The rhodonite-group mineral with the idealised, end-member formula MnMn4[Si5O15] and the crystal chemical formula VIIM(5)MnVIM(1–3)Mn3VIIM(4)Mn[Si5O15] (Roman numerals indicate coordination numbers) is defined as a valid mineral species named vittinkiite after the type locality Vittinki (Vittinge) mines, Isokyrö, Western and Inner Finland Region, Finland. Vittinkiite is an isostructural analogue of rhodonite, ideally CaMn4[Si5O15], with Mn2+ > Ca at the M(5) site. Besides Vittinki, vitiinkiite was found in more than a dozen rhodonite deposits worldwide, however, it is significantly less common in comparison with rhodonite. The mineral typically forms pink to light pink massive, granular aggregates and is associated with quartz, rhodonite, tephroite, pyroxmangite and Mn oxides. Vittinkiite is optically biaxial (+), with α = 1.725(4), β = 1.733(4), γ = 1.745(5) and 2Vmeas = 75(10)° (589 nm). The chemical composition of the holotype (wt.%, electron microprobe) is: MgO 0.52, CaO, 0.93, MnO 51.82, FeO 1.26, ZnO 0.11, SiO2 46.48, total 101.12. The empirical formula calculated based on 15 O apfu is Mn4.71Ca0.11Fe0.11Mg0.08Zn0.01Si4.99O15. Vittinkiite is triclinic, space group P$\bar{1}$, with a = 6.6980(3), b = 7.6203(3), c = 11.8473(5) Å, α = 105.663(3), β = 92.400(3), γ = 94.309(3)°, V = 579.38(7) Å3 and Z = 2. The crystal structure is solved on a single crystal to R1 = 3.85%. Polymorphism of MnSiO3 (rhodonite-, pyroxmangite-, garnet- and clinopyroxene-type manganese metasilicates) is discussed, as well as the relationship between vittinkiite and pyroxmangite, ideally Mn7[Si7O21], and the application of infrared spectroscopy for the identification of manganese pyroxenoids.

This paper presents the nomenclature of the rhodonite group accepted by the Commission on New Minerals, Nomenclature and Classification of the International Mineralogical Association (IMA). An overview of the previous studies of triclinic (space group P$\bar{1}$) pyroxenoids belonging to the rhodonite structure type, with a focus on their crystal chemistry, is given. These minerals have the general structural formula VIIM(5)VIM(1)VIM(2)VIM(3)VIM(4)[Si5O15]. The following dominant cations at the M sites are known at present: M(5) = Ca or Mn2+, M(1–3) = Mn2+; and M(4) = Mn2+ or Fe2+. In accordance with the nomenclature, the rhodonite group consists of three IMA-approved mineral species having the following the general chemical formulae: M(5)AM(1–3)B3M(4)C[Si5O15], where A = Ca or Mn2+; B = Mn2+; and C = Mn2+ or Fe2+. The end-member formulae of approved rhodonite-group minerals are as follows: rhodonite CaMn3Mn[Si5O15]; ferrorhodonite CaMn3Fe[Si5O15]; and vittinkiite MnMn3Mn[Si5O15].

In the Gåsborn area, West Bergslagen, central Sweden, Mn-silicate-magnetite-jacobsite skarns were formed as the result of three successive processes. (1) Deposition of exhalative-sedimentary manganiferous iron-ore-bearing sediments together with cherts and volcanics. (2) Intrusion of a synvolcanic anorogenic granite and some slightly younger gabbros and tonalites: under influence of these intrusives the manganiferous iron-ore-bearing sediments were metamorphosed into (a) rhodonite(I)-magnetite-pyrophanite-garnet assemblages; (b) (manganiferous) hedenbergite(I)-allanite-titanite-garnet-magnetite assemblages; (c) tephroite-jacobsite-pyrophanite-garnet assemblages and (d) magnetite-bearing quartzites. (3) Release of hydrothermal fluids from the granite and subsequent alteration of the above assemblages into metasomatic infiltration skarns, consisting of rhodonite(II), garnet, hedenbergite(II), biotite, actinolite or edenite (with up to 20.11 wt.% MnO), chlorite, bementite, fluorite, helvite, rhodochrosite, hematite, rutile and accessory galena, sphalerite, wittichenite, aikinite, pyrrhotite, chalcopyrite and pyrite.

The maximum temperature (T) and pressure (P) during contact metamorphism are estimated at 550°C and 1.0 kbar respectively. The fluid under influence of which the metasomatic infiltration skarns were formed was relatively rich in Fe, Cl and F and carried little or no Mg and Mn.

During early diagenesis (beginning of stage 2) fo2 was between the hematite/magnetite (hm/mt) and the hausmannite + hematite = jacobsite buffers (h + m = j). During stage 2, with increasing T, fo2 changed from above to below hm/mt. Magnetite and jacobsite at some distance from the hydrothermal veins from which the metasomatic skarn-forming fluids were released, were altered during stage 3 into hematite. Magnetite in, and close to the hydrothermal veins was not altered to hematite, implying an increase in fo2 to above hm/mt with increasing distance from these veins.