The 57Fe Mössbauer spectra of a series of untreated and Ca-saturated nontronites showed a predominant Fe3+ resonance which was computer-fitted with two Fe3+ doublets defining iron in non-equivalent cis-FeO4(OH)2 octahedral sites. In most spectra a doublet indicating tetrahedral Fe3+ was fitted and in one untreated sample a doublet indicating interlayer Fe3+ was identified. In a further untreated sample the interlayer iron was present as Fe2+. Upon Ca-saturation the interlayer iron was displaced. It also appears that the interlayer iron was present in at least two different interlayer sites. From the computer-fitted data it was clear that the interlayer cations have a significant effect on the Mössbauer resonances of iron in the two non-equivalent cis-octahedral and the tetrahedral sites of nontronite.

Mobility measurements were made for dry-ground mica particles dispersed in aqueous KCl, Cr(NO3)3, and cetyltrimethylammonium bromide (CTAB) solutions. In the latter solutions charge reversal occurred at about 2 × 10-6 M and 3 × 10-5 M, respectively. Negative zeta potentials in KCl solutions calculated using the Smoluchowski equation are about one third of the corresponding values obtained from streaming potentials and force measurements using mica sheets. Good agreement, however, was obtained when positively charged groups created during grinding were neutralized, and the zeta potentials were corrected according to the procedure of O'Brien and White with an assumed average particle size of 0.25 μm. When the zeta potentials of positively charged particles were corrected in this way, agreement with values calculated from force measurements was also improved.

Feldspars in granitic saprolite in southwestern Australia have altered to halloysite, kaolinite, and gibbsite with no evidence of noncrystalline material. The secondary minerals are commonly present as intimate mixtures within altered feldspar grains, but discrete zones of gibbsite or halloysite-kaolinite also are present. Variations in the chemical microenvironment within micrometer-size zones in grains apparently controlled the type and distribution of secondary minerals. The alteration of both plagioclase and alkali feldspars involved congruent dissolution by soil solution and crystallization of halloysite, kaolinite, and gibbsite from this solution. Highly altered feldspar grains consist of etched feldspar fragments embedded within a highly porous framework of subhedral to euhedral platy crystals of kaolinite and gibbsite, or of spherical and felted aggregates of halloysite.

A program of simultaneous linear equations has been developed to calculate component proportions and/or component property values for mineral mixtures in soil clays and sediments. The analysis is based on quantitatively measured chemical and physical properties of samples and involves (1) qualitative identification of the mineral components in the mixture by any appropriate means; (2) quantitative measure of the sample property values selected for use in the program; (3) estimation of the proportion of each component in the mixture by a technique such as X-ray powder diffraction; (4) assignment of limits to component property ranges; (5) selection of one of four available calculation options and application of the simultaneous linear-equations program; (6) examination of the residuals of the analysis and, if appropriate, adjustment of the initial estimates for component proportions or property ranges and then repeating step 5; and (7) verification of the final component proportions by comparison with information from step 1. Completeness and/or accuracy of the final results for component proportions may be checked by the closeness of approach to 1.0 for the sum of the component proportions. The method requires that, at minimum, the number of properties measured must equal the number of components in the samples being analyzed and that the minimum number of samples must equal the number of properties measured.

Using the clay fractions of 15 Pennsylvania soils containing kaolinite, illite, smectite, vermiculite, chlorite, interstratified vermiculite/chlorite, quartz, and noncrystalline material, and measuring methylene blue cation-exchange capacity, the amount of Ca displaced by Mg from a Ca-saturated clay, the amount of K displaced by NH4 from a K-saturated clay heated to 110°C, % K2O, % SiO2, % MgO, and weight loss at 110°–300°C and 300°–950°C, the adjustment of property values was found to have the lowest residual value and the most consistent results. The source of analytical errors was also located by examination of residual tables. Samples that were similar in composition gave more reliable component proportions.

The adsorption and oxidation of 3,3′,5,5′-tetramethyl benzidine (TMB) on hectorite has been investigated using X-ray powder diffraction, ultraviolet-visible spectroscopy, electron spin resonance, and infrared spectroscopy. The molecule adsorbed by cation exchange at low adsorption levels and oxidized to the monomeric radical cation (yellow). At higher adsorption levels, intercalation of TMB occurred in amounts greater than the cation-exchange capacity of the hectorite, and the π-π charge-transfer complex (blue) became much more evident. The TMB monomers appeared to lie flat in the layer silicate interlayers, whereas the molecules in the charge-transfer complexes assumed a near-vertical orientation relative to the surface. The oxidation of adsorbed TMB was probably due to diffusion of O2 to the surface, because the structural Fe3+ content of the hectorite was too low to facilitate a significant quantity of direct Fe3+-TMB electron transfer.

