1986).Google Scholar
17. Masahashi, N., Takasugi, T., and Izumi, O., Metall. Trans. 19A, 353 (1988).Google Scholar
18. McKamey, C. G., Liu, C. T., David, S. A., Horton, J. A., Pierce, D. H., and Campbell, J. J., Development of Iron Aluminides for Coal Conversion Systems. ORNL/TM-10793 (Oak Ridge National Laboratory, Oak Ridge, TN, July 1988).Google Scholar