The I13 transmission X-ray microscope at Diamond Light Source (DLS) has been designed to cover a broad range of energies and field of views. The beamline operates on an undulator source, and a multilayer monochromator can be used to work at a larger bandwidth to enable faster acquisitions. The experimental design includes large working distances for the optics to allow installing in situ sample environments. This paper presents the current state of the experimental system and shows some of the latest results.

Three-dimensional (3D) nondestructive microstructural characterization was performed using full-field transmission X-ray microscopy on an Sn-rich alloy, at a spatial resolution of 60 nm. This study highlights the use of synchrotron radiation along with Fresnel zone plate optics to perform absorption contrast tomography for analyzing nanoscale features of fine second phase particles distributed in the tin matrix, which are representative of the bulk microstructure. The 3D reconstruction was also used to quantify microstructural details of the analyzed volume.

The oxidation of nickel powder under a controlled gas and temperature environment was studied using synchrotron-based full-field transmission X-ray microscopy. The use of this technique allowed for the reaction to be imaged in situ at 55 nm resolution. The setup was designed to fit in the limited working distance of the microscope and to provide the gas and temperature environments analogous to solid oxide fuel cell operating conditions. Chemical conversion from nickel to nickel oxide was confirmed using X-ray absorption near-edge structure. Using an unreacted core model, the reaction rate as a function of temperature and activation energy were calculated. This method can be applied to study many other chemical reactions requiring similar environmental conditions.

The microstructure of Co/Pt multilayers with large perpendicular magnetic anisotropy (PMA) was investigated before and after energetic ion irradiation. No pronounced microstructural changes were detected at ion doses sufficient to completely reduce the PMA and cause a spin reorientation transition to in-plane. Ion-induced displacement of Co and Pt atoms near Co/Pt interfaces lead to local “roughening” and Co layer strain relaxation, reducing the PMA. The magnetic domain confinement induced by ion irradiation and magnetic patterning by selective ion irradiation were also investigated.