SCC growth rate measurements and surface oxide film characterization on high SFE austenitic stainless steels in a simulated BWR water environment

Published online by Cambridge University Press:  14 July 2014

S. Ooki ,
T. Yonezawa ,
M. Watanabe  and
H. Kokawa
S. Ooki
Affiliation:
R&D Center, Engineering R&D Department, Tokyo Electric Power Company, 4-1 Egasaki-cho, Tsurumi-ku, Yokohama, 230-8510, Japan
T. Yonezawa
Affiliation:
FRI, NICHe, Tohoku University, 6-6-10 Aoba, Aramaki, Aoba-ku, Sendai, 980-8579, Japan
M. Watanabe
Affiliation:
FRI, NICHe, Tohoku University, 6-6-10 Aoba, Aramaki, Aoba-ku, Sendai, 980-8579, Japan
H. Kokawa
Affiliation:
Department of Materials Proceeding, Graduate School of Engineering, Tohoku University, 6-6-2 Aoba, Aramaki, Aoba-ku, Sendai, 980-8579, Japan
Get access

Abstract

Stress Corrosion Cracking (SCC) has been detected in Boiling Water Reactors (BWRs) on core shrouds and primary water re-circulation piping made of low carbon stainless steels. Material hardening strongly affects SCC propagation behavior, and SCC growth rates increase with increasing hardness of austenitic stainless steels caused by cold work or neutron irradiation.

Research work has been conducted in the authors’ laboratories with the aim of improving SCC resistance using chemical composition control of stainless steels. It has been previously reported that high stacking fault energy (SFE) materials showed better SCC resistance than low SFE materials due to hardening being suppressed in high SFE materials. In the present study, SCC growth rate (CGR) tests were performed using 15% cold worked Types 316L and 25Cr-20Ni stainless steels in a simulated BWR water environment. The 25Cr-20Ni stainless steel used has high SFE value due to chemical composition control and measured SCC growth rates were lower than those of low SFE stainless steels.

However, oxidation behavior is one of the more important factors influencing SCC of austenitic stainless steels in addition to material hardening behavior, and the influence of the chemical composition control necessary to increase SFE on oxidation behavior in BWR primary coolants is still unclear. In this study, therefore, immersion tests using Types 316L and 25Cr-20Ni stainless steel specimens were also conducted in the simulated BWR water environment. The surface oxide films on the specimens were then analyzed with micro-Raman spectroscopy and glow discharge optical emission spectroscopy in order to help clarify the oxidation behavior.

The results of these tests and analyses showed that the NiFe2O4 content of the outer oxide layers on the high SFE stainless steels was higher than that on the low SFE stainless steels. The inner oxide film on the 25Cr-20Ni stainless steel also had a high chromium content.

Based on the above results, SCC resistance and oxidation behavior of high SFE austenitic stainless steels in a simulated BWR water environment will be discussed.

Keywords

chemical compositionoxidemetal
Type
Articles
Information
MRS Online Proceedings Library (OPL) , Volume 1715: Symposium EEE – Materials Behavior under Extreme Irradiation, Stress or Temperature , 2014 , mrss14-1715-eee08-07
Copyright
Copyright © Materials Research Society 2014 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Yonezawa, T., Kanasaki, H., Taneike, M., Sakaguchi, Y., Ooki, S., Tezuka, H., Takamori, K., Suzuki, S., 14th International Conference on Environmental Degradation of Materials in Nuclear Power Systems, (2009) pp. 1274–1288 Google Scholar
Andresen, P. L., Emigh, P. W., Morra, M. M. and Horn, R. H., 11th International Conference on Environmental Degradation of Materials in Nuclear Power Systems, (2003) p816–833 Google Scholar
Yonezawa, T., Suzuki, K., Ooki, S. and Hashimoto, H., Metallurgical and Materials Transactions A, 44A, (2013) pp. 5884–5896 CrossRefGoogle Scholar
Suzuki, S., Collected Abstracts of ICG-EAC (2009)Google Scholar
Beverskog, B. and Puigdomenech, I., Corrosion, 55 (1999) pp. 1077–1087 CrossRefGoogle Scholar
Miyajima, M., Hirano, H., Domae, M. and Kushida, H., Resaerch Report of CRIEPI (2001)Google Scholar
J Edwards, D., Thomas, L. E., Asano, K., Ooki, S., Bruemmer, S. M., 13th International Conference on Environmental Degradation of Materials in Nuclear Power Systems, (2007)Google Scholar
Obata, R., Koshiishi, M., Anzai, H., Nakade, K., Ooki, S., Takamori, K., Suzuki, S., 14th International Conference on Environmental Degradation of Materials in Nuclear Power Systems, (2009)Google Scholar