Synthesis and Electrical Property of VO2 (M) Nanorods

Published online by Cambridge University Press:  01 February 2011

W. Chen ,
L. Q. Mai ,
Y. Y. Qi ,
H. Yu  and
J. F. Peng
W. Chen*
Affiliation:
Institute of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070 Hubei, P. R. China
L. Q. Mai
Affiliation:
Institute of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070 Hubei, P. R. China
Y. Y. Qi
Affiliation:
Institute of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070 Hubei, P. R. China
H. Yu
Affiliation:
Institute of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070 Hubei, P. R. China
J. F. Peng
Affiliation:
Institute of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070 Hubei, P. R. China
*
* E-mail: chenw@public.wh.hb.cn
Get access

Abstract

VO2 (M) nanorods have been synthesized and the morphology and structure of the sample were characterized by XRD, SEM, and HRTEM. The results show that for VO2 (M) nanorods, the transition temperature is 65 °C and the hysteresis loop width is 8 °C. The active energy of low temperature semiconducting phase is 0.2eV, which indicates that its Fermi energy level situates on the middle energy level of the forbidden-band. The doping of Mo6+ decreases its transition temperature.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 848: Symposium FF – Solid-State Chemistry of Inorganic Materials V , 2004 , FF8.7
Copyright
Copyright © Materials Research Society 2005

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERRENCE

1. Hanlon, T. J., Wslker, R. E., and Coat, J. A., Thin Solid Films. 405, 234 (2002)Google Scholar
2. Guinneton, F., Sauques, L., and Valmalette, J. C., J Phys Chem Solid. 62, 1229 (2001)Google Scholar
3. Xia, Y., Yang, P., and Sun, Y., Adv Mater. 15, 353 (2003)Google Scholar
4. Chen, W., Mai, L.Q., Xu, Q., Zhu, Q.Y., and Peng, J. F., Key Eng Mater. 249, 145 (2003)Google Scholar
5. Krumeich, F., Muhr, H. J., Niederberger, M., Bieri, F., Schnyder, B., and Nesper, R.. J Am Chem Soc. 121, 8234 (1999)Google Scholar
6. Almeida, L. A. L., Deep, G. S., Lima, A. M. N.. Appl. Phys. Lett. 77, 4365 (2000)Google Scholar
7. Sahana, M. B., Subbanna, G. N., and Shivashankar, S. A. J. Appl. Phys. 92, 6495 (2002)Google Scholar
8. Mai, L. Q., Chen, W., Xu, Q., Peng, J. F., Zhu, Q. Y.. Chem Phys Lett, 382, 307 (2003)Google Scholar