High-resolution transmission electron microscopy (HRTEM) and electron diffraction experiments have been performed on R1 and R> 1 illite/smectite (I/S) samples that from X-ray powder diffraction (XRD) experiments appear to contain well-ordered layer sequences. The HRTEM images confirmed earlier computer image simulations, which suggested that periodicities due to I/S ordering can be imaged in TEM instruments of moderate resolution. The experiments also confirmed that in instruments of this sort, the strongest contrast arising from the compositional difference between I and S layers occurs under rather unusual imaging conditions of strong overfocus. Some selected-area electron diffraction (SAD) patterns showed additional diffraction spots consistent with R1 and R3 ordering. SAD patterns and cross-fringes arising in HRTEM images from non-00l reciprocal lattice rows indicated that the stacking vectors of most adjacent 2:1 layers were not randomly oriented with respect to each other. Thus, the I/S was not fully turbostratic, but instead consisted of very thin, coherently stacked crystallites that extended across the fundamental particles postulated by Nadeau and coworkers.

S/(I + S) ratios were determined for about seventy HRTEM images obtained and interpreted by three different TEM operators. These ratios were consistent with those obtained from standard XRD procedures, suggesting that results obtained by XRD can be used to infer the initial structural state of mixed-layer I/S prior to treatment of samples for XRD experiments. The HRTEM experiments thus demonstrated that the two specimens examined consisted of ordered I/S existing as small crystals, most of which contained more layers than the fundamental particles of Nadeau and coworkers. The non-turbostratic stacking suggests an energetic interaction between the individual fundamental particles, leading to at least two alternative thermodynamic descriptions of these materials. Although the I/S crystals in the present experiments probably were disaggregated into fundamental particles during sample preparation for XRD, the I/S crystals appear to have separated only along the smectite interlayers. If the term “fundamental particle” is to be used for primary, untreated I/S, its original definition should be modified to include not only free particles, but also those that occur as layers within small crystals. It further should be recognized that these particles can interact thermodynamically and crystallographically with their neighbors.

Sorption and desorption of two neutral, nonpolar organic compounds, 1,2-dibromoethane (EDB, a soil fumigant) and trichloroethene (TCE, an industrial solvent and common ground-water contaminant), by pyrophyllite, kaolinite, illite, and smectite were investigated. For sorption, vapors of the compounds in a stream of dry N2 gas were passed through columns of the powdered clay minerals for different periods of time. The compounds retained by the clays were extracted with methanol and analyzed by gas chromatography (GC). For desorption, N2 was passed through the treated samples, and the desorbed compounds were collected in hexane traps and analyzed by GC.

Initially sorption was rapid for several hours but then proceeded at a slower rate for many hours. Surprisingly, the clays sorbed large quantities of these neutral compounds; for example, the pyrophyllite, kaolinite, illite, and smectite sorbed about 3, 5, 6, and 9% EDB, respectively, by weight. The amounts of TCE sorbed, which is more volatile than EDB, were somewhat less. Only a portion of the compounds sorbed over a period of time were desorbed in the same period of time. Desorption was rapid initially but then proceeded at a slow rate; slow desorption continued for over 100 hr from samples which had undergone sorption for only 1–2 hr. A two-compartment efflux model was used to describe the sorption behavior. A rapidly desorbing component was considered to be present on the outer surfaces of the clay aggregates and a slowly desorbing component, in the interior pores of the aggregates.

To provide a greater understanding of the crystallization of iron oxides under natural aqueous conditions, the combined effect of an inorganic ion (Mn2+) and a reducing organic ligand (L-cysteine) on the conversion of noncrystalline ferric hydroxide to goethite and/or hematite was investigated at pH 8.

At cysteine: Fe ratios ≥ 0.2, L-cysteine caused noncrystalline iron(III) hydroxide to transform rapidly into goethite at pH 8; in the absence of the organic ligand, hematite was the predominant reaction product. The presence of Mn (≥9 mole %) in the cysteine-ferric hydroxide system retarded crystallization and reduced the goethite-promoting effect of cysteine.