The instability of palygorskite and sepiolite under soil conditions was investigated to determine if these fibrous minerals transform directly to smectite under laboratory conditions. The treatment of 100 mg (0.12 mmole) of palygorskite with 1 mmole of NaOH solution (17 ml) at 150°C for 24 hr yielded a smectite. Analcime and smectite were formed when ≥ 3 mmole of NaOH was used. The addition of ≤ 6 mmole NaOH to sepiolite destroyed it gradually. On addition of ≥ 8 mmole NaOH, sepiolite altered to an X-ray amorphous material. In the presence of Al and Si, however, it transformed to smectite and analcime. Transmission electron microscopy, cation-exchange capacity, and X-ray powder diffraction studies of the products suggest that alteration wa. (1) via solution, o. (2) by a structural reorganization wherein the basic 2:1 silicate structural units were unchanged.

X-ray powder diffraction studies were performed with propyl-, dodecyl-, and dodecyldiam-monium bentonites saturated with aqueous mixtures of eleven organic pollutants at concentrations of 0.01 to 100%. The alkylammonium salt treatment separated the montmorillonite unit layers, which increased the interlamellar volume and exposed the interlamellar surfaces for adsorption of the organic pollutants. Washing the salt-treated clays with distilled water removed excess, physically adsorbed alkylammonium ions that could interfere with adsorption of the organic pollutants. Adsorption isotherms conducted at organic pollutant concentrations of 100 and 1000 mg/liter indicated the three alkylammonium montmorillonites, especially propylammonium montmorillonite, were effective adsorbents from aqueous solution, but to a lesser extent than adsorbents currently used in the water and wastewater fields.

The crystal structure of phengite-2M1 from Rio de Oro, Spanish Sahara, was refined in space group C2/c to a residual of 3.3% with 1267 independent X-ray diffraction reflections. The composition of the mica determined by electron microprobe analysis is (K0.948Na0.051Ba0.027)(Al1.510Mg0.273Fe0.144Cr0.095Ti0.010Mn0.003)2.035(Si3.253Al0.747)O10(OH)2. The cell dimensions are a = 5.2153(5), b = 9.043(2), c = 19.974(9) Å, β = 95.789(9)°, and V = 937.2(3) Å3. The substitution of Si for Al in the tetrahedral sheet and larger divalent cations for Al in the octahedra allows the amount of distortions that are generally required to alleviate tetrahedral-octahedral sheet lateral misfit in muscovite, such as tetrahedral rotation and octahedral flattening, to be reduced. The O…H vector is nearly horizontal and points slightly into the octahedral sheet where it may be involved in hydrogen bond contacts inside M(1). In contrast to previously reported refinements of all but one other phengite, no ordering of tetrahedral cations was found in the study specimen. This disorder is considered to be due to the low-pressure, high-temperature amphibolite facies environment of crystallization.

The sorption properties of Co, Cu, Ni, and Ca were studied in a mixed mineral suspension of synthetic MnO2 and Wyoming montmorillonite. The distribution of the sorbed cations between the two solid phases was measured by indirect chemical fractionation with acidified NH2OH-HCl and by direct X-ray spectroscopic analysis of mineral particles using electron microscopy. Electron microscope and NH2OH-HCl measurements of the quantity of Co sorbed on MnO2 agreed within 6%. Seventy-seven, 67, and 69% of the total Co, Cu, and Ni sorbed by the mixed mineral suspension was found on the manganese oxide. The opposite distribution was found for sorbed Ca with 28% on the manganese oxide and 72% on the montmorillonite particles. The observed differences in metal sorption by these minerals are related to the cation-sorption mechanisms of manganese oxide and montmorillonite.

Spherical and platy kaolinite crystals were prepared under several hydrothermal conditions. Spherical kaolinite was produced mainly at high solid/water ratio (1/4) and at low temperatures (150°-200°C). Platy kaolinite predominated in products from experiments with intermediate solid/water ratios (1/256-1/16) and at high temperatures. Boehmite predominated at low solid/water ratios (1/4096) at all experimental temperatures (180°-220°C). The results indicate that the growth of the spherical kaolinite was favored at high degrees of supersaturation, whereas the growth of the platy kaolinite was favored at relatively low degrees of supersaturation.

