Nb Contacts to GaAs: Thermal Stability and Phase Formation

Published online by Cambridge University Press:  21 February 2011

Kevin J. Schulz ,
Xiang-Yun Zheng  and
Y. Austin Chang
Kevin J. Schulz
Affiliation:
University of Wisconsin-Madison, Department of Metallurgical and Mineral Engineering, 1509 University Avenue, Madison, WI 53706
Xiang-Yun Zheng
Affiliation:
University of Wisconsin-Madison, Department of Metallurgical and Mineral Engineering, 1509 University Avenue, Madison, WI 53706
Y. Austin Chang
Affiliation:
University of Wisconsin-Madison, Department of Metallurgical and Mineral Engineering, 1509 University Avenue, Madison, WI 53706
Get access

Abstract

The applicability of Nb as a Schottky barrier on GaAs depends to a large extent on the thermal stability of the contacts. In this study, bulk diffusion couple and phase diagram studies in addition to thin film studies were completed to understand the stability of and the reactions at the Nb/GaAs interface. Nb thin films were deposited onto GaAs substrates by dc magnetron sputtering and were annealed in the temperature range 300 to 1000°C. Analysis was done using plan-TEM and XTEM. The Nb/GaAs interface was found to break down into a series of binary compounds above 500°C. Bulk diffusion couples annealed at 600°C were analyzed using an electron microprobe. The stable sequence of phases formed in the couple, i.e., the diffusion path, was determined and was used to rationalize the observed compound formation in the thin film contact system.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 108 , 1987 , 455
Copyright
Copyright © Materials Research Society 1988

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Footnotes

*

This work was sponsored by the U.S. Department of Energy under contract No. DE-FGO2-86ER452754

References

REFERENCES

1.Wu, X.W., Zhang, L.C., Bradley, P., Chin, D.K., and Van Duzer, T., Appl. Phys. Lett. 50, 288 (1987).Google Scholar
2.Ding, J. (private communication).Google Scholar
3.Lince, J.R., Tsai, C.T., and Williams, R.S., J. Hater. Res. 1, 537 (1986).Google Scholar
4.Beyers, R., Kim, K.B., and Sinclair, R., J. Appl. Phys. 61, 2195(1987).Google Scholar
5.Tsai, C.T. and Williams, R.S., J. Hater. Res. 1, 352 (1986).Google Scholar
6.McGilp, J.F., J. Hater. Res. 2, 516 (1987).Google Scholar
7.Lin, J.-C., Hsieh, K.-C., Schulz, K.J., and Chang, Y.A., J. Hater. Res. (in press).Google Scholar
8.Schmid-Fetzer, R., J. Electron. Mater. (in press).Google Scholar
9.Yu, M.R., Zhu, F.R., Wang, X., Wang, B.Q., Zao, K., Pu, P.S., and Lei, C.L., Chin. J. Semicond. 6, 55 (1985).Google Scholar
10.Lin, J.C., Schulz, K.J., Hsieh, K.-C., and Chang, Y.A., J. Electrochem. Soc. (in press).Google Scholar
11.Sands, T., Keramidas, V.G., Yu, K.M., Washburn, J., and Krishnan, K., J. Appl. Phys. (in press).Google Scholar
12.Wagner, C., J. Electrochem. Soc. 103, 571 (1956).Google Scholar