Polarographic measurements showed that the adsorption of cysteine on noncrystalline iron(III) hydroxide was immediately followed by the oxidation of cysteine to the disulfide with simultaneous reduction of a proportion of the interracial ferric ions. The partly reduced noncrystalline iron(III) hydroxide dissolved at pH 8 more rapidly than the original material, thus facilitating the formation of goethite. In Mn(II)-noncrystalline iron(III) hydroxide coprecipitates, the interfacial oxidation/reduction reaction with cysteine (and hence the partial reduction of the noncrystalline phase) was reduced, due to replacement of some interfacial Fe(III) by non-reducible Mn.

At pH 8, uptake of Mn by crystalline iron oxides was low (< 5 mole %). Mn precipitated preferentially as pure Mn phases, either rhodochrosite (in NaHCO3 buffer) or hausmannite (in NH4Cl/NH3 buffer).

Intercalation of sodium and potassium salts of lauric, myristic, palmitic, elaidic, oleic, 12-hydroxystearic, and a blend of C8–C10 acids in kaolinite has been followed by X-ray powder diffraction, nuclear magnetic resonance (NMR), Fourier-transform infrared spectroscopy, and thermal studies. The 7-Å ‘c’ axis spacing in kaolinite expands to 11 Å as a result of intercalation; this expansion is independent of the alkyl chain length of the fatty acid. The orientation of the organic molecules in the kaolinite interlayer is nearly flat, and 1H NMR indicates an enhanced ordering in the potassium laurate intercalate. The reversal or equalization of the relative intensities of hydroxyl bands at 3696 and 3619 cm-1 of kaolinite are related to the phenomenon of intercalation. The decomposition temperature of these salts decreases when they are intercalated in kaolinite.

Mineralogical (XRD), morphological (transmission electron microscopy), chemical (major, rare-earth elements, and scanning-transmission electron microscopy), and isotope (Sr, O, H) measurements were made of marine detrital smectite from shales to study their reactions during early diagenesis. Albian, Aptian, and Palaeogene smectite samples were selected from Deep Sea Drilling Project drill cores taken in the Atlantic Ocean and from outcrops and drill cores from Belgium and northern France. Detrital, fake-like smectite particles seem to have adapted to their depositional environment by isochemical dissolution and subsequent crystallization of authigenic, lath-like particles. The major-element and rare-earth element compositions of both types of particles are similar. The Sr isotope chemistry suggests that the dissolution-crystallization process occurred soon after deposition in an almost closed chemical system. Except for slight changes in the amount of Fe and the oxygen isotope composition, the reaction took place without noticeable chemical exchange with the interstitial or marine environment. Such closed-system recrystallization of clay minerals may be a common diagenetic process if the water/rock ratio is small, as in shales.

The effects of humic acid (HA) on the crystallization of precipitation products of Al under mildly acidic to alkaline conditions were investigated. The extent of Al precipitation substantially decreased with increasing HA concentration (0 to 75 µg/ml) in the pH range 6 to 10 during the 80-day aging period. The X-ray powder diffraction (XRD) data show that, at pH 6.0, the amount of pseudoboehmite formed in the systems decreased with the increasing concentration of HA present. The proportion of Al hydroxide polymorphs (gibbsite and bayerite) was greatly influenced by the amounts of HA present in the systems. At pH 6.0 and HA concentration of 37.5 µg/ml, all the precipitation products of Al were noncrystalline. At pH 8.0 and a HA concentration of 12.5 µg/ml, the formation of gibbsite and bayerite was completely inhibited and only pseudoboehmite was evident in the XRD patterns. Further increase in HA concentration (25–75 µg/ml HA) at pH 8.0 resulted in no precipitation of Al, and only a broad peak at ∼3.3 Å, characteristic of HA, was observed. The XRD patterns of the precipitates of Al formed in the absence of HA at pH 10.0 showed the characteristic peaks of bayerite. At pH 10.0, the precipitation products of Al formed even at the HA concentration of 2.5 µg/ml yielded no XRD peaks. Infrared absorption spectra and transmission electron micrographs of the precipitation products of Al formed in the systems studied substantiate the findings obtained by XRD. The data obtained in this study indicate that HA affects the formation of Al hydroxide polymorphs, pseudoboehmites and short-range ordered mineral colloids.