The three-dimensional order shown by the two-layer hydrates of Na- and Ca-vermiculite, prepared from Mg-vermiculite from Llano, Texas, has enabled clear, two-dimensional Fourier projections of their interlayer structures to be obtained. Structure factor calculations were made in space group C2 and with unit-cell dimensions of a = 5.358 Å, b = 9.232 Å, and ß = 96.82°; for Na-vermiculite C = 14.96 Å and for Ca-vermiculite c = 15.00 Å. In Na-vermiculite the interlayer cations are octahedrally coordinated to water molecules with the sodium-water polyhedra only located between the triads of oxygen atoms forming bases to tetrahedra in adjacent silicate layers. In Ca-vermiculite the interlayer cations are in both octahedral and 8-fold (distorted cubic) coordination with water molecules. The octahedrally coordinated Ca ions are between the bases of tetrahedra in adjacent silicate layers, but the 8-fold coordinated Ca ions are between the ditrigonal cavities. In both Na- and Ca-vermiculite some water molecules are drawn from planar networks appreciably towards the ditrigonal cavities. The three-dimensional order observed for these vermiculites contrasts with the stacking disorder reported for Mg-vermiculite from Llano. The distinct crystallographic behavior of Na+, Ca2+, and Mg2+ in the hydration layers of Llano vermiculite probably depends on cation sizes and field strengths, together with the need to achieve local charge balance near the sites of tetrahedral Al-for-Si substitution.

Reactions between hydroxy-Al ions and orthosilicic acid as influenced by citric acid were studied at an initial Si concentration of 1.6 × 10−3 M, Si/Al molar ratios of 0.5 and 1.0, OH/Al molar ratios of 1.0-3.0, and citric acid/Al molar ratios of 0-0.3. In the absence of citric acid and at OH/A1 ratios of 1.0-2.8, imogolite (>0.01 μm) was dominant in the precipitates. At citric acid/Al ratios of 0.01-0.1, imogolite and/or pseudoboehmite were dominant in the precipitates at OH/Al ratios of 1.0 and 2.0, and imogolite and/or ill-defined aluminosilicate complexes at OH/Al ratio of 2.8. Instead of allophane or “proto-imogolite” allophane being the predominant species in the precipitates, the formation of ill-defined aluminosilicate complexes at OH/Al ratio of 3.0 was steadily promoted by increasing the solution citric acid/Al ratios from 0 to 0.3. The freeze-dried soluble products (<0.01 μ) ranged from silica gel to “proto-imogolite,” depending upon the basicity of Al and the level of citric acid of the parent solution. The amount of “proto-imogolite” increased with increasing citric acid/Al ratios from 0 to 0.1 in solution. Complexing low molecular weight organic acids, such as citric acid, impeded the formation of the short-range ordered aluminosilicates, allophanes and imogolite.

Reactions of smectite with phenols were investigated to understand the role of clay minerals in abating transport of these organic pollutants to ground water. Sorption of o-methylphenol, o-chlorophenol, and m-methylphenol by the clay with different exchange cations was accomplished by passing phenol vapors in a slow stream of air or nitrogen through the samples. The resulting products, extracted with methanol and analyzed by using mass spectrometry, included monomers, dimers, trimers, and tetramers of the parent phenol and of the corresponding quinones, the oxidation product of the phenols. In extracts from the Fe-clay-phenol complexes formed in air, traces of the phenolic pentamers were also detected. Both sorption and polymerization were much higher in air than in nitrogen. The greatly reduced polymerization in nitrogen suggests that anaerobic environment of the landfill sites may facilitate phenol transport to ground water. The degree of polymerization and its magnitude was in the order Fe- > Al- > Ca- > Na-clay.

