Single crystals of synthetic reidite and natural radiation-damaged zircon from Okueyama, Japan were investigated using X-ray diffraction. The pressure-induced zircon–reidite transition is described by the twisting and translations of SiO4 tetrahedra with disappearance of the SiO4–ZrO8 shared edges. The lattice of radiation-damaged zircons expands mainly from α-decays of radioactive elements such as U and Th. Although old radiation-damaged zircons show anomolous lattice distortion, young radiation-damaged zircons do not show such distortions. These distortions are caused by thermal recovery that suppresses the Si4+–Zr4+ repulsion between the SiO4 tetrahedron and ZrO8 dodecahedron. These changes in structure can be understood by considering the cation–cation repulsion between the SiO4–ZrO8 shared edges.

Zircon- and reidite-type ZrSiO4 produced by shock recovery experiments at different pressures have been studied using infrared (IR) and Raman spectroscopy. The v3 vibration of the SiO4 group in shocked natural zircon shows a spectral change similar to that seen in radiation-damaged zircon: a decrease in frequency and increase in linewidth. The observation could imply a possible similar defective crystal structure between the damaged and shocked zircon. The shock-pressure-induced structural phase transition from zircon (I41/amd) to reidite (I41/a) is proven by the occurrence of additional IR and Raman bands. Although the SiO4 groups in both zircon- and reidite-ZrSiO4 are isolated, the more condensed scheelite gives rise to Si–O stretching bands at lower frequencies, suggesting a weakening of the bond strength. Low-temperature IR data of the reidite-type ZrSiO4 show an insignificant effect of cooling on the phonon modes, suggesting that the structural response of reidite to cooling-induced compression is weak and its thermal expansion is very small.