Contact angles of glycerol and diiodomethane drops were measured on the surface of kaolin pellets covered with different amounts of dodecylamine chloride (DDACl) to as much as one monolayer. For a glycerol drop, the contact angle changed from 25.7° (bare surface) to 45.4° for the surface precoated with 0.125 monolayer of DDACl, but remained nearly constant above this level up to one monolayer. For a diiodomethane drop, the contact angle changed from 28.6° (bare surface) to 58.1° for one DDACl monolayer precoating. Using these contact angles and a modified Young equation, the dispersive and nondispersive components of the surface free energy of DDACl-covered kaolin were calculated. These data showed that in the extreme case (one monolayer) the dispersive component was reduced by the DDACl from ∼36 mJ/m2 (bare surface) to 25.4 mJ/m2, i.e., the value characteristic for paraffin (25.5 mJ/m2); however, the nondispersive component was not reduced to zero. A minimum value (15.83 mJ/m2) was determined for the sample covered with 0.125 DDACl monolayer (calculated), and a slight increase in the nondispersive component was observed for greater coverages. Such a change of the nondispersive component suggests that, at higher coverages, some adsorbed DDACl molecules were oriented with their polar ends off the surface. Based on the values of the γsfd and γsfn, the work of water spreading was calculated. This work was positive for the bare surface (32.8 mJ/m2) and methanol-treated (36.5 mJ/m2) kaolin surface, but negative for 0.125 DDACl monolayer precoating (-31.1 mJ/m2). It remained essentially unchanged for higher coverages. These data mean that bare and methanol-treated kaolinite surfaces were hydrophilic and that DDACl-treated surfaces were hydrophobic.

The prevailing concept that positive-edge to negative-face attraction accounts for the rheological behavior of montmorillonite suspensions at low electrolyte concentration was investigated. In one experiment, Mg2+ released from Na-montmorillonite was measured at several NaCl concentrations; in a second experiment, the viscosity, η, and the extrapolated shear stress, θ, were measured at several clay concentrations, pHs, and NaCl concentrations; and in a third experiment, the absorbance, A, was measured at two wavelengths (450 and 760 nm) at different clay and electrolyte concentrations. The released Mg2+ decreased with increasing NaCl concentration until it became zero at a NaCl concentration between 0.01 and 0.02 M, depending on pH. Thereafter, it increased with increasing NaCl concentration. Both θ and η were highly correlated with the amount of released Mg2+. Also, A remained constant until the NaCl concentration corresponded to that at the minimum of θ. Thereafter, it increased and became linearly related to θ. These results suggest: (1) positive-edge to negative-face interaction cannot solely account for the rheological properties of montmorillonite at low electrolyte concentration, and (2) the release of octahedral Mg2+ from montmorillonite affects θ, because it reduces the negative charge on the particles and, thereby, the repulsive force between them.

Sepiolite from Vallecas-Vicálvaro, Spain, contains 1.3% fluorine. Laser microprobe mass spectrometry of this sepiolite suggests the presence of fragments of (SiO2)nOMgF and (SiO2)nOMgOH, which are typical of the sepiolite structure. During thermal dehydroxylation, the fluorine in this sepiolite is removed simultaneously with OH groups at about 750°C. Nuclear magnetic resonance spectroscopy (NMR) of 19F indicates that the fluorine is located in the interior of the sepiolite structure, probably substituting for OH groups, and is homogeneously distributed. In the Vallecas-Vicálvaro sepiolite, about one of every four OH groups bound to Mg2+ is substituted by fluorine. The kinetics of extraction of Mg2+ and F- ions by acid treatment (1 N HCl) shows a more rapid extraction of Mg2+, with a monotonous decrease of the Mg/F ratio as the extent of extraction increases. These results support the internal location of the fluorine, as suggested by the NMR data.