The kaolinization of bauxite has generally been thought to be a simple process of epigenetic resilification. A study of the karstic boehmitic bauxites in the Vlasenica region of Yugoslavia, however, shows that kaohnization took place in a rather complex manner, in which the alteration was caused by the percolation of siliceous water descending through the deposit by means of cracks, fissures, etc. The matrix of one such Vlasenica deposit was found to be more highly kaolinized than the oolitic fraction. Based on a mineralogical and geochemical examination of matrix material, the following pattern of zoned alteration was identified: kaolinitic zone-boehmite enrichment zone-original bauxite. In the kaolinitic zone, well-crystallized kaolinite, formed by the reaction of dissolved silica with boehmite, has replaced all other minerals in the matrix. This Si metasomatism was accompanied by an outward migration of Al and resulted in the formation of a transition zone in which new boehmite partly replaces both kaolinite and hematite (Al remobilization). A thermodynamic model of the process has been established on the basis of stability diagrams calculated for the mineral assemblages in the alteration zones and in the deposit as a whole.

Single crystals of sudoite from Ottré, Belgium, allow confirmation of a dioctahedral 2:1 layer and a trioctahedral interlayer in a IIb arrangement. A regular 2-layer s structure is formed in which the octahedral stagger within both 2:1 layers is directed along X1 and adjacent layers are alternately displaced by a2/3 and a3/3. Poor quality crystals and twinning prevented three-dimensional refinement. One-dimensional refinement suggests that the smaller d(001) value of dioctahedral chlorites relative to trioctahedral species is due primarily to the thinner dioctahedral sheet.

Dehydration-induced luminescence (DIL), the emission of light from a clay paste upon dehydration, was characterized experimentally for a colloidal kaolinite. The relationship between total photon count of the emitted light and film thickness is linear up to a thickness of 30 μm. The photon emission was obtained over a critical range of water contents (25-60%) of the oven-dry clay, and the kinetics of photon emission was presumed to be closely associated with the kinetics of film dehydration. Whether drying proceeded throughout the bulk or via a moving front was undetermined, but in either mode it was preceded by the formation of a thin dry film at the interface with the atmosphere. Grinding of the kaolinite for several minutes by mortar and pestle before paste preparation resulted in an overall increase of photon emission compared to unground kaolinite and in the formation of more than one emission peak, as well as a prolongation of the light emission. This effect on the kinetics of light emittance was observed for about two months after the application of the mechanical stress and suggests a means of detecting the mechanical stress history of a clay.

An estimate was made of the spectral characteristics of the emitted light using optical filters and by incorporating tryptophan and salicylic acid into the kaolinite paste where they acted as fluorescent probes. The latter technique shifted the frequency of the light emitted by the kaolinite from the ultraviolet to the visible range where it was less effectively reabsorbed. The first method showed that the wavelengths of 97% of the emitted light was <460 nm and that 75% of the light had wavelengths <410 nm. The second method showed that the total intensity of DIL increased in the presence of fluorescence molecules, suggesting that the emittance was in the ultraviolet range.

Parathion and methyl parathion adsorbed at high loads on clays and similar surfaces exhibited properties of a bulk phase, such as a well-defined solubility and a characteristic X-ray powder diffraction (XRD) pattern, different from those of the free substances. The aqueous solubility of parathion condensed at these surfaces was as low as 1.2 μg/ml as compared to 14 μg/ml for free parathion. The BET isotherm described the behavior of the investigated surface condensates even though these condensates were different from the multilayer adsorption for which the BET isotherm was originally developed. The XRD patterns of parathion and methyl parathion adsorbed on Na-bentonite exhibited reflections which were shifted towards higher angles as compared with the XRD patterns of the free compounds. This is in agreement with the lower solubility of the surface condensates. The properties of these condensates were easily controlled by the choice of adsorbent as well as by the choice of conditions under whch they were prepared. The existence of such surface-condensed phases and the manipulation of their properties can be utilized for the slow-release formulation of organophosphate esters which is important, for example, in pesticides application.

A corrensite-like mineral, from near Borgotaro, Parma (Taro Valley, Italy), was studied by X-ray powder diffraction (XRD) and thermal analysis at different temperatures and water vapor pressures in the natural state and after exchange with ten different cations. In the natural state the mineral is characterized by a basal reflection at ∼29 Å shifting to ∼24 Å on heating and to ∼32 Å by glycerol treatment. The dehydration features of the homoionic minerals show that the stability of the complex of water, compensating cation, and silicate framework depends on the electrostatic energy of the water dipole in the cation field, similarly to smectite.

XRD of the exchanged mineral shows a basal reflection of ∼58 Å particularly in the NH4-, Rb-, and Ba-exchanged states. This value suggests a structure characterized by a regular sequence of silicate layers with different layer charge, that generally results in a c periodicity of ∼29 Å, but which shifts to ∼58 Å, and perhaps higher values, because of small differences in the compensating cation layers.

The possible physical and chemical forces controlling the volume change behavior of kaolinite were ascertained from the sediment volume of kaolinite in various solvents under no external load condition and from conventional oedometer measurements of kaolinite in several pore fluids. The minimum sediment volume of 14.5 cm3/10 g clay occupied by kaolinite in water where repulsive (R) forces were dominant indicated that the R contribution was insignificant for kaolinite. The maximum sediment volume of 25.0 cm3/10 g clay in benzene where coulombic attraction forces were significant suggested that electrostatic attraction between silicate sheets and midplane cations and van der Waals forces were not appreciable for kaolinite. The positive edge-negative face bonding of kaolinite particles in benzene was unlikely because the protons required to impart a positive charge to the edges were not available in the nonpolar solvent. The 3688 cm−1 band in the infrared spectrum of a kaolinite-dimethylamine sample decreased by 10 cm−1 on H-bond formation of the solvent molecule with the exposed structural hydroxyls of the octahedral sheet. The adsorbed solvent molecules likely H-bonded with an adjacent clay particle. That such interparticle H-bonds controlled the sediment volume and interparticle attraction in kaolinite was indicated by the decrease in sediment volume with increase in dipole moment of the solvent molecule, i.e., 25.0 cm3/10 g clay in n-heptane (dipole moment, μ = 0), 23.5 cm3/10 g clay in toluene (μ = 0.36), 17.0 cm3/10 g clay in ethanol (μ = 1.67), and 14.5 cm3/10 g clay in water (μ = 1.84).

In the oedometer tests with various pore fluids, a high void ratio (i.e., volume of voids/volume of solids) of ≈ 1.3 was obtained for kaolinite in n-heptane, and hexane (μ ≅ 0) at an external pressure of 1 kg/cm2 probably because the weakly bonded kaolinite particles were randomly oriented. At the corresponding applied pressure a lower void ratio of 0.88 resulted in water (μ = 1.84) where the stronger hydrogen bond between flat layer surfaces of adjacent particles favored a parallel orientation of clay particles.

The variations in void ratio-external pressure relationship indicated that kaolinite underwent lower compressibility in a solvent with low dipole moment and vice versa. Thus, the interparticle H-bond did not play a significant role in controlling the shear resistance and volume change behavior. The volume change behavior was essentially controlled by frictional forces and clay fabric. In nonpolar solvents the random arrangement of kaolinite particles and the frictional forces mobilized a high shear resistance on the application of a consolidation pressure, resulting in a lower compressibility. In a solvent with high dipole moment the parallel array of clay particles mobilized less shear resistance and produced a greater compression.

Several hydrates can be synthesized from well-crystallized kaolinites; of importance to the present work are a 10-Å hydrate (called the QS-10 hydrate), an 8.6-Å hydrate, and two kinds of partially dehydrated mixed-layer hydrates. One kind is a series of unstable materials with d(001) varying continuously between 10 and 8.6 Å, and the other kind is stable with d(001) approximately centered at 7.9 Å. The 10- and 7.9-Å phases have been observed in halloysites by many workers using X-ray powder diffraction, and the 8.6-Å phase has been seen by others in selected area electron diffraction photographs. Infrared spectra reveal additional similarities between the synthetic hydrates and both halloysite(10Å) and partially dehydrated halloysites. Because of these similarities, the synthetic hydrates can be used to develop a model for the dehydration of halloysite(10Å).

Previous work on the 10- and 8.6-Å hydrates identified two structural environments for the interlayer water. In one, the water is keyed into the ditrigonal holes of the silicate layer (hole water), and in the other, the water is more mobile (associated water). Both types are found in the QS-10 hydrate and halloysite(10Å), whereas only hole water occurs in the 8.6-Å hydrate. In the QS-10 hydrate, stronger hydrogen bonding between hole water and the clay makes the hole water more stable than the associated water. This difference in stability is responsible for a two-step dehydration process. The first step is the loss of associated water which results in a material with d(001) = 8.6 Å. This stable hydrate must be heated to temperatures near 200°C to drive off the remaining hole water. The less perfect structure of halloysite and its common curvilinear morphology reduce the difference in stability between hole and associated water molecules, so that when halloysite(10Å) dehydrates, loss of hole water and associated water overlaps, and the d-spacing goes directly to 7.2–7.9 Å.