Glauconites in early ankerite concretions, ferroan calcite-cemented sandstones, and uncemented sandstones in the first Wilcox sandstone of the Lockhart Crossing field, Livingston Parish, Louisiana, show a progressive substitution of Fe for octahedral Al with increasing diagenesis. An octahedral Fe content of 0.50 atoms was calculated from glauconite located in early ankeritic concretions. Octahedral Fe averaged 0.60 and 0.90 atoms in later ferroan calcite-cemented sandstone and uncemented sandstone, respectively. Corresponding octahedral Al averages were 1.16, 1.03, and 0.67, respectively. A systematic increase in average interlayer K from 0.49 to 0.54 to 0.61 was also observed, with apparent increases in diagenesis. All element determinations were made with an electron microprobe and recast on an anion equivalent basis to structural formulae based on the O10(OH)2 unit. The clay preserved in the early ankerite concretions was found to be an illite/smectite containing about 20% expandable layers, and the mineral in the glauconite pellets from uncemented areas of the sandstone, an ordered glauconite. “Minus cement” porosities of the sandstone indicate that glauconitization may have taken place at burial depths greater than 0.6 to 1.8 km, but the mechanism for the incorporation of Fe3+ in the glauconite at that depth is not apparent.

Analytical and high-resolution transmission electron microscopy of weathered plagioclase and K-feldspar provided microtextural and chemical data that suggest a sequential formation of weathering products. An alteration layer < 1 µm thick on feldspar surfaces had short-range order and was termed protocrystalline. Relative to the parent feldspars the protocrystalline layer was depleted in Ca, Na, K, and Si and significantly enriched in Fe. On plagioclase, the protocrystalline material was replaced by Ca-Fe-K-smectite, another protocrystalline material, and spherical halloysite. Abundant tubular halloysite on the corroded surface apparently formed by reprecipitation of components released by plagioclase dissolution. The K-feldspar was markedly more resistant to weathering than the plagioclase.

Recrystallization of the patchily developed protocrystalline rind produced Fe-bearing, aluminous smecrite, which was ultimately replaced by spherical halloysite and laths of kaolinite. Muscovite laths within plagioclase crystals were converted initially to illite by loss of K, then to randomly interstratified illite/smectite, and then to smectite that contained Mg, little K and Fe, and was more aluminous and contained less Ca than the smectite that originally replaced the plagioclase. Smectite was replaced epitactically by kaolinite. Kaolinite was the stable weathering product of the feldspars and muscovite in the profiles. It probably formed in equilibrium with a solution whose composition was no longer controlled by the microenvironment within the feldspar, but approached that of meteoric water.

The swelling of an n-butylammonium vermiculite in solutions of n-butylammonium chloride has been studied by neutron diffraction as a function of temperature and the concentration of the soaking solution. On heating a swollen sample a transition to the crystalline phase took place at a well-defined temperature, the c-axis spacing changing from 120 to 19.4 Å at 14°C in a 0.1 M solution and from 330 to 19.4 Å at 33°C in a 0.01 M solution. The phase transition was completely reversible, and a study of the temperature-concentration phase diagram was made as high as 50°C The swollen phase was studied in a range of concentrations of the external solution between 0.2 M and 5 × 10-4 M, for which the c-axis spacings were 85 and 910 Å, respectively. The reversibility, sharpness, and reproducibility of the phase change from crystalline to swollen gel suggest that the transition is truly thermodynamic, which is not in accord with DLVO theory. The concentration dependence of the observed d-values also could not be explained satisfactorily by DLVO theory.

Volcanic and non-volcanic partings are exposed in coal beds of the Tertiary Beluga and Sterling Formations along the shores of the Kenai lowland, Alaska. About two-thirds of the partings originated as air-fall tephra which fell in coal-forming swamps. The tephra partings in the Pliocene strata are unaltered or slightly altered and have a characteristic mineral assemblage of volcanic glass ± montmoriUonite ± kaolinite ± opal-CT. Miocene strata are slightly altered to totally altered, and a typical mineral assemblage consists of feldspar ± kaolinite ± montmorillonite ± quartz ± crandallite ± altered volcanic glass. Crandallite appears to have formed early in diagenesis by the replacement of volcanic glass prior to the formation of montmorillonite and kaolinite.

About one-third of the partings originated primarily as detrital sediments derived from surrounding metamorphic and sedimentary terranes and were deposited by periodic floods. Mixtures of tephra and detrital sediments were also noted and were difficult to distinguish from tephra partings in the field. Detrital partings are characterized by detrital chlorite + illite + smectite + quartz ± feldspar ± siderite ± kaolinite. The chlorite in these strata is allogenic. Smectite is less common in the detrital partings.